- 熔体流动速率 [g/10min]: 0.55
- 缺口冲击强度: 0.85
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 980
- 热变形温度 [℃]: 68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.959 g/cc | 0.959 g/cc | ASTM D1505/D792 |
| ESCR 100% Igepal® | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| ESCR 10% Igepal® | 200 hour @Temperature 50.0 °C | 200 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 39 g/10 min @Load 21.6 kg, Temperature 190 °C | 39 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D638 |
| Flexural Modulus, 1% Secant | 980 MPa | 142000 psi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |