- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 0.4
- 断裂伸长率 [%]: 103
- 弯曲强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 3.00
- 硬度: 118.0
- 热变形温度 [℃]: 184.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | 17 % | 17 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | |
| Coefficient of Friction, Static | 0.090 | 0.090 | |
| K (wear) Factor | 80.6 x 10-8 mm³/N-M | 40.0 x 10-10 in³-min/ft-lb-hr | K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours). |
| Limiting Pressure Velocity | 0.280 MPa-m/sec | 7990 psi-ft/min | at 0.35 m/s |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |