  3. PA66
  4. DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.49
  • 吸水率 [%]: 0.6
  • 成型收缩率 [%]: 0.002
  • 缺口冲击强度: 1.33
  • 弯曲模量 [MPa]: 8.27
  • 硬度: 118.0
  • 热变形温度 [℃]: 260.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.51 g/cc1.51 g/ccDAM; ASTM D792
Density 1.49 g/cc0.0538 lb/in³DAM; ISO 1183
Filler Content 43 %43 %DAM
Water Absorption  0.60 %
@Temperature 23.0 °C		0.60 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 0.90 %
@Temperature 23.0 °C		0.90 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
 1.5 %
@Temperature 23.0 °C		1.5 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 4.7 %
@Temperature 23.0 °C		4.7 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 4.7 %
@Temperature 23.0 °C		4.7 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Viscosity  44000 cP
@Shear Rate 7000 1/s,
Temperature 315 °C		44000 cP
@Shear Rate 7000 1/s,
Temperature 599 °F		DAM; ISO 11443
 51000 cP
@Shear Rate 5000 1/s,
Temperature 315 °C		51000 cP
@Shear Rate 5000 1/s,
Temperature 599 °F		DAM; ISO 11443
 68000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		68000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		DAM; ISO 11443
 78000 cP
@Shear Rate 2000 1/s,
Temperature 315 °C		78000 cP
@Shear Rate 2000 1/s,
Temperature 599 °F		DAM; ISO 11443
 80000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		80000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		DAM; ISO 11443
 106000 cP
@Shear Rate 1000 1/s,
Temperature 315 °C		106000 cP
@Shear Rate 1000 1/s,
Temperature 599 °F		DAM; ISO 11443
 109000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		109000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		DAM; ISO 11443
 123000 cP
@Shear Rate 700 1/s,
Temperature 315 °C		123000 cP
@Shear Rate 700 1/s,
Temperature 599 °F		DAM; ISO 11443
 123000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		123000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		DAM; ISO 11443
 129000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		129000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		DAM; ISO 11443
 141000 cP
@Shear Rate 500 1/s,
Temperature 315 °C		141000 cP
@Shear Rate 500 1/s,
Temperature 599 °F		DAM; ISO 11443
 169000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		169000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		DAM; ISO 11443
 197000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		197000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		DAM; ISO 11443
 199000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		199000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		DAM; ISO 11443
 228000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		228000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		DAM; ISO 11443
 276000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		276000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		DAM; ISO 11443
 325000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		325000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		DAM; ISO 11443
 378000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		378000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		DAM; ISO 11443
Linear Mold Shrinkage  0.0020 cm/cm
@Thickness 1.60 mm		0.0020 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0030 cm/cm
@Thickness 3.20 mm		0.0030 in/in
@Thickness 0.126 in		Flow; DAM
 0.0040 cm/cm
@Thickness 6.40 mm		0.0040 in/in
@Thickness 0.252 in		Flow; DAM
 0.0090 cm/cm
@Thickness 1.60 mm		0.0090 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.0090 cm/cm
@Thickness 6.40 mm		0.0090 in/in
@Thickness 0.252 in		Transverse; DAM
 0.0090 cm/cm
@Thickness 3.20 mm		0.0090 in/in
@Thickness 0.126 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
@Thickness 2.00 mm		0.010 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 909050%RH; ISO 2039/2
 103103DAM; ASTM D785
 105105DAM; ISO 2039/2
Hardness, Rockwell R 11811850%RH; ISO 2039/2
 125125DAM; ISO 2039/2
Tensile Strength at Break  160 MPa
@Temperature 23.0 °C		23200 psi
@Temperature 73.4 °F		50%RH; ISO 527
 225 MPa
@Temperature 23.0 °C		32600 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  72.0 MPa
@Temperature 77.0 °C		10400 psi
@Temperature 171 °F		50%RH; ASTM D638
 86.0 MPa
@Temperature 121 °C		12500 psi
@Temperature 250 °F		DAM; ASTM D638
 121 MPa
@Temperature 77.0 °C		17500 psi
@Temperature 171 °F		DAM; ASTM D638
 145 MPa
@Temperature 23.0 °C		21000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 207 MPa
@Temperature 23.0 °C		30000 psi
@Temperature 73.4 °F		DAM; ASTM D638
 252 MPa
@Temperature -40.0 °C		36500 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  5.53 MPa
@Strain 0.100 %,
Temperature 150 °C		802 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.50 MPa
@Strain 0.100 %,
Temperature 120 °C		943 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.57 MPa
@Strain 0.100 %,
Temperature 150 °C		953 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.80 MPa
@Strain 0.100 %,
Temperature 100 °C		986 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.01 MPa
@Strain 0.100 %,
Temperature 120 °C		1020 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.31 MPa
@Strain 0.100 %,
Temperature 100 °C		1060 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.39 MPa
@Strain 0.100 %,
Temperature 80.0 °C		1070 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.76 MPa
@Strain 0.100 %,
Temperature 60.0 °C		1130 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.47 MPa
@Strain 0.100 %,
Temperature 80.0 °C		1230 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.90 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1440 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 10.19 MPa
@Strain 0.100 %,
Temperature 60.0 °C		1478 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 11.81 MPa
@Strain 0.200 %,
Temperature 150 °C		1713 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.87 MPa
@Strain 0.200 %,
Temperature 120 °C		1867 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.89 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1870 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 13.29 MPa
@Strain 0.200 %,
Temperature 150 °C		1928 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.49 MPa
@Strain 0.200 %,
Temperature 120 °C		1957 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.51 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1959 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 13.96 MPa
@Strain 0.200 %,
Temperature 100 °C		2025 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.07 MPa
@Strain 0.100 %,
Temperature -40.0 °C		2041 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 14.16 MPa
@Strain 0.100 %,
Temperature 0.000 °C		2054 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 14.36 MPa
@Strain 0.200 %,
Temperature 80.0 °C		2083 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.55 MPa
@Strain 0.100 %,
Temperature -40.0 °C		2110 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 15.05 MPa
@Strain 0.200 %,
Temperature 100 °C		2183 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.07 MPa
@Strain 0.200 %,
Temperature 60.0 °C		2186 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.42 MPa
@Strain 0.200 %,
Temperature 80.0 °C		2527 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.67 MPa
@Strain 0.300 %,
Temperature 150 °C		2563 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.91 MPa
@Strain 0.300 %,
Temperature 120 °C		2743 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.24 MPa
@Strain 0.300 %,
Temperature 150 °C		2791 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.69 MPa
@Strain 0.300 %,
Temperature 120 °C		2856 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.26 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2938 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.47 MPa
@Strain 0.300 %,
Temperature 100 °C		2969 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.15 MPa
@Strain 0.300 %,
Temperature 80.0 °C		3068 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.54 MPa
@Strain 0.200 %,
Temperature 60.0 °C		3124 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.01 MPa
@Strain 0.300 %,
Temperature 100 °C		3192 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.22 MPa
@Strain 0.300 %,
Temperature 60.0 °C		3223 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.54 MPa
@Strain 0.400 %,
Temperature 150 °C		3269 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.7 MPa
@Strain 0.400 %,
Temperature 150 °C		3440 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.8 MPa
@Strain 0.400 %,
Temperature 120 °C		3450 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.69 MPa
@Strain 0.400 %,
Temperature 120 °C		3581 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.16 MPa
@Strain 0.400 %,
Temperature 100 °C		3649 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.47 MPa
@Strain 0.300 %,
Temperature 80.0 °C		3694 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.42 MPa
@Strain 0.400 %,
Temperature 80.0 °C		3832 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.76 MPa
@Strain 0.200 %,
Temperature 0.000 °C		3881 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 27.34 MPa
@Strain 0.400 %,
Temperature 100 °C		3965 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.53 MPa
@Strain 0.400 %,
Temperature 60.0 °C		3993 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.91 MPa
@Strain 0.200 %,
Temperature 23.0 °C		4048 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.4 MPa
@Strain 0.500 %,
Temperature 150 °C		4120 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.51 MPa
@Strain 0.200 %,
Temperature 0.000 °C		4135 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 28.61 MPa
@Strain 0.200 %,
Temperature -40.0 °C		4150 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 28.84 MPa
@Strain 0.200 %,
Temperature -40.0 °C		4183 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 29.54 MPa
@Strain 0.500 %,
Temperature 120 °C		4284 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.69 MPa
@Strain 0.300 %,
Temperature 23.0 °C		4306 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.03 MPa
@Strain 0.500 %,
Temperature 150 °C		4355 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.12 MPa
@Strain 0.500 %,
Temperature 120 °C		4514 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.39 MPa
@Strain 0.400 %,
Temperature 80.0 °C		4553 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.73 MPa
@Strain 0.300 %,
Temperature 60.0 °C		4602 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.03 MPa
@Strain 0.500 %,
Temperature 100 °C		4646 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.6 MPa
@Strain 0.600 %,
Temperature 150 °C		4730 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.34 MPa
@Strain 0.500 %,
Temperature 80.0 °C		4836 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.32 MPa
@Strain 0.600 %,
Temperature 120 °C		4978 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.53 MPa
@Strain 0.500 %,
Temperature 100 °C		5008 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.79 MPa
@Strain 0.600 %,
Temperature 150 °C		5046 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.01 MPa
@Strain 0.500 %,
Temperature 60.0 °C		5078 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.19 MPa
@Strain 0.600 %,
Temperature 120 °C		5249 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.27 MPa
@Strain 0.700 %,
Temperature 150 °C		5261 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.61 MPa
@Strain 0.400 %,
Temperature 23.0 °C		5310 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.24 MPa
@Strain 0.600 %,
Temperature 100 °C		5401 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.54 MPa
@Strain 0.700 %,
Temperature 120 °C		5590 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.88 MPa
@Strain 0.600 %,
Temperature 80.0 °C		5639 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.89 MPa
@Strain 0.700 %,
Temperature 150 °C		5641 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.2 MPa
@Strain 0.300 %,
Temperature 0.000 °C		5690 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.47 MPa
@Strain 0.500 %,
Temperature 80.0 °C		5725 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.58 MPa
@Strain 0.800 %,
Temperature 150 °C		5741 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.23 MPa
@Strain 0.400 %,
Temperature 60.0 °C		5835 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.27 MPa
@Strain 0.600 %,
Temperature 100 °C		5841 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.59 MPa
@Strain 0.600 %,
Temperature 60.0 °C		5887 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.87 MPa
@Strain 0.700 %,
Temperature 120 °C		5928 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.21 MPa
@Strain 0.300 %,
Temperature 23.0 °C		5977 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 42.03 MPa
@Strain 0.700 %,
Temperature 100 °C		6096 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.32 MPa
@Strain 0.300 %,
Temperature 0.000 °C		6138 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 42.5 MPa
@Strain 0.900 %,
Temperature 150 °C		6160 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.51 MPa
@Strain 0.800 %,
Temperature 150 °C		6166 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.56 MPa
@Strain 0.300 %,
Temperature -40.0 °C		6173 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 42.59 MPa
@Strain 0.800 %,
Temperature 120 °C		6177 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.97 MPa
@Strain 0.300 %,
Temperature -40.0 °C		6232 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.83 MPa
@Strain 0.700 %,
Temperature 80.0 °C		6357 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.05 MPa
@Strain 0.800 %,
Temperature 120 °C		6534 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.24 MPa
@Strain 1.00 %,
Temperature 150 °C		6562 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 45.69 MPa
@Strain 0.700 %,
Temperature 100 °C		6627 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.9 MPa
@Strain 0.600 %,
Temperature 80.0 °C		6660 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.94 MPa
@Strain 0.900 %,
Temperature 150 °C		6663 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.96 MPa
@Strain 0.700 %,
Temperature 60.0 °C		6666 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 46.27 MPa
@Strain 0.900 %,
Temperature 120 °C		6711 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 46.32 MPa
@Strain 0.800 %,
Temperature 100 °C		6718 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.49 MPa
@Strain 0.500 %,
Temperature 23.0 °C		6743 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.09 MPa
@Strain 1.10 %,
Temperature 150 °C		6975 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 48.57 MPa
@Strain 0.800 %,
Temperature 80.0 °C		7044 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.08 MPa
@Strain 0.900 %,
Temperature 120 °C		7118 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.24 MPa
@Strain 1.00 %,
Temperature 150 °C		7142 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 49.6 MPa
@Strain 1.00 %,
Temperature 120 °C		7190 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 50.09 MPa
@Strain 0.500 %,
Temperature 60.0 °C		7265 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.29 MPa
@Strain 0.900 %,
Temperature 100 °C		7294 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 50.58 MPa
@Strain 0.800 %,
Temperature 100 °C		7336 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.7 MPa
@Strain 1.20 %,
Temperature 150 °C		7350 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 50.98 MPa
@Strain 0.400 %,
Temperature 0.000 °C		7394 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 51.34 MPa
@Strain 0.800 %,
Temperature 60.0 °C		7446 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.79 MPa
@Strain 0.700 %,
Temperature 80.0 °C		7512 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.13 MPa
@Strain 1.10 %,
Temperature 150 °C		7561 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 52.69 MPa
@Strain 1.10 %,
Temperature 120 °C		7642 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 52.82 MPa
@Strain 1.00 %,
Temperature 120 °C		7661 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.89 MPa
@Strain 1.30 %,
Temperature 150 °C		7671 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 53.04 MPa
@Strain 0.900 %,
Temperature 80.0 °C		7693 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.64 MPa
@Strain 0.400 %,
Temperature 23.0 °C		7780 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 54.03 MPa
@Strain 1.00 %,
Temperature 100 °C		7836 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 54.19 MPa
@Strain 0.400 %,
Temperature 0.000 °C		7860 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 54.2 MPa
@Strain 0.400 %,
Temperature -40.0 °C		7860 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 54.23 MPa
@Strain 0.600 %,
Temperature 23.0 °C		7865 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.76 MPa
@Strain 1.20 %,
Temperature 150 °C		7942 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 54.91 MPa
@Strain 1.40 %,
Temperature 150 °C		7964 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 55.27 MPa
@Strain 0.900 %,
Temperature 100 °C		8016 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.6 MPa
@Strain 1.20 %,
Temperature 120 °C		8060 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 56.04 MPa
@Strain 0.400 %,
Temperature -40.0 °C		8128 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 56.18 MPa
@Strain 1.10 %,
Temperature 120 °C		8148 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.24 MPa
@Strain 0.900 %,
Temperature 60.0 °C		8157 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.87 MPa
@Strain 1.50 %,
Temperature 150 °C		8248 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 57.11 MPa
@Strain 1.00 %,
Temperature 80.0 °C		8283 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 57.24 MPa
@Strain 0.800 %,
Temperature 80.0 °C		8302 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.39 MPa
@Strain 1.30 %,
Temperature 150 °C		8324 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 57.61 MPa
@Strain 1.10 %,
Temperature 100 °C		8356 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 58.38 MPa
@Strain 1.30 %,
Temperature 120 °C		8467 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 58.62 MPa
@Strain 0.600 %,
Temperature 60.0 °C		8502 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 58.71 MPa
@Strain 1.60 %,
Temperature 150 °C		8515 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 59.31 MPa
@Strain 1.20 %,
Temperature 120 °C		8602 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 59.64 MPa
@Strain 1.00 %,
Temperature 100 °C		8650 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.84 MPa
@Strain 1.40 %,
Temperature 150 °C		8679 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 60.44 MPa
@Strain 1.70 %,
Temperature 150 °C		8766 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 60.74 MPa
@Strain 1.00 %,
Temperature 60.0 °C		8810 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 60.76 MPa
@Strain 1.20 %,
Temperature 100 °C		8813 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 60.92 MPa
@Strain 1.10 %,
Temperature 80.0 °C		8836 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 60.98 MPa
@Strain 1.40 %,
Temperature 120 °C		8844 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 61.62 MPa
@Strain 0.700 %,
Temperature 23.0 °C		8937 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.05 MPa
@Strain 1.50 %,
Temperature 150 °C		9000 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.07 MPa
@Strain 1.80 %,
Temperature 150 °C		9003 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 62.28 MPa
@Strain 1.30 %,
Temperature 120 °C		9033 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 62.43 MPa
@Strain 0.900 %,
Temperature 80.0 °C		9055 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.4 MPa
@Strain 0.500 %,
Temperature 0.000 °C		9200 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.44 MPa
@Strain 1.50 %,
Temperature 120 °C		9201 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 63.58 MPa
@Strain 1.90 %,
Temperature 150 °C		9222 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 63.64 MPa
@Strain 1.10 %,
Temperature 100 °C		9230 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 63.83 MPa
@Strain 1.30 %,
Temperature 100 °C		9258 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 64.16 MPa
@Strain 1.60 %,
Temperature 150 °C		9306 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.45 MPa
@Strain 1.20 %,
Temperature 80.0 °C		9348 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 65.02 MPa
@Strain 1.10 %,
Temperature 60.0 °C		9430 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 65.09 MPa
@Strain 2.00 %,
Temperature 150 °C		9441 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 65.22 MPa
@Strain 1.40 %,
Temperature 120 °C		9459 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 65.65 MPa
@Strain 1.60 %,
Temperature 120 °C		9522 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 66.23 MPa
@Strain 1.70 %,
Temperature 150 °C		9606 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.37 MPa
@Strain 0.700 %,
Temperature 60.0 °C		9626 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.41 MPa
@Strain 2.10 %,
Temperature 150 °C		9632 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 66.68 MPa
@Strain 1.40 %,
Temperature 100 °C		9671 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 67.2 MPa
@Strain 1.00 %,
Temperature 80.0 °C		9750 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 67.25 MPa
@Strain 0.500 %,
Temperature 23.0 °C		9754 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.28 MPa
@Strain 1.20 %,
Temperature 100 °C		9758 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 67.67 MPa
@Strain 2.20 %,
Temperature 150 °C		9815 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 67.69 MPa
@Strain 1.30 %,
Temperature 80.0 °C		9818 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 67.79 MPa
@Strain 1.70 %,
Temperature 120 °C		9832 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 67.82 MPa
@Strain 1.50 %,
Temperature 120 °C		9836 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 67.98 MPa
@Strain 0.500 %,
Temperature 0.000 °C		9860 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.01 MPa
@Strain 0.500 %,
Temperature -40.0 °C		9864 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 68.07 MPa
@Strain 1.80 %,
Temperature 150 °C		9873 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.24 MPa
@Strain 0.800 %,
Temperature 23.0 °C		9897 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.92 MPa
@Strain 2.30 %,
Temperature 150 °C		9996 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 69.02 MPa
@Strain 1.20 %,
Temperature 60.0 °C		10010 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 69.46 MPa
@Strain 1.50 %,
Temperature 100 °C		10070 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 69.77 MPa
@Strain 1.80 %,
Temperature 120 °C		10120 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.9 MPa
@Strain 1.90 %,
Temperature 150 °C		10100 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 70.03 MPa
@Strain 2.40 %,
Temperature 150 °C		10160 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 70.37 MPa
@Strain 1.60 %,
Temperature 120 °C		10210 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 70.46 MPa
@Strain 0.500 %,
Temperature -40.0 °C		10220 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 70.57 MPa
@Strain 1.30 %,
Temperature 100 °C		10240 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 70.81 MPa
@Strain 1.40 %,
Temperature 80.0 °C		10270 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 71.13 MPa
@Strain 2.50 %,
Temperature 150 °C		10320 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 71.58 MPa
@Strain 1.10 %,
Temperature 80.0 °C		10380 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 71.58 MPa
@Strain 2.00 %,
Temperature 150 °C		10380 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 71.68 MPa
@Strain 1.90 %,
Temperature 120 °C		10400 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 71.94 MPa
@Strain 1.60 %,
Temperature 100 °C		10430 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 72.18 MPa
@Strain 2.60 %,
Temperature 150 °C		10470 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 72.66 MPa
@Strain 1.30 %,
Temperature 60.0 °C		10540 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 72.83 MPa
@Strain 1.70 %,
Temperature 120 °C		10560 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 73.15 MPa
@Strain 2.70 %,
Temperature 150 °C		10610 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 73.19 MPa
@Strain 2.10 %,
Temperature 150 °C		10620 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 73.48 MPa
@Strain 2.00 %,
Temperature 120 °C		10660 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 73.83 MPa
@Strain 0.800 %,
Temperature 60.0 °C		10710 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.87 MPa
@Strain 1.40 %,
Temperature 100 °C		10710 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.92 MPa
@Strain 1.50 %,
Temperature 80.0 °C		10720 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 74.05 MPa
@Strain 2.80 %,
Temperature 150 °C		10740 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.42 MPa
@Strain 1.70 %,
Temperature 100 °C		10790 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 74.72 MPa
@Strain 2.20 %,
Temperature 150 °C		10840 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 74.74 MPa
@Strain 0.900 %,
Temperature 23.0 °C		10840 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.79 MPa
@Strain 2.90 %,
Temperature 150 °C		10850 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.84 MPa
@Strain 0.600 %,
Temperature 0.000 °C		10850 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.17 MPa
@Strain 2.10 %,
Temperature 120 °C		10900 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 75.19 MPa
@Strain 1.80 %,
Temperature 120 °C		10910 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 75.53 MPa
@Strain 3.00 %,
Temperature 150 °C		10950 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 75.69 MPa
@Strain 1.20 %,
Temperature 80.0 °C		10980 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 76.17 MPa
@Strain 2.30 %,
Temperature 150 °C		11050 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 76.25 MPa
@Strain 1.40 %,
Temperature 60.0 °C		11060 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 76.25 MPa
@Strain 3.10 %,
Temperature 150 °C		11060 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 76.64 MPa
@Strain 1.80 %,
Temperature 100 °C		11120 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 76.66 MPa
@Strain 1.60 %,
Temperature 80.0 °C		11120 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 76.79 MPa
@Strain 2.20 %,
Temperature 120 °C		11140 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 76.87 MPa
@Strain 3.20 %,
Temperature 150 °C		11150 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 76.92 MPa
@Strain 1.50 %,
Temperature 100 °C		11160 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 77.28 MPa
@Strain 1.90 %,
Temperature 120 °C		11210 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 77.49 MPa
@Strain 3.30 %,
Temperature 150 °C		11240 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 77.58 MPa
@Strain 2.40 %,
Temperature 150 °C		11250 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 77.87 MPa
@Strain 3.40 %,
Temperature 150 °C		11290 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 78.25 MPa
@Strain 2.30 %,
Temperature 120 °C		11350 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 78.3 MPa
@Strain 3.50 %,
Temperature 150 °C		11400 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 78.6 MPa
@Strain 3.60 %,
Temperature 150 °C		11400 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 78.87 MPa
@Strain 1.90 %,
Temperature 100 °C		11440 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 78.9 MPa
@Strain 2.50 %,
Temperature 150 °C		11400 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 79.0 MPa
@Strain 3.70 %,
Temperature 150 °C		11500 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 79.3 MPa
@Strain 3.80 %,
Temperature 150 °C		11500 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 79.31 MPa
@Strain 1.70 %,
Temperature 80.0 °C		11500 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 79.38 MPa
@Strain 2.00 %,
Temperature 120 °C		11510 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 79.48 MPa
@Strain 1.30 %,
Temperature 80.0 °C		11530 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 79.57 MPa
@Strain 1.50 %,
Temperature 60.0 °C		11540 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 79.6 MPa
@Strain 3.90 %,
Temperature 150 °C		11500 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 79.65 MPa
@Strain 2.40 %,
Temperature 120 °C		11550 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 79.7 MPa
@Strain 0.600 %,
Temperature 23.0 °C		11600 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.87 MPa
@Strain 1.60 %,
Temperature 100 °C		11580 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 79.9 MPa
@Strain 4.00 %,
Temperature 150 °C		11600 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 80.23 MPa
@Strain 2.60 %,
Temperature 150 °C		11640 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 80.59 MPa
@Strain 0.600 %,
Temperature 0.000 °C		11690 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 80.69 MPa
@Strain 0.600 %,
Temperature -40.0 °C		11700 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.83 MPa
@Strain 0.900 %,
Temperature 60.0 °C		11720 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.87 MPa
@Strain 2.00 %,
Temperature 100 °C		11730 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 80.97 MPa
@Strain 1.00 %,
Temperature 23.0 °C		11740 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.01 MPa
@Strain 2.50 %,
Temperature 120 °C		11750 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.39 MPa
@Strain 2.10 %,
Temperature 120 °C		11800 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 81.43 MPa
@Strain 2.70 %,
Temperature 150 °C		11810 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 81.73 MPa
@Strain 1.80 %,
Temperature 80.0 °C		11850 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 82.23 MPa
@Strain 2.60 %,
Temperature 120 °C		11930 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 82.49 MPa
@Strain 2.80 %,
Temperature 150 °C		11960 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 82.6 MPa
@Strain 1.70 %,
Temperature 100 °C		12000 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.66 MPa
@Strain 1.60 %,
Temperature 60.0 °C		11990 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 82.86 MPa
@Strain 2.10 %,
Temperature 100 °C		12020 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 83.24 MPa
@Strain 1.40 %,
Temperature 80.0 °C		12070 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 83.31 MPa
@Strain 2.20 %,
Temperature 120 °C		12080 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 83.42 MPa
@Strain 2.70 %,
Temperature 120 °C		12100 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 83.61 MPa
@Strain 2.90 %,
Temperature 150 °C		12130 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 84.05 MPa
@Strain 0.600 %,
Temperature -40.0 °C		12190 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 84.18 MPa
@Strain 1.90 %,
Temperature 80.0 °C		12210 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 84.46 MPa
@Strain 2.80 %,
Temperature 120 °C		12250 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 84.67 MPa
@Strain 2.20 %,
Temperature 100 °C		12280 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 84.68 MPa
@Strain 3.00 %,
Temperature 150 °C		12280 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 85.1 MPa
@Strain 2.30 %,
Temperature 120 °C		12300 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 85.16 MPa
@Strain 1.80 %,
Temperature 100 °C		12350 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 85.48 MPa
@Strain 2.90 %,
Temperature 120 °C		12400 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 85.67 MPa
@Strain 3.10 %,
Temperature 150 °C		12430 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 85.68 MPa
@Strain 1.70 %,
Temperature 60.0 °C		12430 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 85.93 MPa
@Strain 0.700 %,
Temperature 0.000 °C		12460 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.26 MPa
@Strain 1.10 %,
Temperature 23.0 °C		12510 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 86.4 MPa
@Strain 3.00 %,
Temperature 120 °C		12500 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 86.48 MPa
@Strain 2.30 %,
Temperature 100 °C		12540 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 86.5 MPa
@Strain 2.00 %,
Temperature 80.0 °C		12500 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 86.65 MPa
@Strain 3.20 %,
Temperature 150 °C		12570 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 86.71 MPa
@Strain 1.50 %,
Temperature 80.0 °C		12580 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 86.88 MPa
@Strain 2.40 %,
Temperature 120 °C		12600 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 87.23 MPa
@Strain 3.10 %,
Temperature 120 °C		12650 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 87.29 MPa
@Strain 1.00 %,
Temperature 60.0 °C		12660 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 87.44 MPa
@Strain 3.30 %,
Temperature 150 °C		12680 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 87.68 MPa
@Strain 1.90 %,
Temperature 100 °C		12720 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 88.04 MPa
@Strain 3.20 %,
Temperature 120 °C		12770 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 88.04 MPa
@Strain 2.40 %,
Temperature 100 °C		12770 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 88.26 MPa
@Strain 3.40 %,
Temperature 150 °C		12800 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 88.44 MPa
@Strain 1.80 %,
Temperature 60.0 °C		12830 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 88.52 MPa
@Strain 2.50 %,
Temperature 120 °C		12840 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 88.62 MPa
@Strain 2.10 %,
Temperature 80.0 °C		12850 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 88.77 MPa
@Strain 3.30 %,
Temperature 120 °C		12880 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 89.11 MPa
@Strain 3.50 %,
Temperature 150 °C		12920 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 89.4 MPa
@Strain 3.40 %,
Temperature 120 °C		13000 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 89.48 MPa
@Strain 2.50 %,
Temperature 100 °C		12980 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 89.77 MPa
@Strain 3.60 %,
Temperature 150 °C		13020 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 89.94 MPa
@Strain 1.60 %,
Temperature 80.0 °C		13040 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 89.96 MPa
@Strain 3.50 %,
Temperature 120 °C		13050 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 90.01 MPa
@Strain 2.00 %,
Temperature 100 °C		13050 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 90.1 MPa
@Strain 2.60 %,
Temperature 120 °C		13100 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 90.43 MPa
@Strain 3.60 %,
Temperature 120 °C		13120 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 90.48 MPa
@Strain 3.70 %,
Temperature 150 °C		13120 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 90.6 MPa
@Strain 2.20 %,
Temperature 80.0 °C		13100 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 90.7 MPa
@Strain 3.70 %,
Temperature 120 °C		13200 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 90.83 MPa
@Strain 2.60 %,
Temperature 100 °C		13170 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 91.0 MPa
@Strain 3.80 %,
Temperature 120 °C		13200 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 91.15 MPa
@Strain 3.80 %,
Temperature 150 °C		13220 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 91.19 MPa
@Strain 1.90 %,
Temperature 60.0 °C		13230 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 91.2 MPa
@Strain 3.90 %,
Temperature 120 °C		13200 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 91.35 MPa
@Strain 1.20 %,
Temperature 23.0 °C		13250 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 91.4 MPa
@Strain 4.00 %,
Temperature 120 °C		13300 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 91.64 MPa
@Strain 0.700 %,
Temperature 23.0 °C		13290 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 91.73 MPa
@Strain 2.70 %,
Temperature 120 °C		13300 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 91.81 MPa
@Strain 3.90 %,
Temperature 150 °C		13320 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 92.16 MPa
@Strain 2.70 %,
Temperature 100 °C		13370 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 92.25 MPa
@Strain 2.10 %,
Temperature 100 °C		13380 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 92.26 MPa
@Strain 4.00 %,
Temperature 150 °C		13380 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 92.49 MPa
@Strain 2.30 %,
Temperature 80.0 °C		13410 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 92.66 MPa
@Strain 0.700 %,
Temperature 0.000 °C		13440 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.9 MPa
@Strain 4.10 %,
Temperature 150 °C		13500 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 93.06 MPa
@Strain 0.700 %,
Temperature -40.0 °C		13500 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.1 MPa
@Strain 2.80 %,
Temperature 120 °C		13500 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 93.14 MPa
@Strain 1.70 %,
Temperature 80.0 °C		13510 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 93.24 MPa
@Strain 1.10 %,
