- 密度 [g/cm3]: 1.33
- 弯曲强度 [MPa]: 132.0
- 弯曲模量 [MPa]: 6.85
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | dry; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 132 MPa | 19100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 8.25 GPa | 1200 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 6.85 GPa | 994 ksi | ISO Data | ||
| Charpy Impact Unnotched | 9.40 J/cm² | 44.7 ft-lb/in² | ISO 179 | ||
| 9.10 J/cm² @Temperature -30.0 °C | 43.3 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||