- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 0.7
- 断裂伸长率 [%]: 234
- 弯曲强度 [MPa]: 164.0
- 弯曲模量 [MPa]: 14.0
- 硬度: 117.0
- 热变形温度 [℃]: 263.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Ultimate | 164 MPa | 23800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 234 MPa | 33900 psi | ASTM D790 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.40 J/cm | 10.1 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.17 | 0.17 | |
| Coefficient of Friction, Static | 0.20 | 0.20 | |
| K (wear) Factor | 15.9 x 10-8 mm³/N-M | 7.90 x 10-10 in³-min/ft-lb-hr | K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours). |
| Limiting Pressure Velocity | 3.29 MPa-m/sec | 93900 psi-ft/min | at 0.35 m/s |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C | 505 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D648 |