- 吸水率 [%]: 1.9
- 缺口冲击强度: 1.32
- 拉伸强度 [MPa]: 108.0
- 弯曲模量 [MPa]: 4.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.9 % | 1.9 % | Wet |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | Dry; ASTM D785 |
| Tensile Strength, Yield | 108 MPa | 15700 psi | Wet; ASTM D638 |
| 167 MPa | 24200 psi | Dry; ASTM D638 | |
| Elongation at Break | 4.0 % | 4.0 % | Dry; ASTM D638 |
| 9.0 % | 9.0 % | Wet; ASTM D638 | |
| Flexural Strength | 157 MPa | 22800 psi | Wet; ASTM D790 |
| 275 MPa | 39900 psi | Dry; ASTM D790 | |
| Flexural Modulus | 4.50 GPa | 653 ksi | Wet; ASTM D790 |
| 8.60 GPa | 1250 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.32 J/cm | 2.47 ft-lb/in | Dry; ASTM D256 |
| 2.40 J/cm | 4.50 ft-lb/in | Wet; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |