- 密度 [g/cm3]: 2.06
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 106.0
- 弯曲模量 [MPa]: 10.3
- 热变形温度 [℃]: 291.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.06 g/cc | 0.0744 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 3.17 mm | 0.015 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 106 MPa | 15400 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm @Thickness 3.17 mm | 0.750 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.980 W/m-K | 6.80 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 291 °C | 555 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 530 °F | Unannealed; ASTM D648 |