- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 1.2
- 热变形温度 [℃]: 262.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 50 % | 50 % | DAM | ||
| Water Absorption | 1.2 % @Thickness 1.00 mm, Temperature 23.0 °C | 1.2 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 4.2 % @Thickness 1.00 mm, Temperature 23.0 °C | 4.2 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm @Thickness 2.00 mm | 0.0085 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 190 MPa @Temperature 23.0 °C | 27600 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 245 MPa @Temperature 23.0 °C | 35500 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Stress | 12.62 MPa @Strain 0.220 %, Temperature 220 °C | 1830 psi @Strain 0.220 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | ||
| 16.06 MPa @Strain 0.250 %, Temperature 150 °C | 2329 psi @Strain 0.250 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.27 MPa @Strain 0.230 %, Temperature 180 °C | 2360 psi @Strain 0.230 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 17.43 MPa @Strain 0.310 %, Temperature 220 °C | 2528 psi @Strain 0.310 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 24.29 MPa @Strain 0.300 %, Temperature 120 °C | 3523 psi @Strain 0.300 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 24.39 MPa @Strain 0.330 %, Temperature 150 °C | 3537 psi @Strain 0.330 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 26.01 MPa @Strain 0.530 %, Temperature 220 °C | 3772 psi @Strain 0.530 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 26.57 MPa @Strain 0.360 %, Temperature 120 °C | 3854 psi @Strain 0.360 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.23 MPa @Strain 0.460 %, Temperature 150 °C | 3949 psi @Strain 0.460 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.75 MPa @Strain 0.510 %, Temperature 200 °C | 4315 psi @Strain 0.510 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 30.4 MPa @Strain 0.490 %, Temperature 180 °C | 4410 psi @Strain 0.490 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 32.6 MPa @Strain 0.770 %, Temperature 220 °C | 4730 psi @Strain 0.770 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 37.38 MPa @Strain 0.320 %, Temperature 23.0 °C | 5422 psi @Strain 0.320 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.52 MPa @Strain 0.700 %, Temperature 150 °C | 5442 psi @Strain 0.700 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.53 MPa @Strain 0.430 %, Temperature 60.0 °C | 5443 psi @Strain 0.430 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.83 MPa @Strain 1.01 %, Temperature 220 °C | 5487 psi @Strain 1.01 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 38.95 MPa @Strain 0.580 %, Temperature 150 °C | 5649 psi @Strain 0.580 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 39.23 MPa @Strain 0.400 %, Temperature 40.0 °C | 5690 psi @Strain 0.400 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.44 MPa @Strain 0.590 %, Temperature 120 °C | 5720 psi @Strain 0.590 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.3 MPa @Strain 0.490 %, Temperature 90.0 °C | 5850 psi @Strain 0.490 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.82 MPa @Strain 0.450 %, Temperature 90.0 °C | 5920 psi @Strain 0.450 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 40.95 MPa @Strain 0.540 %, Temperature 120 °C | 5939 psi @Strain 0.540 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 41.13 MPa @Strain 0.810 %, Temperature 200 °C | 5965 psi @Strain 0.810 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 41.84 MPa @Strain 0.340 %, Temperature 60.0 °C | 6068 psi @Strain 0.340 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 42.13 MPa @Strain 1.25 %, Temperature 220 °C | 6110 psi @Strain 1.25 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 42.55 MPa @Strain 0.780 %, Temperature 180 °C | 6171 psi @Strain 0.780 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 45.6 MPa @Strain 1.48 %, Temperature 220 °C | 6610 psi @Strain 1.48 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 46.14 MPa @Strain 0.980 %, Temperature 150 °C | 6692 psi @Strain 0.980 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.47 MPa @Strain 1.71 %, Temperature 220 °C | 7030 psi @Strain 1.71 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 49.68 MPa @Strain 1.14 %, Temperature 200 °C | 7205 psi @Strain 1.14 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 49.88 MPa @Strain 0.820 %, Temperature 150 °C | 7234 psi @Strain 0.820 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 50.28 MPa @Strain 0.830 %, Temperature 120 °C | 7293 psi @Strain 0.830 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.97 MPa @Strain 1.05 %, Temperature 180 °C | 7393 psi @Strain 1.05 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 51.08 MPa @Strain 1.95 %, Temperature 220 °C | 7409 psi @Strain 1.95 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 51.97 MPa @Strain 0.740 %, Temperature 120 °C | 7538 psi @Strain 0.740 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 52.44 MPa @Strain 1.24 %, Temperature 150 °C | 7606 psi @Strain 1.24 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.46 MPa @Strain 0.700 %, Temperature 90.0 °C | 7609 psi @Strain 0.700 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.91 MPa @Strain 0.630 %, Temperature 60.0 °C | 7674 psi @Strain 0.630 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.36 MPa @Strain 2.19 %, Temperature 220 °C | 7739 psi @Strain 2.19 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 54.91 MPa @Strain 0.570 %, Temperature 40.0 °C | 7964 psi @Strain 0.570 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 55.25 MPa @Strain 2.45 %, Temperature 220 °C | 8013 psi @Strain 2.45 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 56.04 MPa @Strain 1.48 %, Temperature 200 °C | 8128 psi @Strain 1.48 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 56.85 MPa @Strain 2.69 %, Temperature 220 °C | 8245 psi @Strain 2.69 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 56.85 MPa @Strain 0.380 %, Temperature 40.0 °C | 8245 psi @Strain 0.380 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 57.32 MPa @Strain 0.510 %, Temperature 23.0 °C | 8314 psi @Strain 0.510 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.34 MPa @Strain 0.670 %, Temperature 90.0 °C | 8316 psi @Strain 0.670 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 57.4 MPa @Strain 1.48 %, Temperature 150 °C | 8330 psi @Strain 1.48 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.45 MPa @Strain 1.31 %, Temperature 180 °C | 8332 psi @Strain 1.31 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 58.16 MPa @Strain 1.03 %, Temperature 150 °C | 8435 psi @Strain 1.03 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 58.26 MPa @Strain 1.05 %, Temperature 120 °C | 8450 psi @Strain 1.05 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 58.43 MPa @Strain 2.97 %, Temperature 220 °C | 8475 psi @Strain 2.97 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 59.44 MPa @Strain 0.490 %, Temperature 60.0 °C | 8621 psi @Strain 0.490 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 59.83 MPa @Strain 3.25 %, Temperature 220 °C | 8678 psi @Strain 3.25 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 61.02 MPa @Strain 1.82 %, Temperature 200 °C | 8850 psi @Strain 1.82 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 61.18 MPa @Strain 0.930 %, Temperature 120 °C | 8873 psi @Strain 0.930 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 61.26 MPa @Strain 3.51 %, Temperature 220 °C | 8885 psi @Strain 3.51 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 61.38 MPa @Strain 0.870 %, Temperature 90.0 °C | 8902 psi @Strain 0.870 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.02 MPa @Strain 1.75 %, Temperature 150 °C | 8995 psi @Strain 1.75 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.39 MPa @Strain 4.04 %, Temperature 220 °C | 9194 psi @Strain 4.04 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 63.58 MPa @Strain 1.61 %, Temperature 180 °C | 9222 psi @Strain 1.61 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 64.19 MPa @Strain 0.800 %, Temperature 60.0 °C | 9310 psi @Strain 0.800 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.67 MPa @Strain 1.26 %, Temperature 120 °C | 9380 psi @Strain 1.26 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.91 MPa @Strain 2.17 %, Temperature 200 °C | 9414 psi @Strain 2.17 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 65.1 MPa @Strain 1.26 %, Temperature 150 °C | 9440 psi @Strain 1.26 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 65.11 MPa @Strain 4.55 %, Temperature 220 °C | 9443 psi @Strain 4.55 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 65.87 MPa @Strain 2.02 %, Temperature 150 °C | 9554 psi @Strain 2.02 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.09 MPa @Strain 0.720 %, Temperature 40.0 °C | 9586 psi @Strain 0.720 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 68.2 MPa @Strain 2.53 %, Temperature 200 °C | 9890 psi @Strain 2.53 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 68.69 MPa @Strain 1.93 %, Temperature 180 °C | 9963 psi @Strain 1.93 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 69.06 MPa @Strain 1.06 %, Temperature 90.0 °C | 10020 psi @Strain 1.06 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.33 MPa @Strain 1.12 %, Temperature 120 °C | 10060 psi @Strain 1.12 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 69.34 MPa @Strain 2.30 %, Temperature 150 °C | 10060 psi @Strain 2.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.42 MPa @Strain 1.49 %, Temperature 120 °C | 10210 psi @Strain 1.49 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.03 MPa @Strain 2.88 %, Temperature 200 °C | 10300 psi @Strain 2.88 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 71.48 MPa @Strain 0.900 %, Temperature 90.0 °C | 10370 psi @Strain 0.900 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 71.96 MPa @Strain 1.51 %, Temperature 150 °C | 10440 psi @Strain 1.51 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 72.11 MPa @Strain 0.490 %, Temperature 40.0 °C | 10460 psi @Strain 0.490 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 72.2 MPa @Strain 0.620 %, Temperature 60.0 °C | 10500 psi @Strain 0.620 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 72.21 MPa @Strain 0.660 %, Temperature 23.0 °C | 10470 psi @Strain 0.660 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.29 MPa @Strain 2.59 %, Temperature 150 °C | 10480 psi @Strain 2.59 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.02 MPa @Strain 2.26 %, Temperature 180 °C | 10590 psi @Strain 2.26 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 73.45 MPa @Strain 3.24 %, Temperature 200 °C | 10650 psi @Strain 3.24 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 73.55 MPa @Strain 0.960 %, Temperature 60.0 °C | 10670 psi @Strain 0.960 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.76 MPa @Strain 0.420 %, Temperature -20.0 °C | 10700 psi @Strain 0.420 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 74.97 MPa @Strain 2.89 %, Temperature 150 °C | 10870 psi @Strain 2.89 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 75.28 MPa @Strain 1.72 %, Temperature 120 °C | 10920 psi @Strain 1.72 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 75.5 MPa @Strain 1.24 %, Temperature 90.0 °C | 11000 psi @Strain 1.24 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 75.66 MPa @Strain 3.62 %, Temperature 200 °C | 10970 psi @Strain 3.62 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 76.36 MPa @Strain 0.860 %, Temperature 40.0 °C | 11080 psi @Strain 0.860 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 76.42 MPa @Strain 1.30 %, Temperature 120 °C | 11080 psi @Strain 1.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 76.86 MPa @Strain 2.60 %, Temperature 180 °C | 11150 psi @Strain 2.60 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 77.26 MPa @Strain 3.20 %, Temperature 150 °C | 11210 psi @Strain 3.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.62 MPa @Strain 3.98 %, Temperature 200 °C | 11260 psi @Strain 3.98 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 77.8 MPa @Strain 1.78 %, Temperature 150 °C | 11300 psi @Strain 1.78 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 79.33 MPa @Strain 3.51 %, Temperature 150 °C | 11510 psi @Strain 3.51 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.39 MPa @Strain 4.41 %, Temperature 200 °C | 11510 psi @Strain 4.41 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 79.46 MPa @Strain 1.96 %, Temperature 120 °C | 11520 psi @Strain 1.96 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.2 MPa @Strain 2.95 %, Temperature 180 °C | 11600 psi @Strain 2.95 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 81.05 MPa @Strain 4.82 %, Temperature 200 °C | 11760 psi @Strain 4.82 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 81.25 MPa @Strain 3.85 %, Temperature 150 °C | 11780 psi @Strain 3.85 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.34 MPa @Strain 1.44 %, Temperature 90.0 °C | 11800 psi @Strain 1.44 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.76 MPa @Strain 1.13 %, Temperature 60.0 °C | 11860 psi @Strain 1.13 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.87 MPa @Strain 1.11 %, Temperature 90.0 °C | 11870 psi @Strain 1.11 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 82.45 MPa @Strain 0.750 %, Temperature 60.0 °C | 11960 psi @Strain 0.750 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 82.49 MPa @Strain 5.24 %, Temperature 200 °C | 11960 psi @Strain 5.24 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 82.86 MPa @Strain 4.20 %, Temperature 150 °C | 12020 psi @Strain 4.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 82.91 MPa @Strain 2.06 %, Temperature 150 °C | 12030 psi @Strain 2.06 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 83.19 MPa @Strain 3.32 %, Temperature 180 °C | 12070 psi @Strain 3.32 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 83.21 MPa @Strain 1.51 %, Temperature 120 °C | 12070 psi @Strain 1.51 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 83.35 MPa @Strain 2.21 %, Temperature 120 °C | 12090 psi @Strain 2.21 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 83.79 MPa @Strain 5.65 %, Temperature 200 °C | 12150 psi @Strain 5.65 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 84.24 MPa @Strain 4.55 %, Temperature 150 °C | 12220 psi @Strain 4.55 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 84.24 MPa @Strain 0.580 %, Temperature 40.0 °C | 12220 psi @Strain 0.580 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 84.37 MPa @Strain 0.800 %, Temperature 23.0 °C | 12240 psi @Strain 0.800 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 84.93 MPa @Strain 6.07 %, Temperature 200 °C | 12320 psi @Strain 6.07 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 85.24 MPa @Strain 1.01 %, Temperature 40.0 °C | 12360 psi @Strain 1.01 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.42 MPa @Strain 4.94 %, Temperature 150 °C | 12390 psi @Strain 4.94 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.9 MPa @Strain 3.70 %, Temperature 180 °C | 12500 psi @Strain 3.70 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 85.92 MPa @Strain 6.48 %, Temperature 200 °C | 12460 psi @Strain 6.48 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 86.41 MPa @Strain 5.32 %, Temperature 150 °C | 12530 psi @Strain 5.32 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 86.56 MPa @Strain 1.63 %, Temperature 90.0 °C | 12550 psi @Strain 1.63 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 86.7 MPa @Strain 2.47 %, Temperature 120 °C | 12600 psi @Strain 2.47 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 86.74 MPa @Strain 6.93 %, Temperature 200 °C | 12580 psi @Strain 6.93 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 87.17 MPa @Strain 5.71 %, Temperature 150 °C | 12640 psi @Strain 5.71 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 87.19 MPa @Strain 2.35 %, Temperature 150 °C | 12650 psi @Strain 2.35 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 87.47 MPa @Strain 0.560 %, Temperature 23.0 °C | 12690 psi @Strain 0.560 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 88.21 MPa @Strain 4.08 %, Temperature 180 °C | 12790 psi @Strain 4.08 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 88.97 MPa @Strain 1.30 %, Temperature 60.0 °C | 12900 psi @Strain 1.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.15 MPa @Strain 1.72 %, Temperature 120 °C | 12930 psi @Strain 1.72 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 89.55 MPa @Strain 2.74 %, Temperature 120 °C | 12990 psi @Strain 2.74 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.65 MPa @Strain 1.28 %, Temperature 90.0 °C | 13000 psi @Strain 1.28 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 90.36 MPa @Strain 4.46 %, Temperature 180 °C | 13110 psi @Strain 4.46 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 91.1 MPa @Strain 2.66 %, Temperature 150 °C | 13200 psi @Strain 2.66 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 91.32 MPa @Strain 1.85 %, Temperature 90.0 °C | 13240 psi @Strain 1.85 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.88 MPa @Strain 0.560 %, Temperature 0.000 °C | 13330 psi @Strain 0.560 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 92.08 MPa @Strain 3.02 %, Temperature 120 °C | 13360 psi @Strain 3.02 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 92.3 MPa @Strain 4.90 %, Temperature 180 °C | 13400 psi @Strain 4.90 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 92.75 MPa @Strain 0.880 %, Temperature 60.0 °C | 13450 psi @Strain 0.880 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 93.23 MPa @Strain 1.15 %, Temperature 40.0 °C | 13520 psi @Strain 1.15 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 93.93 MPa @Strain 5.33 %, Temperature 180 °C | 13620 psi @Strain 5.33 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 94.26 MPa @Strain 3.31 %, Temperature 120 °C | 13670 psi @Strain 3.31 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 94.41 MPa @Strain 0.930 %, Temperature 23.0 °C | 13690 psi @Strain 0.930 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 94.48 MPa @Strain 2.96 %, Temperature 150 °C | 13700 psi @Strain 2.96 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 94.7 MPa @Strain 1.94 %, Temperature 120 °C | 13700 psi @Strain 1.94 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 95.38 MPa @Strain 0.630 %, Temperature 0.000 °C | 13830 psi @Strain 0.630 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.41 MPa @Strain 5.81 %, Temperature 180 °C | 13840 psi @Strain 5.81 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 95.44 MPa @Strain 1.48 %, Temperature 60.0 °C | 13840 psi @Strain 1.48 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.65 MPa @Strain 2.08 %, Temperature 90.0 °C | 13870 psi @Strain 2.08 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.71 MPa @Strain 0.670 %, Temperature 40.0 °C | 13880 psi @Strain 0.670 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 96.17 MPa @Strain 3.63 %, Temperature 120 °C | 13950 psi @Strain 3.63 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 96.66 MPa @Strain 6.27 %, Temperature 180 °C | 14020 psi @Strain 6.27 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 96.9 MPa @Strain 1.45 %, Temperature 90.0 °C | 14100 psi @Strain 1.45 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 97.64 MPa @Strain 3.30 %, Temperature 150 °C | 14160 psi @Strain 3.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 97.7 MPa @Strain 6.73 %, Temperature 180 °C | 14200 psi @Strain 6.73 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 97.84 MPa @Strain 3.98 %, Temperature 120 °C | 14190 psi @Strain 3.98 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 99.18 MPa @Strain 4.34 %, Temperature 120 °C | 14380 psi @Strain 4.34 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 99.43 MPa @Strain 2.33 %, Temperature 90.0 °C | 14420 psi @Strain 2.33 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 99.5 MPa @Strain 0.640 %, Temperature 23.0 °C | 14400 psi @Strain 0.640 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 99.68 MPa @Strain 2.18 %, Temperature 120 °C | 14460 psi @Strain 2.18 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 100.02 MPa @Strain 0.580 %, Temperature -20.0 °C | 14507 psi @Strain 0.580 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 100.25 MPa @Strain 4.70 %, Temperature 120 °C | 14540 psi @Strain 4.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 100.43 MPa @Strain 3.66 %, Temperature 150 °C | 14566 psi @Strain 3.66 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 100.54 MPa @Strain 1.30 %, Temperature 40.0 °C | 14582 psi @Strain 1.30 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 101.04 MPa @Strain 5.11 %, Temperature 120 °C | 14655 psi @Strain 5.11 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 101.26 MPa @Strain 1.66 %, Temperature 60.0 °C | 14687 psi @Strain 1.66 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.04 MPa @Strain 1.01 %, Temperature 60.0 °C | 14800 psi @Strain 1.01 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 102.77 MPa @Strain 2.60 %, Temperature 90.0 °C | 14906 psi @Strain 2.60 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.84 MPa @Strain 4.04 %, Temperature 150 °C | 14916 psi @Strain 4.04 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 103.18 MPa @Strain 1.62 %, Temperature 90.0 °C | 14965 psi @Strain 1.62 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 103.71 MPa @Strain 1.07 %, Temperature 23.0 °C | 15042 psi @Strain 1.07 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 104.2 MPa @Strain 2.43 %, Temperature 120 °C | 15110 psi @Strain 2.43 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 104.95 MPa @Strain 4.44 %, Temperature 150 °C | 15222 psi @Strain 4.44 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 105.62 MPa @Strain 2.89 %, Temperature 90.0 °C | 15319 psi @Strain 2.89 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 105.85 MPa @Strain 0.640 %, Temperature -20.0 °C | 15352 psi @Strain 0.640 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 106.54 MPa @Strain 1.86 %, Temperature 60.0 °C | 15452 psi @Strain 1.86 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 106.71 MPa @Strain 4.83 %, Temperature 150 °C | 15477 psi @Strain 4.83 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 106.85 MPa @Strain 0.770 %, Temperature 40.0 °C | 15497 psi @Strain 0.770 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 107.37 MPa @Strain 1.46 %, Temperature 40.0 °C | 15573 psi @Strain 1.46 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 108.06 MPa @Strain 3.20 %, Temperature 90.0 °C | 15673 psi @Strain 3.20 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 108.28 MPa @Strain 5.25 %, Temperature 150 °C | 15705 psi @Strain 5.25 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 108.41 MPa @Strain 0.730 %, Temperature 0.000 °C | 15724 psi @Strain 0.730 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 108.44 MPa @Strain 2.70 %, Temperature 120 °C | 15728 psi @Strain 2.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 109.12 MPa @Strain 1.80 %, Temperature 90.0 °C | 15827 psi @Strain 1.80 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 109.55 MPa @Strain 5.66 %, Temperature 150 °C | 15889 psi @Strain 5.66 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 110.04 MPa @Strain 3.54 %, Temperature 90.0 °C | 15960 psi @Strain 3.54 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 110.54 MPa @Strain 6.10 %, Temperature 150 °C | 16033 psi @Strain 6.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 110.86 MPa @Strain 1.14 %, Temperature 60.0 °C | 16079 psi @Strain 1.14 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 111.18 MPa @Strain 0.720 %, Temperature 23.0 °C | 16125 psi @Strain 0.720 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 111.29 MPa @Strain 2.05 %, Temperature 60.0 °C | 16141 psi @Strain 2.05 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 111.61 MPa @Strain 3.89 %, Temperature 90.0 °C | 16188 psi @Strain 3.89 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.3 MPa @Strain 3.01 %, Temperature 120 °C | 16290 psi @Strain 3.01 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 112.46 MPa @Strain 1.21 %, Temperature 23.0 °C | 16311 psi @Strain 1.21 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.8 MPa @Strain 4.26 %, Temperature 90.0 °C | 16360 psi @Strain 4.26 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.46 MPa @Strain 1.61 %, Temperature 40.0 °C | 16456 psi @Strain 1.61 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.63 MPa @Strain 4.69 %, Temperature 90.0 °C | 16481 psi @Strain 4.69 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 114.74 MPa @Strain 1.99 %, Temperature 90.0 °C | 16642 psi @Strain 1.99 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 115.41 MPa @Strain 3.32 %, Temperature 120 °C | 16739 psi @Strain 3.32 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 115.46 MPa @Strain 0.710 %, Temperature 0.000 °C | 16746 psi @Strain 0.710 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 115.48 MPa @Strain 2.27 %, Temperature 60.0 °C | 16749 psi @Strain 2.27 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 117.86 MPa @Strain 0.860 %, Temperature 40.0 °C | 17094 psi @Strain 0.860 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 118.07 MPa @Strain 3.65 %, Temperature 120 °C | 17125 psi @Strain 3.65 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 118.82 MPa @Strain 1.27 %, Temperature 60.0 °C | 17233 psi @Strain 1.27 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 119.14 MPa @Strain 2.52 %, Temperature 60.0 °C | 17280 psi @Strain 2.52 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 119.26 MPa @Strain 1.78 %, Temperature 40.0 °C | 17297 psi @Strain 1.78 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 119.71 MPa @Strain 0.830 %, Temperature 0.000 °C | 17362 psi @Strain 0.830 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 120.07 MPa @Strain 2.19 %, Temperature 90.0 °C | 17415 psi @Strain 2.19 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 120.08 MPa @Strain 1.35 %, Temperature 23.0 °C | 17416 psi @Strain 1.35 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 120.51 MPa @Strain 4.03 %, Temperature 120 °C | 17479 psi @Strain 4.03 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 122.22 MPa @Strain 2.78 %, Temperature 60.0 °C | 17727 psi @Strain 2.78 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 122.42 MPa @Strain 4.44 %, Temperature 120 °C | 17756 psi @Strain 4.44 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 123.12 MPa @Strain 0.810 %, Temperature 23.0 °C | 17857 psi @Strain 0.810 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 123.18 MPa @Strain 0.760 %, Temperature -20.0 °C | 17866 psi @Strain 0.760 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 123.96 MPa @Strain 4.84 %, Temperature 120 °C | 17979 psi @Strain 4.84 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 124.76 MPa @Strain 1.97 %, Temperature 40.0 °C | 18095 psi @Strain 1.97 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 124.83 MPa @Strain 3.07 %, Temperature 60.0 °C | 18105 psi @Strain 3.07 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 124.98 MPa @Strain 2.40 %, Temperature 90.0 °C | 18127 psi @Strain 2.40 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 125.12 MPa @Strain 5.27 %, Temperature 120 °C | 18147 psi @Strain 5.27 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 126.63 MPa @Strain 1.40 %, Temperature 60.0 °C | 18366 psi @Strain 1.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 126.81 MPa @Strain 3.38 %, Temperature 60.0 °C | 18392 psi @Strain 3.38 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 127.15 MPa @Strain 1.49 %, Temperature 23.0 °C | 18442 psi @Strain 1.49 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 127.54 MPa @Strain 0.960 %, Temperature 40.0 °C | 18498 psi @Strain 0.960 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 128.31 MPa @Strain 3.72 %, Temperature 60.0 °C | 18610 psi @Strain 3.72 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 129.33 MPa @Strain 4.10 %, Temperature 60.0 °C | 18758 psi @Strain 4.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 129.63 MPa @Strain 2.65 %, Temperature 90.0 °C | 18801 psi @Strain 2.65 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 129.86 MPa @Strain 2.18 %, Temperature 40.0 °C | 18835 psi @Strain 2.18 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 129.9 MPa @Strain 4.52 %, Temperature 60.0 °C | 18840 psi @Strain 4.52 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 130.16 MPa @Strain 0.930 %, Temperature 0.000 °C | 18878 psi @Strain 0.930 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 130.36 MPa @Strain 0.820 %, Temperature 0.000 °C | 18907 psi @Strain 0.820 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 133.52 MPa @Strain 2.90 %, Temperature 90.0 °C | 19365 psi @Strain 2.90 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 134.23 MPa @Strain 1.65 %, Temperature 23.0 °C | 19468 psi @Strain 1.65 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 134.37 MPa @Strain 1.56 %, Temperature 60.0 °C | 19489 psi @Strain 1.56 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 134.41 MPa @Strain 2.41 %, Temperature 40.0 °C | 19495 psi @Strain 2.41 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 134.58 MPa @Strain 0.890 %, Temperature 23.0 °C | 19519 psi @Strain 0.890 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 136.34 MPa @Strain 1.05 %, Temperature 40.0 °C | 19774 psi @Strain 1.05 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 136.98 MPa @Strain 3.18 %, Temperature 90.0 °C | 19867 psi @Strain 3.18 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 138.42 MPa @Strain 2.69 %, Temperature 40.0 °C | 20076 psi @Strain 2.69 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 139.81 MPa @Strain 3.50 %, Temperature 90.0 °C | 20278 psi @Strain 3.50 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 140.25 MPa @Strain 1.03 %, Temperature 0.000 °C | 20342 psi @Strain 1.03 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 140.77 MPa @Strain 1.82 %, Temperature 23.0 °C | 20417 psi @Strain 1.82 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 141.42 MPa @Strain 1.71 %, Temperature 60.0 °C | 20511 psi @Strain 1.71 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 141.44 MPa @Strain 3.00 %, Temperature 40.0 °C | 20514 psi @Strain 3.00 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 142.11 MPa @Strain 3.84 %, Temperature 90.0 °C | 20611 psi @Strain 3.84 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 142.59 MPa @Strain 0.900 %, Temperature 0.000 °C | 20681 psi @Strain 0.900 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 143.57 MPa @Strain 3.34 %, Temperature 40.0 °C | 20823 psi @Strain 3.34 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 143.79 MPa @Strain 4.22 %, Temperature 90.0 °C | 20855 psi @Strain 4.22 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 144.9 MPa @Strain 4.61 %, Temperature 90.0 °C | 21020 psi @Strain 4.61 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 144.91 MPa @Strain 3.73 %, Temperature 40.0 °C | 21017 psi @Strain 3.73 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 145.64 MPa @Strain 0.980 %, Temperature 23.0 °C | 21123 psi @Strain 0.980 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 145.85 MPa @Strain 1.16 %, Temperature 40.0 °C | 21154 psi @Strain 1.16 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 146.78 MPa @Strain 1.99 %, Temperature 23.0 °C | 21289 psi @Strain 1.99 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 148.53 MPa @Strain 1.89 %, Temperature 60.0 °C | 21542 psi @Strain 1.89 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 149.8 MPa @Strain 1.13 %, Temperature 0.000 °C | 21730 psi @Strain 1.13 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 152.2 MPa @Strain 2.18 %, Temperature 23.0 °C | 22070 psi @Strain 2.18 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 154.13 MPa @Strain 0.990 %, Temperature 0.000 °C | 22355 psi @Strain 0.990 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 155.03 MPa @Strain 2.07 %, Temperature 60.0 °C | 22485 psi @Strain 2.07 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 155.58 MPa @Strain 1.27 %, Temperature 40.0 °C | 22565 psi @Strain 1.27 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 156.25 MPa @Strain 1.08 %, Temperature 23.0 °C | 22662 psi @Strain 1.08 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 157.06 MPa @Strain 2.39 %, Temperature 23.0 °C | 22780 psi @Strain 2.39 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 158.96 MPa @Strain 1.25 %, Temperature 0.000 °C | 23055 psi @Strain 1.25 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 161.27 MPa @Strain 2.29 %, Temperature 60.0 °C | 23390 psi @Strain 2.29 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 161.3 MPa @Strain 2.64 %, Temperature 23.0 °C | 23390 psi @Strain 2.64 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 164.4 MPa @Strain 2.91 %, Temperature 23.0 °C | 23840 psi @Strain 2.91 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 164.86 MPa @Strain 1.40 %, Temperature 40.0 °C | 23911 psi @Strain 1.40 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 165.48 MPa @Strain 1.08 %, Temperature 0.000 °C | 24001 psi @Strain 1.08 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 166.4 MPa @Strain 3.26 %, Temperature 23.0 °C | 24130 psi @Strain 3.26 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 166.58 MPa @Strain 2.52 %, Temperature 60.0 °C | 24160 psi @Strain 2.52 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 167.1 MPa @Strain 1.17 %, Temperature 23.0 °C | 24240 psi @Strain 1.17 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 167.18 MPa @Strain 3.66 %, Temperature 23.0 °C | 24247 psi @Strain 3.66 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 168.06 MPa @Strain 1.37 %, Temperature 0.000 °C | 24375 psi @Strain 1.37 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 171.03 MPa @Strain 