  3. PA66
  4. DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.39
  • 吸水率 [%]: 0.7
  • 成型收缩率 [%]: 0.002
  • 缺口冲击强度: 1.17
  • 弯曲模量 [MPa]: 6.205
  • 热变形温度 [℃]: 261.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.38 g/cc1.38 g/ccDAM; ASTM D792
Density 1.39 g/cc0.0502 lb/in³DAM; ISO 1183
Filler Content 33 %33 %DAM
Water Absorption  0.70 %
@Temperature 23.0 °C		0.70 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 1.2 %
@Temperature 23.0 °C		1.2 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
 1.8 %
@Temperature 23.0 °C		1.8 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 5.4 %
@Temperature 23.0 °C		5.4 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 5.7 %
@Temperature 23.0 °C		5.7 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0020 cm/cm
@Thickness 1.60 mm		0.0020 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0030 cm/cm
@Thickness 3.20 mm		0.0030 in/in
@Thickness 0.126 in		Flow; DAM
 0.0050 cm/cm
@Thickness 6.40 mm		0.0050 in/in
@Thickness 0.252 in		Flow; DAM
 0.010 cm/cm
@Thickness 1.60 mm		0.010 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.010 cm/cm
@Thickness 3.20 mm		0.010 in/in
@Thickness 0.126 in		Transverse; DAM
 0.011 cm/cm
@Thickness 6.40 mm		0.011 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
@Thickness 2.00 mm		0.011 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 101101DAM; ASTM D785
Tensile Strength at Break  140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		50%RH; ISO 527
 200 MPa
@Temperature 23.0 °C		29000 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  86.0 MPa
@Temperature 77.0 °C		12500 psi
@Temperature 171 °F		50%RH; ASTM D638
 110 MPa
@Temperature 77.0 °C		16000 psi
@Temperature 171 °F		DAM; ASTM D638
 124 MPa
@Temperature 23.0 °C		18000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 186 MPa
@Temperature 23.0 °C		27000 psi
@Temperature 73.4 °F		DAM; ASTM D638
 207 MPa
@Temperature -40.0 °C		30000 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 214 MPa
@Temperature -40.0 °C		31000 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  4.275 MPa
@Strain 0.100 %,
Temperature 140 °C		620.0 psi
@Strain 0.100 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 4.50 MPa
@Strain 0.100 %,
Temperature 150 °C		653 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.70 MPa
@Strain 0.100 %,
Temperature 120 °C		682 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.85 MPa
@Strain 0.100 %,
Temperature 120 °C		703 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.10 MPa
@Strain 0.100 %,
Temperature 100 °C		740 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.20 MPa
@Strain 0.100 %,
Temperature 100 °C		754 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.60 MPa
@Strain 0.100 %,
Temperature 80.0 °C		812 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.20 MPa
@Strain 0.100 %,
Temperature 60.0 °C		899 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.30 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1060 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 8.55 MPa
@Strain 0.200 %,
Temperature 140 °C		1240 psi
@Strain 0.200 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 8.80 MPa
@Strain 0.200 %,
Temperature 150 °C		1280 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.30 MPa
@Strain 0.200 %,
Temperature 120 °C		1350 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.70 MPa
@Strain 0.200 %,
Temperature 120 °C		1410 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.0 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1450 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 10.2 MPa
@Strain 0.200 %,
Temperature 100 °C		1480 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.3 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1490 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 10.4 MPa
@Strain 0.200 %,
Temperature 100 °C		1510 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.5 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1520 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 11.03 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1600 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1620 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 11.2 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1620 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.407 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1799.5 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.6 MPa
@Strain 0.300 %,
Temperature 150 °C		1830 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.825 MPa
@Strain 0.300 %,
Temperature 140 °C		1860.1 psi
@Strain 0.300 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 14.0 MPa
@Strain 0.300 %,
Temperature 120 °C		2030 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.6 MPa
@Strain 0.300 %,
Temperature 120 °C		2120 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.096 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2189.5 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.3 MPa
@Strain 0.300 %,
Temperature 100 °C		2220 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.4 MPa
@Strain 0.300 %,
Temperature 100 °C		2230 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.1 MPa
@Strain 0.300 %,
Temperature 80.0 °C		2340 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.732 MPa
@Strain 0.400 %,
Temperature 140 °C		2426.8 psi
@Strain 0.400 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 17.141 MPa
@Strain 0.400 %,
Temperature 150 °C		2486.1 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.5 MPa
@Strain 0.300 %,
Temperature 60.0 °C		2540 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.2 MPa
@Strain 0.400 %,
Temperature 120 °C		2640 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.2 MPa
@Strain 0.400 %,
Temperature 120 °C		2780 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.7 MPa
@Strain 0.400 %,
Temperature 100 °C		2860 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.0 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2900 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 20.325 MPa
@Strain 0.400 %,
Temperature 80.0 °C		2947.9 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.326 MPa
@Strain 0.400 %,
Temperature 100 °C		2948.0 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.5 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2970 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 20.8 MPa
@Strain 0.200 %,
Temperature 0.000 °C		3020 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 20.9 MPa
@Strain 0.500 %,
Temperature 140 °C		3030 psi
@Strain 0.500 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 21.09 MPa
@Strain 0.500 %,
Temperature 150 °C		3059 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.8 MPa
@Strain 0.200 %,
Temperature -40.0 °C		3160 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 21.805 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3162.6 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.1 MPa
@Strain 0.500 %,
Temperature 120 °C		3210 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.3 MPa
@Strain 0.200 %,
Temperature -40.0 °C		3230 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 22.534 MPa
@Strain 0.400 %,
Temperature 60.0 °C		3268.3 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.6 MPa
@Strain 0.500 %,
Temperature 120 °C		3420 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.4 MPa
@Strain 0.500 %,
Temperature 100 °C		3540 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.605 MPa
@Strain 0.600 %,
Temperature 140 °C		3568.7 psi
@Strain 0.600 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 24.653 MPa
@Strain 0.600 %,
Temperature 150 °C		3575.6 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.716 MPa
@Strain 0.500 %,
Temperature 100 °C		3584.8 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.4 MPa
@Strain 0.600 %,
Temperature 120 °C		3680 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.008 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3772.1 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.396 MPa
@Strain 0.500 %,
Temperature 60.0 °C		3973.5 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.9 MPa
@Strain 0.600 %,
Temperature 120 °C		4050 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.985 MPa
@Strain 0.700 %,
Temperature 140 °C		4058.9 psi
@Strain 0.700 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 28.12 MPa
@Strain 0.700 %,
Temperature 150 °C		4078 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.42 MPa
@Strain 0.600 %,
Temperature 100 °C		4122 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.636 MPa
@Strain 0.600 %,
Temperature 100 °C		4153.3 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.794 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4176.2 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.846 MPa
@Strain 0.700 %,
Temperature 120 °C		4183.8 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.9 MPa
@Strain 0.300 %,
Temperature 0.000 °C		4190 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 29.81 MPa
@Strain 0.300 %,
Temperature 23.0 °C		4324 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.728 MPa
@Strain 0.600 %,
Temperature 80.0 °C		4456.7 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.018 MPa
@Strain 0.800 %,
Temperature 140 °C		4498.8 psi
@Strain 0.800 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 31.298 MPa
@Strain 0.800 %,
Temperature 150 °C		4539.4 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 0.700 %,
Temperature 120 °C		4550 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.6 MPa
@Strain 0.300 %,
Temperature 0.000 °C		4580 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 32.07 MPa
@Strain 0.600 %,
Temperature 60.0 °C		4651 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.082 MPa
@Strain 0.800 %,
Temperature 120 °C		4653.1 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.3 MPa
@Strain 0.700 %,
Temperature 100 °C		4680 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.34 MPa
@Strain 0.700 %,
Temperature 100 °C		4691 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.6 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4730 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.6 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4730 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 33.954 MPa
@Strain 0.900 %,
Temperature 140 °C		4924.6 psi
@Strain 0.900 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 34.09 MPa
@Strain 0.900 %,
Temperature 150 °C		4944 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.967 MPa
@Strain 0.700 %,
Temperature 80.0 °C		5071.5 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.0 MPa
@Strain 0.800 %,
Temperature 120 °C		5080 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.224 MPa
@Strain 0.900 %,
Temperature 120 °C		5108.8 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.596 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5162.8 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.888 MPa
@Strain 0.800 %,
Temperature 100 °C		5205.1 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.06 MPa
@Strain 0.800 %,
Temperature 100 °C		5230 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.302 MPa
@Strain 1.00 %,
Temperature 140 °C		5265.2 psi
@Strain 1.00 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 36.465 MPa
@Strain 0.700 %,
Temperature 60.0 °C		5288.8 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 0.400 %,
Temperature 0.000 °C		5310 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 36.787 MPa
@Strain 1.00 %,
Temperature 150 °C		5335.5 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.2 MPa
@Strain 0.900 %,
Temperature 120 °C		5540 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.366 MPa
@Strain 1.00 %,
Temperature 120 °C		5564.5 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.82 MPa
@Strain 0.800 %,
Temperature 80.0 °C		5630 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.22 MPa
@Strain 0.900 %,
Temperature 100 °C		5688 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.32 MPa
@Strain 0.400 %,
Temperature 23.0 °C		5703 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 39.336 MPa
@Strain 1.10 %,
Temperature 140 °C		5705.2 psi
@Strain 1.10 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 39.4 MPa
@Strain 0.900 %,
Temperature 100 °C		5710 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.483 MPa
@Strain 1.10 %,
Temperature 150 °C		5726.5 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.486 MPa
@Strain 0.800 %,
Temperature 60.0 °C		5872.0 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.222 MPa
@Strain 1.10 %,
Temperature 120 °C		5978.8 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.3 MPa
@Strain 1.00 %,
Temperature 120 °C		5990 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.746 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6054.8 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.782 MPa
@Strain 1.20 %,
Temperature 140 °C		6060.0 psi
@Strain 1.20 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 41.89 MPa
@Strain 1.20 %,
Temperature 150 °C		6076 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.3 MPa
@Strain 0.400 %,
Temperature 0.000 °C		6140 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 42.356 MPa
@Strain 1.00 %,
Temperature 100 °C		6143.2 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.48 MPa
@Strain 0.900 %,
Temperature 80.0 °C		6161 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.73 MPa
@Strain 1.00 %,
Temperature 100 °C		6197 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 0.400 %,
Temperature -40.0 °C		6280 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.792 MPa
@Strain 1.20 %,
Temperature 120 °C		6351.5 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.882 MPa
@Strain 0.400 %,
Temperature -40.0 °C		6364.6 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.032 MPa
@Strain 1.30 %,
Temperature 140 °C		6386.3 psi
@Strain 1.30 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 1.10 %,
Temperature 120 °C		6400 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.105 MPa
@Strain 1.30 %,
Temperature 150 °C		6396.9 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 44.132 MPa
@Strain 0.900 %,
Temperature 60.0 °C		6400.8 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.394 MPa
@Strain 1.10 %,
Temperature 100 °C		6583.9 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.67 MPa
@Strain 1.10 %,
Temperature 100 °C		6624 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.755 MPa
@Strain 1.00 %,
Temperature 80.0 °C		6636.2 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.1 MPa
@Strain 0.500 %,
Temperature 0.000 °C		6690 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 46.267 MPa
@Strain 1.30 %,
Temperature 120 °C		6710.5 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 46.32 MPa
@Strain 1.40 %,
Temperature 150 °C		6718 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 46.381 MPa
@Strain 1.40 %,
Temperature 140 °C		6727.0 psi
@Strain 1.40 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 46.9 MPa
@Strain 1.20 %,
Temperature 120 °C		6800 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.617 MPa
@Strain 0.700 %,
Temperature 23.0 °C		6906.3 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.872 MPa
@Strain 1.00 %,
Temperature 60.0 °C		6943.3 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.942 MPa
@Strain 1.20 %,
Temperature 100 °C		6953.4 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.142 MPa
@Strain 1.50 %,
Temperature 140 °C		6982.4 psi
@Strain 1.50 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 48.246 MPa
@Strain 1.50 %,
Temperature 150 °C		6997.5 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 48.61 MPa
@Strain 1.20 %,
Temperature 100 °C		7050 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.647 MPa
@Strain 1.40 %,
Temperature 120 °C		7055.7 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 48.82 MPa
@Strain 0.500 %,
Temperature 23.0 °C		7081 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.03 MPa
@Strain 1.10 %,
Temperature 80.0 °C		7111 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 1.30 %,
Temperature 120 °C		7180 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.2 MPa
@Strain 1.30 %,
Temperature 100 °C		7280 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.269 MPa
@Strain 1.60 %,
Temperature 150 °C		7290.9 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 50.784 MPa
@Strain 1.60 %,
Temperature 140 °C		7365.6 psi
@Strain 1.60 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 50.837 MPa
@Strain 1.50 %,
Temperature 120 °C		7373.3 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 51.35 MPa
@Strain 1.30 %,
Temperature 100 °C		7448 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 51.425 MPa
@Strain 1.10 %,
Temperature 60.0 °C		7458.6 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.0 MPa
@Strain 1.40 %,
Temperature 120 °C		7540 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.154 MPa
@Strain 1.70 %,
Temperature 140 °C		7564.3 psi
@Strain 1.70 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 52.195 MPa
@Strain 1.70 %,
Temperature 150 °C		7570.3 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 52.209 MPa
@Strain 1.20 %,
Temperature 80.0 °C		7572.3 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.65 MPa
@Strain 1.40 %,
Temperature 100 °C		7636 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.836 MPa
@Strain 1.60 %,
Temperature 120 °C		7663.2 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 53.022 MPa
@Strain 0.800 %,
Temperature 23.0 °C		7690.2 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.9 MPa
@Strain 1.40 %,
Temperature 100 °C		7820 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 53.928 MPa
@Strain 1.80 %,
Temperature 150 °C		7821.6 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 1.50 %,
Temperature 120 °C		7860 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 0.500 %,
Temperature 0.000 °C		7890 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7900 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 54.51 MPa
@Strain 1.20 %,
Temperature 60.0 °C		7906 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.698 MPa
@Strain 1.80 %,
Temperature 140 °C		7933.3 psi