Temperature 60.0 °C		13520 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 93.3 MPa
@Strain 4.20 %,
Temperature 150 °C		13500 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 93.39 MPa
@Strain 2.80 %,
Temperature 100 °C		13550 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 93.79 MPa
@Strain 4.30 %,
Temperature 150 °C		13600 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 93.81 MPa
@Strain 2.00 %,
Temperature 60.0 °C		13610 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 94.01 MPa
@Strain 4.40 %,
Temperature 150 °C		13640 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 94.2 MPa
@Strain 4.50 %,
Temperature 150 °C		13700 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 94.3 MPa
@Strain 2.40 %,
Temperature 80.0 °C		13700 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.31 MPa
@Strain 4.60 %,
Temperature 150 °C		13680 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 94.36 MPa
@Strain 2.20 %,
Temperature 100 °C		13690 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 94.44 MPa
@Strain 4.70 %,
Temperature 150 °C		13700 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 94.46 MPa
@Strain 2.90 %,
Temperature 120 °C		13700 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 94.54 MPa
@Strain 4.80 %,
Temperature 150 °C		13710 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 94.59 MPa
@Strain 2.90 %,
Temperature 100 °C		13720 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 94.64 MPa
@Strain 4.90 %,
Temperature 150 °C		13730 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 94.74 MPa
@Strain 5.00 %,
Temperature 150 °C		13740 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 95.7 MPa
@Strain 3.00 %,
Temperature 100 °C		13900 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 95.86 MPa
@Strain 3.00 %,
Temperature 120 °C		13900 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 95.99 MPa
@Strain 1.30 %,
Temperature 23.0 °C		13920 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 96.06 MPa
@Strain 2.50 %,
Temperature 80.0 °C		13930 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 96.12 MPa
@Strain 1.80 %,
Temperature 80.0 °C		13940 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 96.22 MPa
@Strain 2.10 %,
Temperature 60.0 °C		13960 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 96.26 MPa
@Strain 0.800 %,
Temperature 0.000 °C		13960 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 96.49 MPa
@Strain 2.30 %,
Temperature 100 °C		13990 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 96.61 MPa
@Strain 3.10 %,
Temperature 100 °C		14010 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 97.16 MPa
@Strain 3.10 %,
Temperature 120 °C		14090 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 97.41 MPa
@Strain 0.700 %,
Temperature -40.0 °C		14130 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.51 MPa
@Strain 3.20 %,
Temperature 100 °C		14140 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 97.66 MPa
@Strain 2.60 %,
Temperature 80.0 °C		14160 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 98.28 MPa
@Strain 3.20 %,
Temperature 120 °C		14250 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 98.38 MPa
@Strain 2.40 %,
Temperature 100 °C		14270 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 98.39 MPa
@Strain 3.30 %,
Temperature 100 °C		14270 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 98.47 MPa
@Strain 2.20 %,
Temperature 60.0 °C		14280 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 98.75 MPa
@Strain 1.20 %,
Temperature 60.0 °C		14320 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 98.88 MPa
@Strain 1.90 %,
Temperature 80.0 °C		14340 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 99.04 MPa
@Strain 3.40 %,
Temperature 100 °C		14360 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 99.14 MPa
@Strain 2.70 %,
Temperature 80.0 °C		14380 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 99.56 MPa
@Strain 3.30 %,
Temperature 120 °C		14440 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 99.74 MPa
@Strain 3.50 %,
Temperature 100 °C		14470 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 100.29 MPa
@Strain 2.50 %,
Temperature 100 °C		14546 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 100.42 MPa
@Strain 3.60 %,
Temperature 100 °C		14565 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 100.5 MPa
@Strain 2.80 %,
Temperature 80.0 °C		14580 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 100.58 MPa
@Strain 1.40 %,
Temperature 23.0 °C		14588 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 100.59 MPa
@Strain 3.40 %,
Temperature 120 °C		14589 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 100.74 MPa
@Strain 2.30 %,
Temperature 60.0 °C		14611 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.9 MPa
@Strain 3.70 %,
Temperature 100 °C		14630 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 101.2 MPa
@Strain 3.80 %,
Temperature 100 °C		14680 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 101.4 MPa
@Strain 3.90 %,
Temperature 100 °C		14710 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 101.48 MPa
@Strain 2.00 %,
Temperature 80.0 °C		14718 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 101.6 MPa
@Strain 4.00 %,
Temperature 100 °C		14740 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 101.66 MPa
@Strain 3.50 %,
Temperature 120 °C		14745 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 101.8 MPa
@Strain 2.90 %,
Temperature 80.0 °C		14760 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 102.08 MPa
@Strain 2.60 %,
Temperature 100 °C		14805 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 102.64 MPa
@Strain 3.60 %,
Temperature 120 °C		14887 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 102.87 MPa
@Strain 2.40 %,
Temperature 60.0 °C		14920 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 103.01 MPa
@Strain 3.00 %,
Temperature 80.0 °C		14940 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 103.1 MPa
@Strain 0.800 %,
Temperature 23.0 °C		14950 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.61 MPa
@Strain 3.70 %,
Temperature 120 °C		15027 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 103.63 MPa
@Strain 2.70 %,
Temperature 100 °C		15030 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 103.67 MPa
@Strain 1.30 %,
Temperature 60.0 °C		15036 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 103.92 MPa
@Strain 2.10 %,
Temperature 80.0 °C		15072 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 104.13 MPa
@Strain 3.10 %,
Temperature 80.0 °C		15103 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 104.32 MPa
@Strain 3.80 %,
Temperature 120 °C		15130 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 104.35 MPa
@Strain 0.800 %,
Temperature 0.000 °C		15135 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 104.5 MPa
@Strain 0.800 %,
Temperature -40.0 °C		15160 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 104.79 MPa
@Strain 2.50 %,
Temperature 60.0 °C		15199 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 104.88 MPa
@Strain 1.50 %,
Temperature 23.0 °C		15212 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 105.14 MPa
@Strain 3.90 %,
Temperature 120 °C		15249 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 105.15 MPa
@Strain 3.20 %,
Temperature 80.0 °C		15251 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 105.16 MPa
@Strain 2.80 %,
Temperature 100 °C		15252 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 106.01 MPa
@Strain 4.00 %,
Temperature 120 °C		15375 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 106.12 MPa
@Strain 0.900 %,
Temperature 0.000 °C		15391 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 106.16 MPa
@Strain 3.30 %,
Temperature 80.0 °C		15397 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 106.21 MPa
@Strain 2.20 %,
Temperature 80.0 °C		15404 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 106.61 MPa
@Strain 2.60 %,
Temperature 60.0 °C		15463 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 106.7 MPa
@Strain 4.10 %,
Temperature 120 °C		15480 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 106.75 MPa
@Strain 2.90 %,
Temperature 100 °C		15483 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 107.1 MPa
@Strain 3.40 %,
Temperature 80.0 °C		15530 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 107.33 MPa
@Strain 4.20 %,
Temperature 120 °C		15567 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 107.86 MPa
@Strain 3.50 %,
Temperature 80.0 °C		15644 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 108.02 MPa
@Strain 4.30 %,
Temperature 120 °C		15667 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 108.21 MPa
@Strain 3.00 %,
Temperature 100 °C		15695 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 108.28 MPa
@Strain 2.70 %,
Temperature 60.0 °C		15705 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 108.29 MPa
@Strain 1.40 %,
Temperature 60.0 °C		15706 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 108.49 MPa
@Strain 4.40 %,
Temperature 120 °C		15735 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 108.54 MPa
@Strain 2.30 %,
Temperature 80.0 °C		15742 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 108.54 MPa
@Strain 3.60 %,
Temperature 80.0 °C		15742 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 108.77 MPa
@Strain 1.60 %,
Temperature 23.0 °C		15776 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 109.06 MPa
@Strain 4.50 %,
Temperature 120 °C		15818 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 109.2 MPa
@Strain 3.70 %,
Temperature 80.0 °C		15840 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 109.57 MPa
@Strain 3.10 %,
Temperature 100 °C		15892 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 109.61 MPa
@Strain 4.60 %,
Temperature 120 °C		15898 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 109.7 MPa
@Strain 3.80 %,
Temperature 80.0 °C		15910 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 109.99 MPa
@Strain 4.70 %,
Temperature 120 °C		15953 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 110 MPa
@Strain 2.80 %,
Temperature 60.0 °C		16000 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 110.1 MPa
@Strain 3.90 %,
Temperature 80.0 °C		15970 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 110.26 MPa
@Strain 0.800 %,
Temperature -40.0 °C		15992 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.4 MPa
@Strain 4.00 %,
Temperature 80.0 °C		16010 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 110.43 MPa
@Strain 4.80 %,
Temperature 120 °C		16017 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 110.7 MPa
@Strain 4.90 %,
Temperature 120 °C		16060 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 110.73 MPa
@Strain 2.40 %,
Temperature 80.0 °C		16060 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 110.79 MPa
@Strain 3.20 %,
Temperature 100 °C		16069 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 111 MPa
@Strain 5.00 %,
Temperature 120 °C		16100 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 111.63 MPa
@Strain 2.90 %,
Temperature 60.0 °C		16191 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 111.91 MPa
@Strain 3.30 %,
Temperature 100 °C		16231 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 112.47 MPa
@Strain 1.70 %,
Temperature 23.0 °C		16312 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 112.66 MPa
@Strain 1.50 %,
Temperature 60.0 °C		16340 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 112.73 MPa
@Strain 2.50 %,
Temperature 80.0 °C		16350 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 113.04 MPa
@Strain 3.40 %,
Temperature 100 °C		16395 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 113.07 MPa
@Strain 3.00 %,
Temperature 60.0 °C		16399 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 113.7 MPa
@Strain 0.900 %,
Temperature 23.0 °C		16490 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.14 MPa
@Strain 3.50 %,
Temperature 100 °C		16555 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 114.41 MPa
@Strain 3.10 %,
Temperature 60.0 °C		16594 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 114.72 MPa
@Strain 2.60 %,
Temperature 80.0 °C		16639 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 115.05 MPa
@Strain 3.60 %,
Temperature 100 °C		16687 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 115.08 MPa
@Strain 1.00 %,
Temperature 0.000 °C		16691 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.5 MPa
@Strain 0.900 %,
Temperature 0.000 °C		16750 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 115.64 MPa
@Strain 3.20 %,
Temperature 60.0 °C		16772 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 115.9 MPa
@Strain 3.70 %,
Temperature 100 °C		16810 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 115.93 MPa
@Strain 1.80 %,
Temperature 23.0 °C		16814 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 116.54 MPa
@Strain 0.900 %,
Temperature -40.0 °C		16903 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116.64 MPa
@Strain 1.60 %,
Temperature 60.0 °C		16917 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 116.68 MPa
@Strain 2.70 %,
Temperature 80.0 °C		16923 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 116.73 MPa
@Strain 3.80 %,
Temperature 100 °C		16930 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 116.79 MPa
@Strain 3.30 %,
Temperature 60.0 °C		16939 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 117.41 MPa
@Strain 3.90 %,
Temperature 100 °C		17029 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 117.85 MPa
@Strain 3.40 %,
Temperature 60.0 °C		17093 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 118.1 MPa
@Strain 4.00 %,
Temperature 100 °C		17130 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 118.61 MPa
@Strain 2.80 %,
Temperature 80.0 °C		17203 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 118.71 MPa
@Strain 4.10 %,
Temperature 100 °C		17217 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 118.98 MPa
@Strain 3.50 %,
Temperature 60.0 °C		17257 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 119.1 MPa
@Strain 4.20 %,
Temperature 100 °C		17270 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 119.51 MPa
@Strain 1.90 %,
Temperature 23.0 °C		17333 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 119.52 MPa
@Strain 4.30 %,
Temperature 100 °C		17335 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 119.82 MPa
@Strain 3.60 %,
Temperature 60.0 °C		17378 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 119.89 MPa
@Strain 4.40 %,
Temperature 100 °C		17389 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 120.15 MPa
@Strain 2.90 %,
Temperature 80.0 °C		17426 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 120.18 MPa
@Strain 1.70 %,
Temperature 60.0 °C		17431 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 120.28 MPa
@Strain 4.50 %,
Temperature 100 °C		17445 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 120.6 MPa
@Strain 3.70 %,
Temperature 60.0 °C		17490 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 121.3 MPa
@Strain 3.80 %,
Temperature 60.0 °C		17590 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 121.74 MPa
@Strain 3.00 %,
Temperature 80.0 °C		17657 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 121.9 MPa
@Strain 3.90 %,
Temperature 60.0 °C		17680 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 122.5 MPa
@Strain 4.00 %,
Temperature 60.0 °C		17770 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 122.85 MPa
@Strain 2.00 %,
Temperature 23.0 °C		17818 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 122.91 MPa
@Strain 0.900 %,
Temperature -40.0 °C		17827 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 123.38 MPa
@Strain 3.10 %,
Temperature 80.0 °C		17895 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 123.64 MPa
@Strain 1.10 %,
Temperature 0.000 °C		17932 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 123.77 MPa
@Strain 1.80 %,
Temperature 60.0 °C		17951 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 123.97 MPa
@Strain 1.00 %,
Temperature 23.0 °C		17980 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 124.71 MPa
@Strain 3.20 %,
Temperature 80.0 °C		18088 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 125.82 MPa
@Strain 2.10 %,
Temperature 23.0 °C		18249 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 126.05 MPa
@Strain 3.30 %,
Temperature 80.0 °C		18282 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 126.88 MPa
@Strain 1.00 %,
Temperature 0.000 °C		18402 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 127.12 MPa
@Strain 1.90 %,
Temperature 60.0 °C		18437 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 127.23 MPa
@Strain 3.40 %,
Temperature 80.0 °C		18453 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 128.3 MPa
@Strain 3.50 %,
Temperature 80.0 °C		18610 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 128.52 MPa
@Strain 1.00 %,
Temperature -40.0 °C		18640 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 128.77 MPa
@Strain 2.20 %,
Temperature 23.0 °C		18677 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.4 MPa
@Strain 3.60 %,
Temperature 80.0 °C		18770 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 130.04 MPa
@Strain 2.00 %,
Temperature 60.0 °C		18861 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 130.22 MPa
@Strain 3.70 %,
Temperature 80.0 °C		18887 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 131.13 MPa
@Strain 3.80 %,
Temperature 80.0 °C		19019 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 131.48 MPa
@Strain 1.20 %,
Temperature 0.000 °C		19070 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 131.6 MPa
@Strain 2.30 %,
Temperature 23.0 °C		19090 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 131.88 MPa
@Strain 3.90 %,
Temperature 80.0 °C		19128 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 132.53 MPa
@Strain 4.00 %,
Temperature 80.0 °C		19222 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 132.82 MPa
@Strain 2.10 %,
Temperature 60.0 °C		19264 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 133.19 MPa
@Strain 4.10 %,
Temperature 80.0 °C		19318 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 133.59 MPa
@Strain 1.10 %,
Temperature 23.0 °C		19376 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 133.68 MPa
@Strain 4.20 %,
Temperature 80.0 °C		19389 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 134.12 MPa
@Strain 4.30 %,
Temperature 80.0 °C		19452 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 134.29 MPa
@Strain 2.40 %,
Temperature 23.0 °C		19477 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 134.39 MPa
@Strain 4.40 %,
Temperature 80.0 °C		19492 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 134.73 MPa
@Strain 4.50 %,
Temperature 80.0 °C		19541 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 134.79 MPa
@Strain 1.00 %,
Temperature -40.0 °C		19550 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 135.69 MPa
@Strain 2.20 %,
Temperature 60.0 °C		19680 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 136.88 MPa
@Strain 2.50 %,
Temperature 23.0 °C		19853 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 137.76 MPa
@Strain 1.10 %,
Temperature 0.000 °C		19980 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 138.37 MPa
@Strain 2.30 %,
Temperature 60.0 °C		20069 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 138.76 MPa
@Strain 1.30 %,
Temperature 0.000 °C		20125 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 139.47 MPa
@Strain 2.60 %,
Temperature 23.0 °C		20228 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 139.97 MPa
@Strain 1.10 %,
Temperature -40.0 °C		20301 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 140.8 MPa
@Strain 2.40 %,
Temperature 60.0 °C		20420 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 141.73 MPa
@Strain 2.70 %,
Temperature 23.0 °C		20556 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 142.47 MPa
@Strain 1.20 %,
Temperature 23.0 °C		20664 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 142.96 MPa
@Strain 2.50 %,
Temperature 60.0 °C		20735 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 143.9 MPa
@Strain 2.80 %,
Temperature 23.0 °C		20870 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 145.23 MPa
@Strain 2.60 %,
Temperature 60.0 °C		21064 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 145.33 MPa
@Strain 1.40 %,
Temperature 0.000 °C		21078 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 145.89 MPa
@Strain 2.90 %,
Temperature 23.0 °C		21160 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 146.16 MPa
@Strain 1.10 %,
Temperature -40.0 °C		21199 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 147.13 MPa
@Strain 2.70 %,
Temperature 60.0 °C		21339 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 147.73 MPa
@Strain 3.00 %,
Temperature 23.0 °C		21426 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 148.01 MPa
@Strain 1.20 %,
Temperature 0.000 °C		21467 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 148.88 MPa
@Strain 2.80 %,
Temperature 60.0 °C		21593 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 149.53 MPa
@Strain 3.10 %,
Temperature 23.0 °C		21688 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 150.72 MPa
@Strain 2.90 %,
Temperature 60.0 °C		21860 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 150.79 MPa
@Strain 1.30 %,
Temperature 23.0 °C		21870 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 150.93 MPa
@Strain 3.20 %,
Temperature 23.0 °C		21891 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 150.94 MPa
@Strain 1.20 %,
Temperature -40.0 °C		21892 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 151.55 MPa
@Strain 1.50 %,
Temperature 0.000 °C		21981 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 152.28 MPa
@Strain 3.00 %,
Temperature 60.0 °C		22086 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 152.48 MPa
@Strain 3.30 %,
Temperature 23.0 °C		22115 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 153.66 MPa
@Strain 3.10 %,
Temperature 60.0 °C		22287 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 153.72 MPa
@Strain 3.40 %,
Temperature 23.0 °C		22295 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 155.03 MPa
@Strain 3.50 %,
Temperature 23.0 °C		22485 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 155.03 MPa
@Strain 3.20 %,
Temperature 60.0 °C		22485 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 155.91 MPa
@Strain 3.60 %,
Temperature 23.0 °C		22613 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 156.25 MPa
@Strain 3.30 %,
Temperature 60.0 °C		22662 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 156.9 MPa
@Strain 3.70 %,
Temperature 23.0 °C		22760 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 157.04 MPa
@Strain 1.20 %,
Temperature -40.0 °C		22777 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 157.18 MPa
@Strain 3.40 %,
Temperature 60.0 °C		22797 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 157.34 MPa
@Strain 1.60 %,
Temperature 0.000 °C		22820 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 157.6 MPa
@Strain 3.80 %,
Temperature 23.0 °C		22860 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 157.81 MPa
@Strain 1.30 %,
Temperature 0.000 °C		22888 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 158.07 MPa
@Strain 3.50 %,
Temperature 60.0 °C		22926 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 158.2 MPa
@Strain 3.90 %,
Temperature 23.0 °C		22950 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 158.5 MPa
@Strain 4.00 %,
Temperature 23.0 °C		22990 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 158.53 MPa
@Strain 1.40 %,
Temperature 23.0 °C		22993 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 158.95 MPa
@Strain 3.60 %,
Temperature 60.0 °C		23054 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 159.7 MPa
@Strain 3.70 %,
Temperature 60.0 °C		23160 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 159.97 MPa
@Strain 3.80 %,
Temperature 60.0 °C		23202 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 160.13 MPa
@Strain 3.90 %,
Temperature 60.0 °C		23225 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 160.2 MPa
@Strain 4.00 %,
Temperature 60.0 °C		23240 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 161.78 MPa
@Strain 1.30 %,
Temperature -40.0 °C		23464 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 163.11 MPa
@Strain 1.70 %,
Temperature 0.000 °C		23657 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 165.82 MPa
@Strain 1.50 %,
Temperature 23.0 °C		24050 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 167.01 MPa
@Strain 1.40 %,
Temperature 0.000 °C		24223 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 167.47 MPa
@Strain 1.30 %,
Temperature -40.0 °C		24290 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 168.71 MPa
@Strain 1.80 %,
Temperature 0.000 °C		24469 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 171.8 MPa
@Strain 1.40 %,
Temperature -40.0 °C		24920 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 172.43 MPa
@Strain 1.60 %,
Temperature 23.0 °C		25009 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 173.54 MPa
@Strain 1.90 %,
Temperature 0.000 °C		25170 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 175.47 MPa
@Strain 1.50 %,
Temperature 0.000 °C		25450 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 177.22 MPa
@Strain 1.40 %,
Temperature -40.0 °C		25704 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 178.3 MPa
@Strain 2.00 %,
Temperature 0.000 °C		25860 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 178.64 MPa
@Strain 1.70 %,
Temperature 23.0 °C		25910 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 181.56 MPa
@Strain 1.50 %,
Temperature -40.0 °C		26333 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 182.57 MPa
@Strain 2.10 %,
Temperature 0.000 °C		26480 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 183.6 MPa
@Strain 1.60 %,
Temperature 0.000 °C		26630 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 184.3 MPa
@Strain 1.80 %,
Temperature 23.0 °C		26730 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 186.2 MPa
@Strain 1.50 %,
Temperature -40.0 °C		27010 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 186.41 MPa
@Strain 2.20 %,
Temperature 0.000 °C		27037 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 189.49 MPa
@Strain 1.90 %,
Temperature 23.0 °C		27483 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 190.21 MPa
@Strain 2.30 %,
Temperature 0.000 °C		27588 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 190.75 MPa
@Strain 1.60 %,
Temperature -40.0 °C		27666 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 191.03 MPa
@Strain 1.70 %,
Temperature 0.000 °C		27707 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 193.7 MPa
@Strain 2.40 %,
Temperature 0.000 °C		28090 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 193.97 MPa
@Strain 2.00 %,
Temperature 23.0 °C		28133 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 194.89 MPa
@Strain 1.60 %,
Temperature -40.0 °C		28266 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 196.77 MPa
@Strain 2.50 %,
Temperature 0.000 °C		28539 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 198.16 MPa
@Strain 1.80 %,
Temperature 0.000 °C		28741 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 198.43 MPa
@Strain 2.10 %,
Temperature 23.0 °C		28780 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 199.66 MPa
@Strain 2.60 %,
Temperature 0.000 °C		28958 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 199.71 MPa
@Strain 1.70 %,
Temperature -40.0 °C		28966 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 202.28 MPa
@Strain 2.20 %,
Temperature 23.0 °C		29338 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 202.46 MPa
@Strain 2.70 %,
Temperature 0.000 °C		29364 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 203.37 MPa
@Strain 1.70 %,
Temperature -40.0 °C		29496 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 204.78 MPa
@Strain 1.90 %,
Temperature 0.000 °C		29701 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 205.13 MPa
@Strain 2.80 %,
Temperature 0.000 °C		29752 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 205.82 MPa
@Strain 2.30 %,
Temperature 23.0 °C		29852 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 207.45 MPa
@Strain 2.90 %,
Temperature 0.000 °C		30088 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 208.02 MPa
@Strain 1.80 %,
Temperature -40.0 °C		30171 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 209.08 MPa
@Strain 2.40 %,
Temperature 23.0 °C		30325 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 209.51 MPa
@Strain 3.00 %,
Temperature 0.000 °C		30387 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 211.02 MPa
@Strain 2.00 %,
Temperature 0.000 °C		30606 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 211.15 MPa
@Strain 3.10 %,
Temperature 0.000 °C		30625 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 211.65 MPa
@Strain 1.80 %,
Temperature -40.0 °C		30697 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 212.05 MPa
@Strain 2.50 %,
Temperature 23.0 °C		30755 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 214.52 MPa
@Strain 2.60 %,
Temperature 23.0 °C		31114 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 216.1 MPa
@Strain 1.90 %,
Temperature -40.0 °C		31340 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 216.64 MPa
@Strain 2.70 %,
Temperature 23.0 °C		31421 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 216.65 MPa
@Strain 2.10 %,
Temperature 0.000 °C		31422 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 218.61 MPa
@Strain 2.80 %,
Temperature 23.0 °C		31707 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 219.36 MPa
@Strain 1.90 %,
Temperature -40.0 °C		31816 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 219.79 MPa
@Strain 2.90 %,
Temperature 23.0 °C		31878 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 220.5 MPa
@Strain 3.00 %,
Temperature 23.0 °C		31980 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 221.97 MPa
@Strain 2.20 %,
Temperature 0.000 °C		32194 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 223.58 MPa
@Strain 2.00 %,
Temperature -40.0 °C		32428 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 226.52 MPa
@Strain 2.00 %,
Temperature -40.0 °C		32854 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 227.04 MPa
@Strain 2.30 %,
Temperature 0.000 °C		32929 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 230.99 MPa
@Strain 2.10 %,
Temperature -40.0 °C		33502 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 231.53 MPa
@Strain 2.40 %,
Temperature 0.000 °C		33581 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 233.17 MPa
@Strain 2.10 %,
Temperature -40.0 °C		33819 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 235.88 MPa
@Strain 2.50 %,
Temperature 0.000 °C		34212 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 237.99 MPa
@Strain 2.20 %,
Temperature -40.0 °C		34518 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 239.72 MPa
@Strain 2.20 %,
Temperature -40.0 °C		34769 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 239.96 MPa
@Strain 2.60 %,
Temperature 0.000 °C		34803 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 243.85 MPa
@Strain 2.70 %,
Temperature 0.000 °C		35368 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 244.66 MPa
@Strain 2.30 %,
Temperature -40.0 °C		35485 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 245.8 MPa
@Strain 2.30 %,
Temperature -40.0 °C		35650 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 247.05 MPa
@Strain 2.80 %,
Temperature 0.000 °C		35832 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 249.31 MPa
@Strain 2.90 %,
Temperature 0.000 °C		36159 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 250.47 MPa
@Strain 3.00 %,
Temperature 0.000 °C		36328 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 250.86 MPa
@Strain 2.40 %,
Temperature -40.0 °C		36384 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 251.47 MPa
@Strain 2.40 %,
Temperature -40.0 °C		36473 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 256.67 MPa
@Strain 2.50 %,
Temperature -40.0 °C		37227 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 256.69 MPa
@Strain 2.50 %,
Temperature -40.0 °C		37230 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 261.68 MPa
@Strain 2.60 %,
Temperature -40.0 °C		37954 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 262.17 MPa
@Strain 2.60 %,
Temperature -40.0 °C		38025 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 266.33 MPa
@Strain 2.70 %,
Temperature -40.0 °C		38628 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 267.44 MPa
@Strain 2.70 %,
Temperature -40.0 °C		38789 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 270.9 MPa
@Strain 2.80 %,
Temperature -40.0 °C		39290 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 272.33 MPa
@Strain 2.80 %,
Temperature -40.0 °C		39498 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 275.21 MPa
@Strain 2.90 %,
Temperature -40.0 °C		39916 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 276.88 MPa
@Strain 2.90 %,
Temperature -40.0 °C		40158 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 278.5 MPa
@Strain 3.00 %,
Temperature -40.0 °C		40390 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 281.19 MPa
@Strain 3.00 %,
Temperature -40.0 °C		40783 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ISO 527
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  11.0 GPa
@Temperature 23.0 °C		1600 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 14.0 GPa
@Temperature 23.0 °C		2030 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength  260 MPa
@Temperature 23.0 °C		37700 psi
@Temperature 73.4 °F		50%RH; ISO 178
 285 MPa
@Temperature 23.0 °C		41300 psi
@Temperature 73.4 °F		DAM; ASTM D790
 340 MPa
@Temperature 23.0 °C		49300 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus  8.27 GPa
@Temperature 23.0 °C		1200 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 8.90 GPa
@Temperature 23.0 °C		1290 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 11.03 GPa
@Temperature 23.0 °C		1600 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 12.0 GPa
@Temperature 23.0 °C		1740 ksi
@Temperature 73.4 °F		DAM; ISO 178
Shear Strength 93.0 MPa
@Temperature 23.0 °C		13500 psi
@Temperature 73.4 °F		50%RH; ASTM D732
Izod Impact, Notched  1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.87 J/cm
@Temperature 23.0 °C		3.50 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  11.0 kJ/m²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 11.0 kJ/m²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 12.0 kJ/m²
@Temperature -30.0 °C		5.71 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 14.0 kJ/m²
@Temperature 23.0 °C		6.66 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 16.0 kJ/m²
@Temperature 23.0 °C		7.61 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  65.0 kJ/m²
@Temperature -30.0 °C		30.9 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 90.0 kJ/m²
@Temperature 23.0 °C		42.8 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
 105 kJ/m²
@Temperature -30.0 °C		50.0 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 105 kJ/m²
@Temperature 23.0 °C		50.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched  7.50 J/cm²
@Temperature -30.0 °C		35.7 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 8.50 J/cm²
@Temperature -30.0 °C		40.4 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 10.0 J/cm²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 10.5 J/cm²
@Temperature 23.0 °C		50.0 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  1.10 J/cm²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 1.10 J/cm²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.20 J/cm²
@Temperature -30.0 °C		5.71 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.20 J/cm²
@Temperature -30.0 °C		5.71 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 1.60 J/cm²
@Temperature 23.0 °C		7.61 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.90 J/cm²
@Temperature 23.0 °C		9.04 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 10800 MPa
@Temperature 23.0 °C		1.57e+6 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.0340 %,
Temperature 100 °C		435 psi
@Strain 0.0340 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.0370 %,
Temperature 100 °C		435 psi
@Strain 0.0370 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.0540 %,
Temperature 90.0 °C		508 psi
@Strain 0.0540 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.0440 %,
Temperature 90.0 °C		508 psi
@Strain 0.0440 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 4.50 MPa
@Strain 0.0660 %,
Temperature 60.0 °C		653 psi
@Strain 0.0660 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 4.50 MPa
@Strain 0.0540 %,
Temperature 60.0 °C		653 psi
@Strain 0.0540 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.0700 %,
Temperature 100 °C		870 psi
@Strain 0.0700 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.0750 %,
Temperature 100 °C		870 psi
@Strain 0.0750 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 6.50 MPa
@Strain 0.0540 %,
Temperature 23.0 °C		943 psi
@Strain 0.0540 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 6.50 MPa
@Strain 0.0600 %,
Temperature 23.0 °C		943 psi
@Strain 0.0600 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.109 %,
Temperature 90.0 °C		1020 psi
@Strain 0.109 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.0890 %,
Temperature 90.0 °C		1020 psi
@Strain 0.0890 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.131 %,
Temperature 60.0 °C		1310 psi
@Strain 0.131 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.115 %,
Temperature 100 °C		1310 psi
@Strain 0.115 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.107 %,
Temperature 100 °C		1310 psi
@Strain 0.107 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.108 %,
Temperature 60.0 °C		1310 psi
@Strain 0.108 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 10.5 MPa
@Strain 0.163 %,
Temperature 90.0 °C		1520 psi
@Strain 0.163 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 10.5 MPa
@Strain 0.134 %,
Temperature 90.0 °C		1520 psi
@Strain 0.134 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.158 %,
Temperature 100 °C		1740 psi
@Strain 0.158 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.146 %,
Temperature 100 °C		1740 psi
@Strain 0.146 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 13.0 MPa
@Strain 0.121 %,
Temperature 23.0 °C		1890 psi
@Strain 0.121 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 13.0 MPa
@Strain 0.110 %,
Temperature 23.0 °C		1890 psi
@Strain 0.110 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 13.5 MPa
@Strain 0.197 %,
Temperature 60.0 °C		1960 psi
@Strain 0.197 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 13.5 MPa
@Strain 0.163 %,
Temperature 60.0 °C		1960 psi
@Strain 0.163 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 14.0 MPa
@Strain 0.219 %,
Temperature 90.0 °C		2030 psi
@Strain 0.219 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 14.0 MPa
@Strain 0.179 %,
Temperature 90.0 °C		2030 psi
@Strain 0.179 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.205 %,
Temperature 100 °C		2180 psi
@Strain 0.205 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.189 %,
Temperature 100 °C		2180 psi
@Strain 0.189 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 17.5 MPa
@Strain 0.275 %,
Temperature 90.0 °C		2540 psi
@Strain 0.275 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 17.5 MPa
@Strain 0.225 %,
Temperature 90.0 °C		2540 psi
@Strain 0.225 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.263 %,
Temperature 60.0 °C		2610 psi
@Strain 0.263 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.236 %,
Temperature 100 °C		2610 psi
@Strain 0.236 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.258 %,
Temperature 100 °C		2610 psi
@Strain 0.258 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.217 %,
Temperature 60.0 °C		2610 psi
@Strain 0.217 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 19.5 MPa
@Strain 0.184 %,
Temperature 23.0 °C		2830 psi
@Strain 0.184 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 19.5 MPa
@Strain 0.167 %,
Temperature 23.0 °C		2830 psi
@Strain 0.167 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.332 %,
Temperature 90.0 °C		3050 psi
@Strain 0.332 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.316 %,
Temperature 100 °C		3050 psi
@Strain 0.316 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.289 %,
Temperature 100 °C		3050 psi
@Strain 0.289 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.272 %,
Temperature 90.0 °C		3050 psi
@Strain 0.272 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 22.5 MPa
@Strain 0.271 %,
Temperature 60.0 °C		3260 psi
@Strain 0.271 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 22.5 MPa
@Strain 0.329 %,
Temperature 60.0 °C		3260 psi
@Strain 0.329 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.383 %,
Temperature 100 °C		3480 psi
@Strain 0.383 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.349 %,
Temperature 100 °C		3480 psi
@Strain 0.349 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 24.5 MPa
@Strain 0.319 %,
Temperature 90.0 °C		3550 psi
@Strain 0.319 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 24.5 MPa
@Strain 0.390 %,
Temperature 90.0 °C		3550 psi
@Strain 0.390 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 26.0 MPa
@Strain 0.228 %,
Temperature 23.0 °C		3770 psi
@Strain 0.228 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 26.0 MPa
@Strain 0.251 %,
Temperature 23.0 °C		3770 psi
@Strain 0.251 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.394 %,
Temperature 60.0 °C		3920 psi
@Strain 0.394 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.417 %,
Temperature 100 °C		3920 psi
@Strain 0.417 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.460 %,
Temperature 100 °C		3920 psi
@Strain 0.460 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.326 %,
Temperature 60.0 °C		3920 psi
@Strain 0.326 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 28.0 MPa
@Strain 0.368 %,
Temperature 90.0 °C		4060 psi
@Strain 0.368 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 28.0 MPa
@Strain 0.450 %,
Temperature 90.0 °C		4060 psi
@Strain 0.450 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.549 %,
Temperature 100 °C		4350 psi
@Strain 0.549 %,
Temperature 212 °F		50%RH; 10h; Break; Isochronous; ISO 899
 30.0 MPa
@Strain 0.495 %,
Temperature 100 °C		4350 psi
@Strain 0.495 %,
Temperature 212 °F		50%RH; 1h; Break; Isochronous; ISO 899
 31.5 MPa
@Strain 0.417 %,
Temperature 90.0 °C		4570 psi
@Strain 0.417 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.511 %,
Temperature 90.0 °C		4570 psi
@Strain 0.511 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.460 %,
Temperature 60.0 °C		4570 psi
@Strain 0.460 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.380 %,
Temperature 60.0 °C		4570 psi
@Strain 0.380 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 32.5 MPa
@Strain 0.321 %,
Temperature 23.0 °C		4710 psi
@Strain 0.321 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 32.5 MPa
@Strain 0.292 %,
Temperature 23.0 °C		4710 psi
@Strain 0.292 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 35.0 MPa
@Strain 0.468 %,
Temperature 90.0 °C		5080 psi
@Strain 0.468 %,
Temperature 194 °F		50%RH; 1h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 0.574 %,
Temperature 90.0 °C		5080 psi
@Strain 0.574 %,
Temperature 194 °F		50%RH; 10h; Break; Isochronous; ISO 899
 36.0 MPa
@Strain 0.526 %,
Temperature 60.0 °C		5220 psi
@Strain 0.526 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 36.0 MPa
@Strain 0.434 %,
Temperature 60.0 °C		5220 psi
@Strain 0.434 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 39.0 MPa
@Strain 0.396 %,
Temperature 23.0 °C		5660 psi
@Strain 0.396 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 39.0 MPa
@Strain 0.360 %,
Temperature 23.0 °C		5660 psi
@Strain 0.360 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 40.5 MPa
@Strain 0.592 %,
Temperature 60.0 °C		5870 psi
@Strain 0.592 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 40.5 MPa
@Strain 0.488 %,
Temperature 60.0 °C		5870 psi
@Strain 0.488 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 45.0 MPa
@Strain 0.543 %,
Temperature 60.0 °C		6530 psi
@Strain 0.543 %,
Temperature 140 °F		50%RH; 1h; Break; Isochronous; ISO 899
 45.0 MPa
@Strain 0.658 %,
Temperature 60.0 °C		6530 psi
@Strain 0.658 %,
Temperature 140 °F		50%RH; 10h; Break; Isochronous; ISO 899
 45.5 MPa
@Strain 0.477 %,
Temperature 23.0 °C		6600 psi
@Strain 0.477 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 45.5 MPa
@Strain 0.435 %,
Temperature 23.0 °C		6600 psi
@Strain 0.435 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 52.0 MPa
@Strain 0.518 %,
Temperature 23.0 °C		7540 psi
@Strain 0.518 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 52.0 MPa
@Strain 0.567 %,
Temperature 23.0 °C		7540 psi
@Strain 0.567 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 58.5 MPa
@Strain 0.670 %,
Temperature 23.0 °C		8480 psi
@Strain 0.670 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 58.5 MPa
@Strain 0.612 %,
Temperature 23.0 °C		8480 psi
@Strain 0.612 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 65.0 MPa
@Strain 0.723 %,
Temperature 23.0 °C		9430 psi
@Strain 0.723 %,
Temperature 73.4 °F		50%RH; 1h; Break; Isochronous; ISO 899
 65.0 MPa
@Strain 0.792 %,
Temperature 23.0 °C		9430 psi
@Strain 0.792 %,
Temperature 73.4 °F		50%RH; 10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 7960 MPa
@Temperature 23.0 °C		1.15e+6 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.0474 %,
Temperature 100 °C		435 psi
@Strain 0.0474 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.0440 %,
Temperature 100 °C		435 psi
@Strain 0.0440 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.0405 %,
Temperature 100 °C		435 psi
@Strain 0.0405 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.0660 %,
Temperature 90.0 °C		508 psi
@Strain 0.0660 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.0800 %,
Temperature 90.0 °C		508 psi
@Strain 0.0800 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.0960 %,
Temperature 90.0 °C		508 psi
@Strain 0.0960 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 4.50 MPa
@Strain 0.124 %,
Temperature 60.0 °C		653 psi
@Strain 0.124 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 4.50 MPa
@Strain 0.102 %,
Temperature 60.0 °C		653 psi
@Strain 0.102 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 4.50 MPa
@Strain 0.0820 %,
Temperature 60.0 °C		653 psi
@Strain 0.0820 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.0890 %,
Temperature 100 °C		870 psi
@Strain 0.0890 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.0820 %,
Temperature 100 °C		870 psi
@Strain 0.0820 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.0960 %,
Temperature 100 °C		870 psi
@Strain 0.0960 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 6.50 MPa
@Strain 0.0740 %,
Temperature 23.0 °C		943 psi
@Strain 0.0740 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 6.50 MPa
@Strain 0.0660 %,
Temperature 23.0 °C		943 psi
@Strain 0.0660 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 6.50 MPa
@Strain 0.0820 %,
Temperature 23.0 °C		943 psi
@Strain 0.0820 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.161 %,
Temperature 90.0 °C		1020 psi
@Strain 0.161 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.132 %,
Temperature 90.0 °C		1020 psi
@Strain 0.132 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.192 %,
Temperature 90.0 °C		1020 psi
@Strain 0.192 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.247 %,
Temperature 60.0 °C		1310 psi
@Strain 0.247 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.148 %,
Temperature 100 °C		1310 psi
@Strain 0.148 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.163 %,
Temperature 60.0 °C		1310 psi
@Strain 0.163 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.126 %,
Temperature 100 °C		1310 psi
@Strain 0.126 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.204 %,
Temperature 60.0 °C		1310 psi
@Strain 0.204 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.137 %,
Temperature 100 °C		1310 psi
@Strain 0.137 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 10.5 MPa
@Strain 0.243 %,
Temperature 90.0 °C		1520 psi
@Strain 0.243 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 10.5 MPa
@Strain 0.199 %,
Temperature 90.0 °C		1520 psi
@Strain 0.199 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 10.5 MPa
@Strain 0.289 %,
Temperature 90.0 °C		1520 psi
@Strain 0.289 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.204 %,
Temperature 100 °C		1740 psi
@Strain 0.204 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.173 %,
Temperature 100 °C		1740 psi
@Strain 0.173 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.188 %,
Temperature 100 °C		1740 psi
@Strain 0.188 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 13.0 MPa
@Strain 0.134 %,
Temperature 23.0 °C		1890 psi
@Strain 0.134 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 13.0 MPa
@Strain 0.150 %,
Temperature 23.0 °C		1890 psi
@Strain 0.150 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 13.0 MPa
@Strain 0.166 %,
Temperature 23.0 °C		1890 psi
@Strain 0.166 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 13.5 MPa
@Strain 0.371 %,
Temperature 60.0 °C		1960 psi
@Strain 0.371 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 13.5 MPa
@Strain 0.306 %,
Temperature 60.0 °C		1960 psi
@Strain 0.306 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 13.5 MPa
@Strain 0.245 %,
Temperature 60.0 °C		1960 psi
@Strain 0.245 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 14.0 MPa
@Strain 0.267 %,
Temperature 90.0 °C		2030 psi
@Strain 0.267 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 14.0 MPa
@Strain 0.325 %,
Temperature 90.0 °C		2030 psi
@Strain 0.325 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 14.0 MPa
@Strain 0.387 %,
Temperature 90.0 °C		2030 psi
@Strain 0.387 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.267 %,
Temperature 100 °C		2180 psi