2.78 %, Temperature 60.0 °C | 24806 psi @Strain 2.78 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 172.45 MPa @Strain 1.05 %, Temperature -20.0 °C | 25012 psi @Strain 1.05 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 173.91 MPa @Strain 1.53 %, Temperature 40.0 °C | 25224 psi @Strain 1.53 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 174.27 MPa @Strain 3.12 %, Temperature 60.0 °C | 25276 psi @Strain 3.12 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 174.33 MPa @Strain 1.14 %, Temperature -20.0 °C | 25284 psi @Strain 1.14 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 175.91 MPa @Strain 3.55 %, Temperature 60.0 °C | 25514 psi @Strain 3.55 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 176.72 MPa @Strain 1.17 %, Temperature 0.000 °C | 25631 psi @Strain 1.17 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 177.18 MPa @Strain 1.50 %, Temperature 0.000 °C | 25698 psi @Strain 1.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 177.79 MPa @Strain 1.28 %, Temperature 23.0 °C | 25786 psi @Strain 1.28 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 182.59 MPa @Strain 1.68 %, Temperature 40.0 °C | 26482 psi @Strain 1.68 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 184.66 MPa @Strain 1.23 %, Temperature -20.0 °C | 26783 psi @Strain 1.23 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 185.69 MPa @Strain 1.15 %, Temperature -20.0 °C | 26932 psi @Strain 1.15 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 186.31 MPa @Strain 1.64 %, Temperature 0.000 °C | 27022 psi @Strain 1.64 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 187.73 MPa @Strain 1.27 %, Temperature 0.000 °C | 27228 psi @Strain 1.27 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 188.51 MPa @Strain 1.40 %, Temperature 23.0 °C | 27341 psi @Strain 1.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 190.63 MPa @Strain 1.85 %, Temperature 40.0 °C | 27649 psi @Strain 1.85 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 195.03 MPa @Strain 1.33 %, Temperature -20.0 °C | 28287 psi @Strain 1.33 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 195.22 MPa @Strain 1.81 %, Temperature 0.000 °C | 28314 psi @Strain 1.81 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 198.07 MPa @Strain 1.36 %, Temperature 0.000 °C | 28728 psi @Strain 1.36 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 198.14 MPa @Strain 1.26 %, Temperature -20.0 °C | 28738 psi @Strain 1.26 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 198.16 MPa @Strain 2.03 %, Temperature 40.0 °C | 28741 psi @Strain 2.03 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 198.66 MPa @Strain 1.53 %, Temperature 23.0 °C | 28813 psi @Strain 1.53 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 203.68 MPa @Strain 2.00 %, Temperature 0.000 °C | 29541 psi @Strain 2.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 204.86 MPa @Strain 2.23 %, Temperature 40.0 °C | 29712 psi @Strain 2.23 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 205.38 MPa @Strain 1.44 %, Temperature -20.0 °C | 29788 psi @Strain 1.44 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 208.08 MPa @Strain 1.66 %, Temperature 23.0 °C | 30180 psi @Strain 1.66 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 208.41 MPa @Strain 1.47 %, Temperature 0.000 °C | 30227 psi @Strain 1.47 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 210.08 MPa @Strain 2.46 %, Temperature 40.0 °C | 30470 psi @Strain 2.46 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 210.45 MPa @Strain 1.36 %, Temperature -20.0 °C | 30523 psi @Strain 1.36 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 210.95 MPa @Strain 2.22 %, Temperature 0.000 °C | 30596 psi @Strain 2.22 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 212.47 MPa @Strain 2.83 %, Temperature 40.0 °C | 30816 psi @Strain 2.83 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 215.74 MPa @Strain 2.50 %, Temperature 0.000 °C | 31290 psi @Strain 2.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 216.17 MPa @Strain 1.56 %, Temperature -20.0 °C | 31353 psi @Strain 1.56 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 217.71 MPa @Strain 1.82 %, Temperature 23.0 °C | 31576 psi @Strain 1.82 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 218.49 MPa @Strain 1.58 %, Temperature 0.000 °C | 31689 psi @Strain 1.58 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 222.34 MPa @Strain 1.48 %, Temperature -20.0 °C | 32248 psi @Strain 1.48 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 226.64 MPa @Strain 1.99 %, Temperature 23.0 °C | 32871 psi @Strain 1.99 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 226.94 MPa @Strain 1.69 %, Temperature -20.0 °C | 32915 psi @Strain 1.69 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 228.38 MPa @Strain 1.70 %, Temperature 0.000 °C | 33124 psi @Strain 1.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 234.3 MPa @Strain 1.59 %, Temperature -20.0 °C | 33980 psi @Strain 1.59 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 234.6 MPa @Strain 2.20 %, Temperature 23.0 °C | 34030 psi @Strain 2.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 237.27 MPa @Strain 1.82 %, Temperature 0.000 °C | 34413 psi @Strain 1.82 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 238.99 MPa @Strain 1.86 %, Temperature -20.0 °C | 34663 psi @Strain 1.86 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 240.69 MPa @Strain 2.49 %, Temperature 23.0 °C | 34909 psi @Strain 2.49 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 246.18 MPa @Strain 1.70 %, Temperature -20.0 °C | 35705 psi @Strain 1.70 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 246.6 MPa @Strain 1.96 %, Temperature 0.000 °C | 35770 psi @Strain 1.96 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 250.71 MPa @Strain 2.05 %, Temperature -20.0 °C | 36362 psi @Strain 2.05 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 255.46 MPa @Strain 2.10 %, Temperature 0.000 °C | 37051 psi @Strain 2.