@Strain 1.80 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 54.93 MPa
@Strain 1.70 %,
Temperature 120 °C		7967 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 55.003 MPa
@Strain 1.30 %,
Temperature 80.0 °C		7977.5 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.37 MPa
@Strain 1.50 %,
Temperature 100 °C		8031 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.565 MPa
@Strain 1.90 %,
Temperature 150 °C		8059.0 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 55.705 MPa
@Strain 0.500 %,
Temperature -40.0 °C		8079.3 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.8 MPa
@Strain 0.600 %,
Temperature 0.000 °C		8090 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 56.166 MPa
@Strain 1.90 %,
Temperature 140 °C		8146.2 psi
@Strain 1.90 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 56.252 MPa
@Strain 1.50 %,
Temperature 100 °C		8158.7 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 56.5 MPa
@Strain 1.60 %,
Temperature 120 °C		8190 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.93 MPa
@Strain 1.80 %,
Temperature 120 °C		8257 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 57.202 MPa
@Strain 2.00 %,
Temperature 150 °C		8296.5 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 57.6 MPa
@Strain 0.600 %,
Temperature 23.0 °C		8350 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 57.689 MPa
@Strain 1.30 %,
Temperature 60.0 °C		8367.1 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.7 MPa
@Strain 1.40 %,
Temperature 80.0 °C		8370 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 58.054 MPa
@Strain 0.900 %,
Temperature 23.0 °C		8420.0 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.114 MPa
@Strain 1.60 %,
Temperature 100 °C		8428.7 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.221 MPa
@Strain 2.00 %,
Temperature 140 °C		8444.3 psi
@Strain 2.00 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 58.604 MPa
@Strain 1.60 %,
Temperature 100 °C		8499.8 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 58.647 MPa
@Strain 2.10 %,
Temperature 150 °C		8506.0 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 58.7 MPa
@Strain 1.70 %,
Temperature 120 °C		8510 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 58.834 MPa
@Strain 1.90 %,
Temperature 120 °C		8533.2 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 60.074 MPa
@Strain 1.70 %,
Temperature 100 °C		8713.0 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.178 MPa
@Strain 2.10 %,
Temperature 140 °C		8728.1 psi
@Strain 2.10 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 60.187 MPa
@Strain 2.20 %,
Temperature 150 °C		8729.4 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 60.301 MPa
@Strain 1.50 %,
Temperature 80.0 °C		8745.9 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 60.494 MPa
@Strain 1.40 %,
Temperature 60.0 °C		8773.9 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 60.547 MPa
@Strain 2.00 %,
Temperature 120 °C		8781.6 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 60.662 MPa
@Strain 1.70 %,
Temperature 100 °C		8798.3 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 60.8 MPa
@Strain 1.80 %,
Temperature 120 °C		8820 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 61.536 MPa
@Strain 2.30 %,
Temperature 150 °C		8925.1 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 61.813 MPa
@Strain 2.20 %,
Temperature 140 °C		8965.2 psi
@Strain 2.20 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 62.07 MPa
@Strain 2.10 %,
Temperature 120 °C		9003 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 62.72 MPa
@Strain 1.80 %,
Temperature 100 °C		9097 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 62.788 MPa
@Strain 2.40 %,
Temperature 150 °C		9106.6 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 62.8 MPa
@Strain 1.90 %,
Temperature 120 °C		9110 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 62.805 MPa
@Strain 1.60 %,
Temperature 80.0 °C		9109.1 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 62.899 MPa
@Strain 1.00 %,
Temperature 23.0 °C		9122.7 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.916 MPa
@Strain 1.80 %,
Temperature 100 °C		9125.2 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 63.113 MPa
@Strain 2.30 %,
Temperature 140 °C		9153.8 psi
@Strain 2.30 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 63.299 MPa
@Strain 1.50 %,
Temperature 60.0 °C		9180.8 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.689 MPa
@Strain 2.20 %,
Temperature 120 °C		9237.3 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 63.943 MPa
@Strain 2.50 %,
Temperature 150 °C		9274.2 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 64.6 MPa
@Strain 2.00 %,
Temperature 120 °C		9370 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 64.679 MPa
@Strain 2.40 %,
Temperature 140 °C		9380.9 psi
@Strain 2.40 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 64.8 MPa
@Strain 0.600 %,
Temperature 0.000 °C		9400 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 64.9 MPa
@Strain 0.700 %,
Temperature 0.000 °C		9410 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.0 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9430 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 65.072 MPa
@Strain 1.90 %,
Temperature 100 °C		9437.9 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 65.072 MPa
@Strain 1.90 %,
Temperature 100 °C		9437.9 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 65.099 MPa
@Strain 2.60 %,
Temperature 150 °C		9441.8 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 65.117 MPa
@Strain 1.70 %,
Temperature 80.0 °C		9444.4 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 65.307 MPa
@Strain 2.30 %,
Temperature 120 °C		9472.0 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 65.73 MPa
@Strain 1.60 %,
Temperature 60.0 °C		9533 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 65.74 MPa
@Strain 2.50 %,
Temperature 140 °C		9535 psi
@Strain 2.50 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 65.9 MPa
@Strain 0.700 %,
Temperature 23.0 °C		9560 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.92 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9561 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 66.158 MPa
@Strain 2.70 %,
Temperature 150 °C		9595.4 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 66.4 MPa
@Strain 2.10 %,
Temperature 120 °C		9630 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 66.735 MPa
@Strain 2.40 %,
Temperature 120 °C		9679.1 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 66.836 MPa
@Strain 2.00 %,
Temperature 100 °C		9693.8 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 66.934 MPa
@Strain 2.00 %,
Temperature 100 °C		9708.0 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 67.125 MPa
@Strain 2.60 %,
Temperature 140 °C		9735.7 psi
@Strain 2.60 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 67.217 MPa
@Strain 2.80 %,
Temperature 150 °C		9749.0 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 67.333 MPa
@Strain 1.80 %,
Temperature 80.0 °C		9765.8 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 67.558 MPa
@Strain 1.10 %,
Temperature 23.0 °C		9798.5 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.068 MPa
@Strain 2.50 %,
Temperature 120 °C		9872.4 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 68.084 MPa
@Strain 2.90 %,
Temperature 150 °C		9874.8 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 68.1 MPa
@Strain 2.20 %,
Temperature 120 °C		9880 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 68.161 MPa
@Strain 1.70 %,
Temperature 60.0 °C		9885.9 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 68.691 MPa
@Strain 2.70 %,
Temperature 140 °C		9962.8 psi
@Strain 2.70 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 68.698 MPa
@Strain 2.10 %,
Temperature 100 °C		9963.8 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 68.951 MPa
@Strain 3.00 %,
Temperature 150 °C		10001 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 69.306 MPa
@Strain 2.60 %,
Temperature 120 °C		10052 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.482 MPa
@Strain 2.10 %,
Temperature 100 °C		10078 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 69.548 MPa
@Strain 1.90 %,
Temperature 80.0 °C		10087 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 69.8 MPa
@Strain 2.30 %,
Temperature 120 °C		10100 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 69.817 MPa
@Strain 3.10 %,
Temperature 150 °C		10126 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 70.061 MPa
@Strain 2.80 %,
Temperature 140 °C		10162 psi
@Strain 2.80 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 70.448 MPa
@Strain 2.70 %,
Temperature 120 °C		10218 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 70.462 MPa
@Strain 2.20 %,
Temperature 100 °C		10220 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 70.499 MPa
@Strain 1.80 %,
Temperature 60.0 °C		10225 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 70.588 MPa
@Strain 3.20 %,
Temperature 150 °C		10238 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 71.235 MPa
@Strain 2.90 %,
Temperature 140 °C		10332 psi
@Strain 2.90 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 71.246 MPa
