- 熔体流动速率 [g/10min]: 70.0
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 7.0
- 弯曲强度 [MPa]: 85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number | ||
| Melt Flow | 70 g/10 min @Temperature 275 °C | 70 g/10 min @Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 4.50 GPa | 653 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 | ||
| Tensile Creep Modulus, 1 hour | 3700 MPa | 537000 psi | ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 2500 MPa | 363000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.5 @Frequency 1.00e+6 Hz | 5.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz | 0.16 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.30 @Frequency 100 Hz | 0.30 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10 K/min | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||