@Strain 0.267 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.245 %,
Temperature 100 °C		2180 psi
@Strain 0.245 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.224 %,
Temperature 100 °C		2180 psi
@Strain 0.224 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 17.5 MPa
@Strain 0.335 %,
Temperature 90.0 °C		2540 psi
@Strain 0.335 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 17.5 MPa
@Strain 0.409 %,
Temperature 90.0 °C		2540 psi
@Strain 0.409 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 17.5 MPa
@Strain 0.488 %,
Temperature 90.0 °C		2540 psi
@Strain 0.488 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.494 %,
Temperature 60.0 °C		2610 psi
@Strain 0.494 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.337 %,
Temperature 100 °C		2610 psi
@Strain 0.337 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.309 %,
Temperature 100 °C		2610 psi
@Strain 0.309 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.408 %,
Temperature 60.0 °C		2610 psi
@Strain 0.408 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.327 %,
Temperature 60.0 °C		2610 psi
@Strain 0.327 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.282 %,
Temperature 100 °C		2610 psi
@Strain 0.282 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 19.5 MPa
@Strain 0.228 %,
Temperature 23.0 °C		2830 psi
@Strain 0.228 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 19.5 MPa
@Strain 0.205 %,
Temperature 23.0 °C		2830 psi
@Strain 0.205 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 19.5 MPa
@Strain 0.253 %,
Temperature 23.0 °C		2830 psi
@Strain 0.253 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.495 %,
Temperature 90.0 °C		3050 psi
@Strain 0.495 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.347 %,
Temperature 100 °C		3050 psi
@Strain 0.347 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.405 %,
Temperature 90.0 °C		3050 psi
@Strain 0.405 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.381 %,
Temperature 100 °C		3050 psi
@Strain 0.381 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.417 %,
Temperature 100 °C		3050 psi
@Strain 0.417 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 21.0 MPa
@Strain 0.590 %,
Temperature 90.0 °C		3050 psi
@Strain 0.590 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 22.5 MPa
@Strain 0.618 %,
Temperature 60.0 °C		3260 psi
@Strain 0.618 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 22.5 MPa
@Strain 0.409 %,
Temperature 60.0 °C		3260 psi
@Strain 0.409 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 22.5 MPa
@Strain 0.510 %,
Temperature 60.0 °C		3260 psi
@Strain 0.510 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.422 %,
Temperature 100 °C		3480 psi
@Strain 0.422 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.465 %,
Temperature 100 °C		3480 psi
@Strain 0.465 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.509 %,
Temperature 100 °C		3480 psi
@Strain 0.509 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 24.5 MPa
@Strain 0.696 %,
Temperature 90.0 °C		3550 psi
@Strain 0.696 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 24.5 MPa
@Strain 0.477 %,
Temperature 90.0 °C		3550 psi
@Strain 0.477 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 24.5 MPa
@Strain 0.583 %,
Temperature 90.0 °C		3550 psi
@Strain 0.583 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 26.0 MPa
@Strain 0.278 %,
Temperature 23.0 °C		3770 psi
@Strain 0.278 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 26.0 MPa
@Strain 0.310 %,
Temperature 23.0 °C		3770 psi
@Strain 0.310 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 26.0 MPa
@Strain 0.344 %,
Temperature 23.0 °C		3770 psi
@Strain 0.344 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.612 %,
Temperature 60.0 °C		3920 psi
@Strain 0.612 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.490 %,
Temperature 60.0 °C		3920 psi
@Strain 0.490 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.508 %,
Temperature 100 °C		3920 psi
@Strain 0.508 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.616 %,
Temperature 100 °C		3920 psi
@Strain 0.616 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.561 %,
Temperature 100 °C		3920 psi
@Strain 0.561 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 27.0 MPa
@Strain 0.741 %,
Temperature 60.0 °C		3920 psi
@Strain 0.741 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 28.0 MPa
@Strain 0.804 %,
Temperature 90.0 °C		4060 psi
@Strain 0.804 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 28.0 MPa
@Strain 0.550 %,
Temperature 90.0 °C		4060 psi
@Strain 0.550 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 28.0 MPa
@Strain 0.673 %,
Temperature 90.0 °C		4060 psi
@Strain 0.673 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.674 %,
Temperature 100 °C		4350 psi
@Strain 0.674 %,
Temperature 212 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 30.0 MPa
@Strain 0.741 %,
Temperature 100 °C		4350 psi
@Strain 0.741 %,
Temperature 212 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 30.0 MPa
@Strain 0.608 %,
Temperature 100 °C		4350 psi
@Strain 0.608 %,
Temperature 212 °F		50%RH; 100h; Break; Isochronous; ISO 899
 31.5 MPa
@Strain 0.917 %,
Temperature 90.0 °C		4570 psi
@Strain 0.917 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.865 %,
Temperature 60.0 °C		4570 psi
@Strain 0.865 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.767 %,
Temperature 90.0 °C		4570 psi
@Strain 0.767 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.713 %,
Temperature 60.0 °C		4570 psi
@Strain 0.713 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.572 %,
Temperature 60.0 °C		4570 psi
@Strain 0.572 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 31.5 MPa
@Strain 0.626 %,
Temperature 90.0 °C		4570 psi
@Strain 0.626 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 32.5 MPa
@Strain 0.396 %,
Temperature 23.0 °C		4710 psi
@Strain 0.396 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 32.5 MPa
@Strain 0.356 %,
Temperature 23.0 °C		4710 psi
@Strain 0.356 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 32.5 MPa
@Strain 0.439 %,
Temperature 23.0 °C		4710 psi
@Strain 0.439 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 35.0 MPa
@Strain 1.03 %,
Temperature 90.0 °C		5080 psi
@Strain 1.03 %,
Temperature 194 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 0.864 %,
Temperature 90.0 °C		5080 psi
@Strain 0.864 %,
Temperature 194 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 0.704 %,
Temperature 90.0 °C		5080 psi
@Strain 0.704 %,
Temperature 194 °F		50%RH; 100h; Break; Isochronous; ISO 899
 36.0 MPa
@Strain 0.654 %,
Temperature 60.0 °C		5220 psi
@Strain 0.654 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 36.0 MPa
@Strain 0.815 %,
Temperature 60.0 °C		5220 psi
@Strain 0.815 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 36.0 MPa
@Strain 0.988 %,
Temperature 60.0 °C		5220 psi
@Strain 0.988 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 39.0 MPa
@Strain 0.541 %,
Temperature 23.0 °C		5660 psi
@Strain 0.541 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 39.0 MPa
@Strain 0.488 %,
Temperature 23.0 °C		5660 psi
@Strain 0.488 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 39.0 MPa
@Strain 0.440 %,
Temperature 23.0 °C		5660 psi
@Strain 0.440 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 40.5 MPa
@Strain 0.917 %,
Temperature 60.0 °C		5870 psi
@Strain 0.917 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 40.5 MPa
@Strain 0.736 %,
Temperature 60.0 °C		5870 psi
@Strain 0.736 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 40.5 MPa
@Strain 1.11 %,
Temperature 60.0 °C		5870 psi
@Strain 1.11 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 45.0 MPa
@Strain 1.24 %,
Temperature 60.0 °C		6530 psi
@Strain 1.24 %,
Temperature 140 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 45.0 MPa
@Strain 0.818 %,
Temperature 60.0 °C		6530 psi
@Strain 0.818 %,
Temperature 140 °F		50%RH; 100h; Break; Isochronous; ISO 899
 45.0 MPa
@Strain 1.02 %,
Temperature 60.0 °C		6530 psi
@Strain 1.02 %,
Temperature 140 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 45.5 MPa
@Strain 0.588 %,
Temperature 23.0 °C		6600 psi
@Strain 0.588 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 45.5 MPa
@Strain 0.530 %,
Temperature 23.0 °C		6600 psi
@Strain 0.530 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 45.5 MPa
@Strain 0.650 %,
Temperature 23.0 °C		6600 psi
@Strain 0.650 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 52.0 MPa
@Strain 0.770 %,
Temperature 23.0 °C		7540 psi
@Strain 0.770 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 52.0 MPa
@Strain 0.630 %,
Temperature 23.0 °C		7540 psi
@Strain 0.630 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 52.0 MPa
@Strain 0.697 %,
Temperature 23.0 °C		7540 psi
@Strain 0.697 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 58.5 MPa
@Strain 0.821 %,
Temperature 23.0 °C		8480 psi
@Strain 0.821 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 58.5 MPa
@Strain 0.742 %,
Temperature 23.0 °C		8480 psi
@Strain 0.742 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 58.5 MPa
@Strain 0.905 %,
Temperature 23.0 °C		8480 psi
@Strain 0.905 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 65.0 MPa
@Strain 1.06 %,
Temperature 23.0 °C		9430 psi
@Strain 1.06 %,
Temperature 73.4 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 65.0 MPa
@Strain 0.872 %,
Temperature 23.0 °C		9430 psi
@Strain 0.872 %,
Temperature 73.4 °F		50%RH; 100h; Break; Isochronous; ISO 899
 65.0 MPa
@Strain 0.964 %,
Temperature 23.0 °C		9430 psi
@Strain 0.964 %,
Temperature 73.4 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+12 ohm-cm
@Temperature 23.0 °C		1.00e+12 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance  1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  4.1
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.1
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.5
@Frequency 100 Hz,
Temperature 23.0 °C		4.5
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.9
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.9
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength 27.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		686 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.0145
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.0145
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.060
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.060
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index  600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  61.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		33.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 61.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		33.9 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 79.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		43.9 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 79.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		43.9 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 128 µm/m-°C
@Temperature 55.0 - 160 °C		71.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 128 µm/m-°C
@Temperature 55.0 - 160 °C		71.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 260 °C500 °FDAM; ASTM D648
 262 °C504 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 252 °C486 °FDAM; ASTM D648
 255 °C491 °FDAM; ISO 75-1/-2
Glass Transition Temp, Tg 80.0 °C176 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical with Impact  120 °C
@Thickness 0.710 mm		248 °F
@Thickness 0.0280 in		DAM; UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
Oxygen Index 23 %23 %DAM; ISO 4589-1/-2
Glow Wire Test  650 °C
@Thickness 0.710 mm		1200 °F
@Thickness 0.0280 in		DAM; IEC 60695-2-12
 650 °C
@Thickness 1.50 mm		1200 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 675 °C
@Thickness 1.50 mm		1250 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 675 °C
@Thickness 0.710 mm		1250 °F
@Thickness 0.0280 in		DAM; Ignition; IEC 60695-2-13
 700 °C
@Thickness 3.00 mm		1290 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 825 °C
@Thickness 3.00 mm		1520 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesCreep Resistance, GoodDAM
 General PurposeDAM
 LubricatedDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF43<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF43ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Electrical/Electronic ApplicationsDAM
 Industrial ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45476.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4