@Strain 2.20 %,
Temperature 100 °C		10333 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 71.3 MPa
@Strain 2.40 %,
Temperature 120 °C		10300 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 71.358 MPa
@Strain 3.30 %,
Temperature 150 °C		10350 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 71.571 MPa
@Strain 2.00 %,
Temperature 80.0 °C		10381 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 71.59 MPa
@Strain 2.80 %,
Temperature 120 °C		10380 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 71.845 MPa
@Strain 1.20 %,
Temperature 23.0 °C		10420 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.989 MPa
@Strain 3.00 %,
Temperature 140 °C		10441 psi
@Strain 3.00 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 72.032 MPa
@Strain 3.40 %,
Temperature 150 °C		10447 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 72.128 MPa
@Strain 2.30 %,
Temperature 100 °C		10461 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 72.542 MPa
@Strain 2.90 %,
Temperature 120 °C		10521 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 72.706 MPa
@Strain 3.50 %,
Temperature 150 °C		10545 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 72.8 MPa
@Strain 2.50 %,
Temperature 120 °C		10600 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 72.837 MPa
@Strain 1.90 %,
Temperature 60.0 °C		10564 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 72.996 MPa
@Strain 3.10 %,
Temperature 140 °C		10587 psi
@Strain 3.10 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 73.284 MPa
@Strain 3.60 %,
Temperature 150 °C		10629 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 73.498 MPa
@Strain 2.10 %,
Temperature 80.0 °C		10660 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 73.53 MPa
@Strain 0.800 %,
Temperature 0.000 °C		10660 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.59 MPa
@Strain 3.00 %,
Temperature 120 °C		10670 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 73.696 MPa
@Strain 2.40 %,
Temperature 100 °C		10689 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 73.696 MPa
@Strain 2.30 %,
Temperature 100 °C		10689 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.862 MPa
@Strain 3.70 %,
Temperature 150 °C		10713 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.1 MPa
@Strain 2.60 %,
Temperature 120 °C		10700 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 74.344 MPa
@Strain 3.80 %,
Temperature 150 °C		10783 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.4 MPa
@Strain 0.800 %,
Temperature 23.0 °C		10800 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.446 MPa
@Strain 3.10 %,
Temperature 120 °C		10797 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 74.464 MPa
@Strain 3.20 %,
Temperature 140 °C		10800 psi
@Strain 3.20 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 74.825 MPa
@Strain 3.90 %,
Temperature 150 °C		10852 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.894 MPa
@Strain 2.00 %,
Temperature 60.0 °C		10862 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 74.9 MPa
@Strain 2.40 %,
Temperature 100 °C		10900 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.166 MPa
@Strain 2.50 %,
Temperature 100 °C		10902 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 75.303 MPa
@Strain 3.20 %,
Temperature 120 °C		10922 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 75.307 MPa
@Strain 4.00 %,
Temperature 150 °C		10922 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 75.328 MPa
@Strain 2.20 %,
Temperature 80.0 °C		10925 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 75.442 MPa
@Strain 3.30 %,
Temperature 140 °C		10942 psi
@Strain 3.30 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 75.5 MPa
@Strain 2.70 %,
Temperature 120 °C		11000 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 75.5 MPa
@Strain 0.700 %,
Temperature -40.0 °C		11000 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 75.665 MPa
@Strain 1.30 %,
Temperature 23.0 °C		10974 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.692 MPa
@Strain 4.10 %,
Temperature 150 °C		10978 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 75.9 MPa
@Strain 0.700 %,
Temperature 0.000 °C		11000 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.065 MPa
@Strain 3.30 %,
Temperature 120 °C		11032 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 76.077 MPa
@Strain 4.20 %,
Temperature 150 °C		11034 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 76.421 MPa
@Strain 3.40 %,
Temperature 140 °C		11084 psi
@Strain 3.40 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 76.44 MPa
@Strain 2.60 %,
Temperature 100 °C		11090 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 76.462 MPa
@Strain 4.30 %,
Temperature 150 °C		11090 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 76.7 MPa
@Strain 2.80 %,
Temperature 120 °C		11100 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 76.731 MPa
@Strain 3.40 %,
Temperature 120 °C		11129 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 76.751 MPa
@Strain 4.40 %,
Temperature 150 °C		11132 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 76.795 MPa
@Strain 3.50 %,
Temperature 140 °C		11138 psi
@Strain 3.50 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 76.944 MPa
@Strain 4.50 %,
Temperature 150 °C		11160 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 76.95 MPa
@Strain 0.700 %,
Temperature -40.0 °C		11160 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 77.044 MPa
@Strain 2.10 %,
Temperature 60.0 °C		11174 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 77.062 MPa
@Strain 2.30 %,
Temperature 80.0 °C		11177 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 77.224 MPa
@Strain 2.50 %,
Temperature 100 °C		11200 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 77.233 MPa
@Strain 4.60 %,
Temperature 150 °C		11202 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 77.302 MPa
@Strain 3.60 %,
Temperature 140 °C		11212 psi
@Strain 3.60 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 77.398 MPa
@Strain 3.50 %,
Temperature 120 °C		11226 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 77.425 MPa
@Strain 4.70 %,
Temperature 150 °C		11230 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 77.618 MPa
@Strain 4.80 %,
Temperature 150 °C		11258 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 77.812 MPa
@Strain 2.70 %,
Temperature 100 °C		11286 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 77.874 MPa
@Strain 3.60 %,
Temperature 120 °C		11295 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 77.9 MPa
@Strain 2.90 %,
Temperature 120 °C		11300 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 77.907 MPa
@Strain 4.90 %,
Temperature 150 °C		11299 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 78.003 MPa
@Strain 5.00 %,
Temperature 150 °C		11313 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 78.445 MPa
@Strain 3.70 %,
Temperature 120 °C		11378 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 78.574 MPa
@Strain 3.70 %,
Temperature 140 °C		11396 psi
@Strain 3.70 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 78.699 MPa
@Strain 2.40 %,
Temperature 80.0 °C		11414 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 78.8 MPa
@Strain 2.60 %,
Temperature 100 °C		11400 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 78.988 MPa
@Strain 2.80 %,
Temperature 100 °C		11456 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 79.0 MPa
@Strain 3.00 %,
Temperature 120 °C		11500 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 79.016 MPa
@Strain 3.80 %,
Temperature 120 °C		11460 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 79.101 MPa
@Strain 2.20 %,
Temperature 60.0 °C		11473 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 79.486 MPa
@Strain 1.40 %,
Temperature 23.0 °C		11528 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.492 MPa
@Strain 3.90 %,
Temperature 120 °C		11529 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 79.552 MPa
@Strain 3.80 %,
Temperature 140 °C		11538 psi
@Strain 3.80 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 79.873 MPa
@Strain 4.00 %,
Temperature 120 °C		11585 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 80.0 MPa
@Strain 3.10 %,
Temperature 120 °C		11600 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 80.164 MPa
@Strain 2.90 %,
Temperature 100 °C		11627 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 80.254 MPa
@Strain 4.10 %,
Temperature 120 °C		11640 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 80.335 MPa
@Strain 3.90 %,
Temperature 140 °C		11652 psi
@Strain 3.90 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 80.337 MPa
@Strain 2.50 %,
Temperature 80.0 °C		11652 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 80.46 MPa
@Strain 2.70 %,
Temperature 100 °C		11670 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 80.634 MPa
@Strain 4.20 %,
Temperature 120 °C		11695 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 80.824 MPa
@Strain 4.00 %,
Temperature 140 °C		11723 psi
@Strain 4.00 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 80.92 MPa
@Strain 4.30 %,
