- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 12.0
- 弯曲模量 [MPa]: 6.00
- 热变形温度 [℃]: 258.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 25 % | 25 % | DAM | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 87.0 MPa @Temperature 23.0 °C | 12600 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 122 MPa @Temperature 23.0 °C | 17700 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 8.0 % @Temperature 23.0 °C | 8.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 4.70 GPa @Temperature 23.0 °C | 682 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 6.90 GPa @Temperature 23.0 °C | 1000 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 6.00 GPa @Temperature 23.0 °C | 870 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 180/1A | ||
| 12.0 kJ/m² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 13.0 kJ/m² @Temperature -40.0 °C | 6.19 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | |||
| 13.0 kJ/m² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 20.0 kJ/m² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 23.0 kJ/m² @Temperature 23.0 °C | 10.9 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 8.10 J/cm² @Temperature 23.0 °C | 38.5 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| 8.30 J/cm² @Temperature 23.0 °C | 39.5 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 8.70 J/cm² @Temperature -30.0 °C | 41.4 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 8.90 J/cm² @Temperature -30.0 °C | 42.4 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 2.20 J/cm² @Temperature 23.0 °C | 10.5 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.40 J/cm² @Temperature 23.0 °C | 11.4 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Impact Modifier | DAM | ||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Fatigue Resistant | DAM | ||||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Heat Stabilized | DAM | ||||
| Impact Modified | DAM | ||||
| Impact Resistance, Good | DAM | ||||
| Oil Resistant | DAM | ||||
| Thermal Aging Resistance, Good | DAM | ||||
| Toughness, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-IGF25< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-IGF25 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||