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 257.35 MPa @Strain 1.85 %, Temperature -20.0 °C | 37326 psi @Strain 1.85 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 260.25 MPa @Strain 2.25 %, Temperature -20.0 °C | 37746 psi @Strain 2.25 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 263.48 MPa @Strain 2.27 %, Temperature 0.000 °C | 38215 psi @Strain 2.27 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 266.34 MPa @Strain 2.55 %, Temperature -20.0 °C | 38629 psi @Strain 2.55 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 268.58 MPa @Strain 2.03 %, Temperature -20.0 °C | 38954 psi @Strain 2.03 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 270.34 MPa @Strain 2.54 %, Temperature 0.000 °C | 39210 psi @Strain 2.54 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 279.79 MPa @Strain 2.21 %, Temperature -20.0 °C | 40580 psi @Strain 2.21 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 289.95 MPa @Strain 2.39 %, Temperature -20.0 °C | 42054 psi @Strain 2.39 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 299.36 MPa @Strain 2.63 %, Temperature -20.0 °C | 43419 psi @Strain 2.63 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| Elongation at Break | 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 3.2 % @Temperature 23.0 °C | 3.2 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 5.818 GPa @Temperature 150 °C | 843.8 ksi @Temperature 302 °F | 50%RH; ISO 527 | ||
| 5.879 GPa @Temperature 200 °C | 852.7 ksi @Temperature 392 °F | DAM; ISO 527 | |||
| 6.326 GPa @Temperature 180 °C | 917.5 ksi @Temperature 356 °F | DAM; ISO 527 | |||
| 6.741 GPa @Temperature 150 °C | 977.7 ksi @Temperature 302 °F | DAM; ISO 527 | |||
| 7.137 GPa @Temperature 120 °C | 1035 ksi @Temperature 248 °F | 50%RH; ISO 527 | |||
| 7.684 GPa @Temperature 120 °C | 1114 ksi @Temperature 248 °F | DAM; ISO 527 | |||
| 7.806 GPa @Temperature 90.0 °C | 1132 ksi @Temperature 194 °F | 50%RH; ISO 527 | |||
| 8.612 GPa @Temperature 60.0 °C | 1249 ksi @Temperature 140 °F | 50%RH; ISO 527 | |||
| 8.958 GPa @Temperature 90.0 °C | 1299 ksi @Temperature 194 °F | DAM; ISO 527 | |||
| 9.46 GPa @Temperature 40.0 °C | 1370 ksi @Temperature 104 °F | 50%RH; ISO 527 | |||
| 12.444 GPa @Temperature 60.0 °C | 1804.9 ksi @Temperature 140 °F | DAM; ISO 527 | |||
| 13.2 GPa @Temperature 23.0 °C | 1910 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 14.69 GPa @Temperature 40.0 °C | 2131 ksi @Temperature 104 °F | DAM; ISO 527 | |||
| 15.89 GPa @Temperature 0.000 °C | 2305 ksi @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 16.8 GPa @Temperature 23.0 °C | 2440 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| 17.094 GPa @Temperature -20.0 °C | 2479.3 ksi @Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 17.118 GPa @Temperature 0.000 °C | 2482.8 ksi @Temperature 32.0 °F | DAM; ISO 527 | |||
| 18.037 GPa @Temperature -20.0 °C | 2616.1 ksi @Temperature -4.00 °F | DAM; ISO 527 | |||
| Fatigue Strength | 83.0 MPa @# of Cycles 71327 , Temperature 23.0 °C | 12000 psi @# of Cycles 71327 , Temperature 73.4 °F | 50%RH; 10Hz,R=0.1; 4mm; ISO 13003 | ||
| 99.6 MPa @# of Cycles 3182 , Temperature 23.0 °C | 14400 psi @# of Cycles 3182 , Temperature 73.4 °F | 50%RH; 10Hz,R=0.1; 4mm; ISO 13003 | |||
| 116.2 MPa @# of Cycles 1073 , Temperature 23.0 °C | 16850 psi @# of Cycles 1073 , Temperature 73.4 °F | 50%RH; 10Hz,R=0.1; 4mm; ISO 13003 | |||
| 132.8 MPa @# of Cycles 471 , Temperature 23.0 °C | 19260 psi @# of Cycles 471 , Temperature 73.4 °F | 50%RH; 10Hz,R=0.1; 4mm; ISO 13003 | |||
| 149.4 MPa @# of Cycles 236 , Temperature 23.0 °C | 21670 psi @# of Cycles 236 , Temperature 73.4 °F | 50%RH; 10Hz,R=0.1; 4mm; ISO 13003 | |||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 1.60 J/cm² @Temperature 23.0 °C | 7.61 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.80 J/cm² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 10000 MPa @Temperature 23.0 °C | 1.45e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 8000 MPa @Temperature 23.0 °C | 1.16e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | ||
| Surface Resistance | 4.00e+14 ohm @Temperature 23.0 °C | 4.00e+14 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| Comparative Tracking Index | 400 - 600 V @Thickness 3.00 mm, Temperature 23.0 °C | 400 - 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 41.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 0.830 mm | 248 °F @Thickness 0.0327 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 115 °C @Thickness 0.830 mm | 239 °F @Thickness 0.0327 in | DAM; UL 746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 115 °C @Thickness 0.830 mm | 239 °F @Thickness 0.0327 in | DAM; UL 746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.830 mm | HB @Thickness 0.0327 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.830 mm | HB @Thickness 0.0327 in | DAM; UL94 | |||
| Oxygen Index | 24 % | 24 % | DAM; ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Creep Resistance, Good | DAM | ||||
| Fatigue Resistant | DAM | ||||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Heat Stabilized | DAM | ||||
| Oil Resistant | DAM | ||||
| Stiffness, High | DAM | ||||
| Strength, High | DAM | ||||
| Thermal Aging Resistance, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF50< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-GF50 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||