Temperature 120 °C		11740 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.0 MPa
@Strain 3.20 %,
Temperature 120 °C		11700 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 81.064 MPa
@Strain 2.30 %,
Temperature 60.0 °C		11757 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 81.144 MPa
@Strain 3.00 %,
Temperature 100 °C		11769 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 81.206 MPa
@Strain 4.40 %,
Temperature 120 °C		11778 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.396 MPa
@Strain 4.50 %,
Temperature 120 °C		11806 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.586 MPa
@Strain 4.60 %,
Temperature 120 °C		11833 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.607 MPa
@Strain 4.10 %,
Temperature 140 °C		11836 psi
@Strain 4.10 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 81.777 MPa
@Strain 4.70 %,
Temperature 120 °C		11861 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.782 MPa
@Strain 2.60 %,
Temperature 80.0 °C		11861 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 81.9 MPa
@Strain 3.30 %,
Temperature 120 °C		11900 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 81.967 MPa
@Strain 4.80 %,
Temperature 120 °C		11888 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.967 MPa
@Strain 4.90 %,
Temperature 120 °C		11888 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 82.062 MPa
@Strain 5.00 %,
Temperature 120 °C		11902 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 82.096 MPa
@Strain 4.20 %,
Temperature 140 °C		11907 psi
@Strain 4.20 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 82.124 MPa
@Strain 3.10 %,
Temperature 100 °C		11911 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 82.2 MPa
@Strain 2.80 %,
Temperature 100 °C		11900 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.353 MPa
@Strain 0.900 %,
Temperature 0.000 °C		11944 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 82.585 MPa
@Strain 4.30 %,
Temperature 140 °C		11978 psi
@Strain 4.30 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 82.683 MPa
@Strain 4.40 %,
Temperature 140 °C		11992 psi
@Strain 4.40 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 82.7 MPa
@Strain 3.40 %,
Temperature 120 °C		12000 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 82.741 MPa
@Strain 0.900 %,
Temperature 23.0 °C		12001 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.747 MPa
@Strain 2.40 %,
Temperature 60.0 °C		12001 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 83.006 MPa
@Strain 3.20 %,
Temperature 100 °C		12039 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 83.12 MPa
@Strain 1.50 %,
Temperature 23.0 °C		12060 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.155 MPa
@Strain 4.50 %,
Temperature 140 °C		12061 psi
@Strain 4.50 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 83.227 MPa
@Strain 2.70 %,
Temperature 80.0 °C		12071 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 83.3 MPa
@Strain 2.90 %,
Temperature 100 °C		12100 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 83.438 MPa
@Strain 4.60 %,
Temperature 140 °C		12102 psi
@Strain 4.60 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 83.5 MPa
@Strain 3.50 %,
Temperature 120 °C		12100 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 83.888 MPa
@Strain 3.30 %,
Temperature 100 °C		12167 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 83.955 MPa
@Strain 4.70 %,
Temperature 140 °C		12177 psi
@Strain 4.70 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 84.2 MPa
@Strain 3.60 %,
Temperature 120 °C		12200 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 84.382 MPa
@Strain 2.80 %,
Temperature 80.0 °C		12239 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 84.524 MPa
@Strain 2.50 %,
Temperature 60.0 °C		12259 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 84.574 MPa
@Strain 3.40 %,
Temperature 100 °C		12266 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 84.738 MPa
@Strain 4.80 %,
Temperature 140 °C		12290 psi
@Strain 4.80 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 84.966 MPa
@Strain 3.00 %,
Temperature 100 °C		12323 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 85.0 MPa
@Strain 3.70 %,
Temperature 120 °C		12300 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 85.13 MPa
@Strain 4.90 %,
Temperature 140 °C		12350 psi
@Strain 4.90 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 85.26 MPa
@Strain 3.50 %,
Temperature 100 °C		12370 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 85.423 MPa
@Strain 5.00 %,
Temperature 140 °C		12390 psi
@Strain 5.00 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 85.5 MPa
@Strain 3.80 %,
Temperature 120 °C		12400 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 85.5 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12400 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 85.538 MPa
@Strain 2.90 %,
Temperature 80.0 °C		12406 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 85.946 MPa
@Strain 3.60 %,
Temperature 100 °C		12465 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 86.1 MPa
@Strain 3.90 %,
Temperature 120 °C		12500 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 86.113 MPa
@Strain 2.60 %,
Temperature 60.0 °C		12490 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 86.4 MPa
@Strain 0.800 %,
Temperature 0.000 °C		12500 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.436 MPa
@Strain 3.70 %,
Temperature 100 °C		12537 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 86.45 MPa
@Strain 5.50 %,
Temperature 140 °C		12540 psi
@Strain 5.50 %,
Temperature 284 °F		DAM; ISO 11403-1/-2
 86.598 MPa
@Strain 3.00 %,
Temperature 80.0 °C		12560 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 86.661 MPa
@Strain 1.60 %,
Temperature 23.0 °C		12569 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 86.7 MPa
@Strain 4.00 %,
Temperature 120 °C		12600 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 86.73 MPa
@Strain 3.10 %,
Temperature 100 °C		12580 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 86.926 MPa
@Strain 3.80 %,
Temperature 100 °C		12608 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 87.1 MPa
@Strain 4.10 %,
Temperature 120 °C		12600 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 87.318 MPa
@Strain 3.20 %,
Temperature 100 °C		12664 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.514 MPa
@Strain 3.90 %,
Temperature 100 °C		12693 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 87.56 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12700 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.6 MPa
@Strain 4.20 %,
Temperature 120 °C		12700 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 87.658 MPa
@Strain 3.10 %,
Temperature 80.0 °C		12714 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 87.703 MPa
@Strain 2.70 %,
Temperature 60.0 °C		12720 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 87.906 MPa
@Strain 4.00 %,
Temperature 100 °C		12750 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 88.0 MPa
@Strain 4.30 %,
Temperature 120 °C		12800 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 88.298 MPa
@Strain 4.10 %,
Temperature 100 °C		12807 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 88.4 MPa
@Strain 4.40 %,
Temperature 120 °C		12800 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 88.592 MPa
@Strain 3.30 %,
Temperature 100 °C		12849 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 88.621 MPa
@Strain 3.20 %,
Temperature 80.0 °C		12853 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 88.69 MPa
@Strain 4.20 %,
Temperature 100 °C		12860 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 88.7 MPa
@Strain 4.50 %,
Temperature 120 °C		12900 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 88.984 MPa
@Strain 4.30 %,
Temperature 100 °C		12906 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 89.012 MPa
@Strain 2.80 %,
Temperature 60.0 °C		12910 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 89.1 MPa
@Strain 4.60 %,
Temperature 120 °C		12900 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 89.278 MPa
@Strain 4.40 %,
Temperature 100 °C		12949 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 89.391 MPa
@Strain 3.30 %,
Temperature 80.0 °C		12965 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 89.4 MPa
@Strain 4.70 %,
Temperature 120 °C		13000 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 89.572 MPa
@Strain 4.50 %,
Temperature 100 °C		12991 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 89.6 MPa
@Strain 4.80 %,
Temperature 120 °C		13000 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 89.67 MPa
@Strain 4.60 %,
Temperature 100 °C		13010 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 89.768 MPa
@Strain 4.70 %,
Temperature 100 °C		13020 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 89.829 MPa
@Strain 1.70 %,
Temperature 23.0 °C		13029 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 89.9 MPa
@Strain 4.90 %,
Temperature 120 °C		13000 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 89.964 MPa
@Strain 4.80 %,
Temperature 100 °C		13048 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 90.062 MPa
@Strain 4.90 %,
Temperature 100 °C		13062 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 90.062 MPa
@Strain 5.00 %,
Temperature 100 °C		13062 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 90.1 MPa
@Strain 5.00 %,
Temperature 120 °C		13100 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 90.113 MPa
@Strain 1.00 %,
Temperature 0.000 °C		13070 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 90.134 MPa
@Strain 2.90 %,
Temperature 60.0 °C		13073 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 90.162 MPa
@Strain 3.40 %,
Temperature 80.0 °C		13077 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 90.356 MPa
@Strain 3.40 %,
Temperature 100 °C		13105 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 90.501 MPa
@Strain 1.00 %,
Temperature 23.0 °C		13126 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.836 MPa
@Strain 3.50 %,
Temperature 80.0 °C		13175 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 91.256 MPa
@Strain 3.00 %,
Temperature 60.0 °C		13236 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 91.414 MPa
@Strain 3.60 %,
Temperature 80.0 °C		13259 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 91.434 MPa
@Strain 3.50 %,
Temperature 100 °C		13261 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 91.896 MPa
@Strain 3.70 %,
Temperature 80.0 °C		13328 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 91.924 MPa
@Strain 3.60 %,
Temperature 100 °C		13332 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 92.378 MPa
@Strain 3.10 %,
Temperature 60.0 °C		13398 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 92.474 MPa
@Strain 3.80 %,
Temperature 80.0 °C		13412 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 92.708 MPa
@Strain 3.70 %,
Temperature 100 °C		13446 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 92.859 MPa
@Strain 3.90 %,
Temperature 80.0 °C		13468 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 92.904 MPa
@Strain 1.80 %,
Temperature 23.0 °C		13475 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 93.245 MPa
@Strain 4.00 %,
Temperature 80.0 °C		13524 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 93.407 MPa
@Strain 3.20 %,
Temperature 60.0 °C		13548 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 93.534 MPa
@Strain 4.10 %,
Temperature 80.0 °C		13566 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 93.919 MPa
@Strain 4.20 %,
Temperature 80.0 °C		13622 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.08 MPa
@Strain 3.80 %,
Temperature 100 °C		13650 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 94.208 MPa
@Strain 4.30 %,
Temperature 80.0 °C		13664 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.4 MPa
@Strain 4.40 %,
Temperature 80.0 °C		13700 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.435 MPa
@Strain 3.30 %,
Temperature 60.0 °C		13697 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 94.593 MPa
@Strain 4.50 %,
Temperature 80.0 °C		13720 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.689 MPa
@Strain 4.60 %,
Temperature 80.0 °C		13734 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.786 MPa
@Strain 4.70 %,
Temperature 80.0 °C		13748 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.978 MPa
@Strain 4.80 %,
Temperature 80.0 °C		13775 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.978 MPa
@Strain 4.90 %,
Temperature 80.0 °C		13775 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 95.04 MPa
@Strain 0.900 %,
Temperature -40.0 °C		13780 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 95.075 MPa
@Strain 5.00 %,
Temperature 80.0 °C		13789 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 95.158 MPa
@Strain 3.90 %,
Temperature 100 °C		13802 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 95.183 MPa
@Strain 3.40 %,
Temperature 60.0 °C		13805 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 95.7 MPa
@Strain 1.90 %,
Temperature 23.0 °C		13900 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 95.931 MPa
@Strain 3.50 %,
Temperature 60.0 °C		13914 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 96.04 MPa
@Strain 4.00 %,
Temperature 100 °C		13930 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 96.1 MPa
@Strain 0.900 %,
Temperature 0.000 °C		13900 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.492 MPa
@Strain 3.60 %,
Temperature 60.0 °C		13995 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 96.53 MPa
@Strain 4.10 %,
Temperature 100 °C		14000 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 96.53 MPa
@Strain 4.20 %,
Temperature 100 °C		14000 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 97.053 MPa
@Strain 3.70 %,
Temperature 60.0 °C		14076 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 97.216 MPa
@Strain 4.30 %,
Temperature 100 °C		14100 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 97.614 MPa
@Strain 3.80 %,
Temperature 60.0 °C		14158 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 97.872 MPa
@Strain 0.900 %,
Temperature -40.0 °C		14195 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 97.873 MPa
@Strain 1.10 %,
Temperature 23.0 °C		14195 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.067 MPa
@Strain 1.10 %,
Temperature 0.000 °C		14223 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.082 MPa
@Strain 3.90 %,
Temperature 60.0 °C		14226 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 98.216 MPa
@Strain 2.00 %,
Temperature 23.0 °C		14245 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 98.294 MPa
@Strain 4.40 %,
Temperature 100 °C		14256 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 98.549 MPa
@Strain 4.00 %,
Temperature 60.0 °C		14293 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 98.923 MPa
@Strain 4.10 %,
Temperature 60.0 °C		14348 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 99.176 MPa
@Strain 4.50 %,
Temperature 100 °C		14384 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 99.297 MPa
@Strain 4.20 %,
Temperature 60.0 °C		14402 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 99.577 MPa
@Strain 4.30 %,
Temperature 60.0 °C		14442 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 99.666 MPa
@Strain 4.60 %,
Temperature 100 °C		14455 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 99.951 MPa
@Strain 4.40 %,
Temperature 60.0 °C		14497 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.06 MPa
@Strain 4.70 %,
Temperature 100 °C		14513 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 100.14 MPa
@Strain 4.50 %,
Temperature 60.0 °C		14524 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.42 MPa
@Strain 4.60 %,
Temperature 60.0 °C		14565 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.45 MPa
@Strain 4.80 %,
Temperature 100 °C		14569 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 100.51 MPa
@Strain 4.70 %,
Temperature 60.0 °C		14578 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.61 MPa
@Strain 4.80 %,
Temperature 60.0 °C		14592 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.61 MPa
@Strain 5.00 %,
Temperature 60.0 °C		14592 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.65 MPa
@Strain 4.90 %,
Temperature 100 °C		14598 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 100.7 MPa
@Strain 4.90 %,
Temperature 60.0 °C		14610 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.94 MPa
@Strain 5.00 %,
Temperature 100 °C		14640 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 101.01 MPa
@Strain 2.10 %,
Temperature 23.0 °C		14650 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 103.9 MPa
@Strain 2.20 %,
Temperature 23.0 °C		15070 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 104.08 MPa
@Strain 1.20 %,
Temperature 0.000 °C		15096 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104.33 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15132 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.86 MPa
@Strain 1.20 %,
Temperature 23.0 °C		15209 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 106.2 MPa
@Strain 1.00 %,
Temperature 0.000 °C		15400 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 106.7 MPa
@Strain 2.30 %,
Temperature 23.0 °C		15480 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 107.18 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15545 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.09 MPa
@Strain 2.40 %,
Temperature 23.0 °C		15677 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 110.95 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16092 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.98 MPa
@Strain 2.50 %,
Temperature 23.0 °C		16096 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 111.45 MPa
@Strain 1.30 %,
Temperature 0.000 °C		16164 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 112.04 MPa
@Strain 1.30 %,
Temperature 23.0 °C		16250 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 113.5 MPa
@Strain 2.60 %,
Temperature 23.0 °C		16460 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 115.7 MPa
@Strain 1.10 %,
Temperature 0.000 °C		16780 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 115.83 MPa
@Strain 2.70 %,
Temperature 23.0 °C		16800 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 116.6 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16910 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.69 MPa
@Strain 2.80 %,
Temperature 23.0 °C		17070 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 118.05 MPa
@Strain 1.40 %,
Temperature 0.000 °C		17122 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 119.12 MPa
@Strain 1.40 %,
Temperature 23.0 °C		17277 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 119.46 MPa
@Strain 2.90 %,
Temperature 23.0 °C		17326 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 121.14 MPa
@Strain 3.00 %,
Temperature 23.0 °C		17570 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 122.36 MPa
@Strain 1.20 %,
Temperature -40.0 °C		17747 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 122.63 MPa
@Strain 3.10 %,
Temperature 23.0 °C		17786 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 123.93 MPa
@Strain 3.20 %,
Temperature 23.0 °C		17975 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 124.3 MPa
@Strain 1.20 %,
Temperature 0.000 °C		18030 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 124.64 MPa
@Strain 1.50 %,
Temperature 0.000 °C		18078 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 125.05 MPa
@Strain 3.30 %,
Temperature 23.0 °C		18137 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 125.52 MPa
@Strain 1.50 %,
Temperature 23.0 °C		18205 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 125.69 MPa
@Strain 1.20 %,
Temperature -40.0 °C		18230 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 125.98 MPa
@Strain 3.40 %,
Temperature 23.0 °C		18272 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 126.92 MPa
@Strain 3.50 %,
Temperature 23.0 °C		18408 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 127.57 MPa
@Strain 3.60 %,
Temperature 23.0 °C		18502 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 128.22 MPa
@Strain 3.70 %,
Temperature 23.0 °C		18597 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 128.78 MPa
@Strain 3.80 %,
Temperature 23.0 °C		18678 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.25 MPa
@Strain 3.90 %,
Temperature 23.0 °C		18746 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.34 MPa
@Strain 5.00 %,
Temperature 23.0 °C		18759 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.53 MPa
@Strain 4.00 %,
Temperature 23.0 °C		18787 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.62 MPa
@Strain 4.90 %,
Temperature 23.0 °C		18800 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.81 MPa
@Strain 4.80 %,
Temperature 23.0 °C		18827 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.9 MPa
@Strain 4.10 %,
Temperature 23.0 °C		18840 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.99 MPa
@Strain 4.20 %,
Temperature 23.0 °C		18853 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.99 MPa
@Strain 4.70 %,
Temperature 23.0 °C		18853 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 130.08 MPa
@Strain 4.60 %,
Temperature 23.0 °C		18867 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 130.08 MPa
@Strain 4.30 %,
Temperature 23.0 °C		18867 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 130.18 MPa
@Strain 4.40 %,
Temperature 23.0 °C		18881 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 130.18 MPa
@Strain 4.50 %,
Temperature 23.0 °C		18881 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 130.27 MPa
@Strain 1.60 %,
Temperature 0.000 °C		18894 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 130.92 MPa
@Strain 1.30 %,
Temperature -40.0 °C		18988 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 132.02 MPa
@Strain 1.60 %,
Temperature 23.0 °C		19148 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 132.9 MPa
@Strain 1.30 %,
Temperature 0.000 °C		19280 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 134.67 MPa
@Strain 1.30 %,
Temperature -40.0 °C		19532 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 135.7 MPa
@Strain 1.70 %,
Temperature 0.000 °C		19680 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 137.93 MPa
@Strain 1.70 %,
Temperature 23.0 °C		20005 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 138.74 MPa
@Strain 1.40 %,
Temperature -40.0 °C		20123 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 141 MPa
@Strain 1.40 %,
Temperature 0.000 °C		20500 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 141.04 MPa
@Strain 1.80 %,
Temperature 0.000 °C		20456 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 143.37 MPa
@Strain 1.80 %,
Temperature 23.0 °C		20794 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 143.65 MPa
@Strain 1.40 %,
Temperature -40.0 °C		20835 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 145.79 MPa
@Strain 1.90 %,
Temperature 0.000 °C		21145 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 146.56 MPa
@Strain 1.50 %,
Temperature -40.0 °C		21257 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 148.7 MPa
@Strain 1.90 %,
Temperature 23.0 °C		21570 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 149 MPa
@Strain 1.50 %,
Temperature 0.000 °C		21600 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 150.45 MPa
@Strain 2.00 %,
Temperature 0.000 °C		21821 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 152.13 MPa
@Strain 1.50 %,
Temperature -40.0 °C		22065 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 154.04 MPa
@Strain 2.00 %,
Temperature 23.0 °C		22342 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 154.19 MPa
@Strain 1.60 %,
Temperature -40.0 °C		22363 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 154.91 MPa
@Strain 2.10 %,
Temperature 0.000 °C		22468 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 156.9 MPa
@Strain 1.60 %,
Temperature 0.000 °C		22760 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 158.89 MPa
@Strain 2.10 %,
Temperature 23.0 °C		23045 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 158.98 MPa
@Strain 2.20 %,
Temperature 0.000 °C		23058 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 160.3 MPa
@Strain 1.60 %,
Temperature -40.0 °C		23250 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 161.37 MPa
@Strain 1.70 %,
Temperature -40.0 °C		23405 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 162.67 MPa
@Strain 2.30 %,
Temperature 0.000 °C		23593 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 163.35 MPa
@Strain 2.20 %,
Temperature 23.0 °C		23692 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 164.1 MPa
@Strain 1.70 %,
Temperature 0.000 °C		23800 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 166.35 MPa
@Strain 2.40 %,
Temperature 0.000 °C		24127 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 167.62 MPa
@Strain 2.30 %,
Temperature 23.0 °C		24311 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 168.06 MPa
@Strain 1.70 %,
Temperature -40.0 °C		24375 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 168.18 MPa
@Strain 1.80 %,
Temperature -40.0 °C		24392 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 169.85 MPa
@Strain 2.50 %,
Temperature 0.000 °C		24635 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 170.9 MPa
@Strain 1.80 %,
Temperature 0.000 °C		24790 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 171.4 MPa
@Strain 2.40 %,
Temperature 23.0 °C		24860 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 173.15 MPa
@Strain 2.60 %,
Temperature 0.000 °C		25113 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 174.62 MPa
@Strain 1.90 %,
Temperature -40.0 °C		25327 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 175.18 MPa
@Strain 2.50 %,
Temperature 23.0 °C		25408 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 175.71 MPa
@Strain 1.80 %,
Temperature -40.0 °C		25485 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 176.05 MPa
@Strain 2.70 %,
Temperature 0.000 °C		25534 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 177.5 MPa
@Strain 1.90 %,
Temperature 0.000 °C		25740 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 178.77 MPa
@Strain 2.80 %,
Temperature 0.000 °C		25928 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 178.87 MPa
@Strain 2.60 %,
Temperature 23.0 °C		25943 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 180.87 MPa
@Strain 2.00 %,
Temperature -40.0 °C		26233 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 181.49 MPa
@Strain 2.90 %,
Temperature 0.000 °C		26323 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 181.88 MPa
@Strain 2.70 %,
Temperature 23.0 °C		26380 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 182.76 MPa
@Strain 1.90 %,
Temperature -40.0 °C		26507 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 183.7 MPa
@Strain 2.00 %,
Temperature 0.000 °C		26640 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 183.72 MPa
@Strain 3.00 %,
Temperature 0.000 °C		26646 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 185.2 MPa
@Strain 2.80 %,
Temperature 23.0 °C		26860 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 185.76 MPa
@Strain 3.10 %,
Temperature 0.000 °C		26942 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 187.4 MPa
@Strain 2.10 %,
Temperature -40.0 °C		27180 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 187.6 MPa
@Strain 3.20 %,
Temperature 0.000 °C		27210 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 188.3 MPa
@Strain 2.90 %,
Temperature 23.0 °C		27310 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 188.96 MPa
@Strain 3.30 %,
Temperature 0.000 °C		27406 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 189.6 MPa
@Strain 2.00 %,
Temperature -40.0 °C		27500 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 189.8 MPa
@Strain 2.10 %,
Temperature 0.000 °C		27530 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 190.12 MPa
@Strain 3.40 %,
Temperature 0.000 °C		27575 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 190.9 MPa
@Strain 3.50 %,
Temperature 0.000 °C		27690 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 191.12 MPa
@Strain 3.00 %,
Temperature 23.0 °C		27720 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 193 MPa
@Strain 3.10 %,
Temperature 23.0 °C		28000 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 193.02 MPa
@Strain 2.20 %,
Temperature -40.0 °C		27995 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 195.19 MPa
@Strain 3.20 %,
Temperature 23.0 °C		28310 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 195.6 MPa
@Strain 2.20 %,
Temperature 0.000 °C		28370 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 196.24 MPa
@Strain 2.10 %,
Temperature -40.0 °C		28462 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 196.9 MPa
@Strain 3.30 %,
Temperature 23.0 °C		28560 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 198.44 MPa
@Strain 2.30 %,
Temperature -40.0 °C		28781 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 198.6 MPa
@Strain 3.40 %,
Temperature 23.0 °C		28800 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 200 MPa
@Strain 3.50 %,
Temperature 23.0 °C		29000 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 200.8 MPa
@Strain 2.30 %,
Temperature 0.000 °C		29120 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 202.26 MPa
@Strain 2.20 %,
Temperature -40.0 °C		29335 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 203.5 MPa
@Strain 2.40 %,
Temperature -40.0 °C		29520 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 205.8 MPa
@Strain 2.40 %,
Temperature 0.000 °C		29850 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 207.67 MPa
@Strain 2.30 %,
Temperature -40.0 °C		30120 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 208.75 MPa
@Strain 2.50 %,
Temperature -40.0 °C		30277 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 210.4 MPa
@Strain 2.50 %,
Temperature 0.000 °C		30520 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 212.88 MPa
@Strain 2.40 %,
Temperature -40.0 °C		30876 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 213.16 MPa
@Strain 2.60 %,
Temperature -40.0 °C		30916 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 215 MPa
@Strain 2.60 %,
Temperature 0.000 °C		31200 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 217.67 MPa
@Strain 2.70 %,
Temperature -40.0 °C		31570 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 218.9 MPa
@Strain 2.50 %,
Temperature -40.0 °C		31750 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 219.4 MPa
@Strain 2.70 %,
Temperature 0.000 °C		31820 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 221.9 MPa
@Strain 2.80 %,
Temperature -40.0 °C		32180 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 223 MPa
@Strain 2.80 %,
Temperature 0.000 °C		32300 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 224.3 MPa
@Strain 2.60 %,
Temperature -40.0 °C		32530 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 225.68 MPa
@Strain 2.90 %,
Temperature -40.0 °C		32732 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 226.4 MPa
@Strain 2.90 %,
Temperature 0.000 °C		32840 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 229.1 MPa
@Strain 2.70 %,
Temperature -40.0 °C		33230 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 229.36 MPa
@Strain 3.00 %,
Temperature -40.0 °C		33266 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 229.6 MPa
@Strain 3.00 %,
Temperature 0.000 °C		33300 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 233.4 MPa
@Strain 2.80 %,
Temperature -40.0 °C		33850 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 236.9 MPa
@Strain 2.90 %,
Temperature -40.0 °C		34360 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 240 MPa
@Strain 3.00 %,
Temperature -40.0 °C		34800 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		DAM; ISO 527
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  8.00 GPa
@Temperature 23.0 °C		1160 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 10.5 GPa
@Temperature 23.0 °C		1520 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength  200 MPa
@Temperature 23.0 °C		29000 psi
@Temperature 73.4 °F		50%RH; ISO 178
 262 MPa
@Temperature 23.0 °C		38000 psi
@Temperature 73.4 °F		DAM; ASTM D790
 290 MPa
@Temperature 23.0 °C		42100 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus  6.205 GPa
@Temperature 23.0 °C		900.0 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 6.205 GPa
@Temperature 23.0 °C		900.0 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 8.965 GPa
@Temperature 23.0 °C		1300 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 9.30 GPa
@Temperature 23.0 °C		1350 ksi
@Temperature 73.4 °F		DAM; ISO 178
Shear Strength 86.0 MPa
@Temperature 23.0 °C		12500 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  1.17 J/cm
@Temperature 23.0 °C		2.19 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Unnotched  13.3 J/cm
@Temperature 23.0 °C		24.9 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
 14.9 J/cm
@Temperature 23.0 °C		27.9 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D4812
Izod Impact, Notched (ISO)  10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 10.0 kJ/m²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 10.0 kJ/m²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 12.0 kJ/m²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 15.0 kJ/m²
@Temperature 23.0 °C		7.14 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  70.0 kJ/m²
@Temperature -30.0 °C		33.3 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 70.0 kJ/m²
@Temperature -30.0 °C		33.3 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 80.0 kJ/m²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 90.0 kJ/m²
@Temperature 23.0 °C		42.8 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  7.00 J/cm²
@Temperature -30.0 °C		33.3 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 7.50 J/cm²
@Temperature -30.0 °C		35.7 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 8.50 J/cm²
@Temperature 23.0 °C		40.4 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 10.0 J/cm²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.00 J/cm²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 1.00 J/cm²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.00 J/cm²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.70 J/cm²
@Temperature 23.0 °C		8.09 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.2
@Frequency 100 Hz,
Temperature 23.0 °C		4.2
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.5
@Frequency 1000 Hz,
Temperature 23.0 °C		4.5
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
Dielectric Strength 20.9 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		531 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
Dissipation Factor  0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.015
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.015
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
Comparative Tracking Index  600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  65.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		36.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 65.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		36.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 83.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		46.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 83.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		46.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 137 µm/m-°C
@Temperature 55.0 - 160 °C		76.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 137 µm/m-°C
@Temperature 55.0 - 160 °C		76.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 261 °C502 °FDAM; ISO 75-1/-2
 261 °C502 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 249 °C480 °FDAM; ASTM D648
 252 °C486 °FDAM; ISO 75-1/-2
Glass Transition Temp, Tg 80.0 °C176 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
 120 °C
@Thickness 0.710 mm		248 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
Oxygen Index 24 %24 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesCreep Resistance, GoodDAM
 General PurposeDAM
 LubricatedDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF33<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF33ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Electrical/Electronic ApplicationsDAM
 Industrial ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45477.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70G33L NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4