- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.8
- 成型收缩率 [%]: 0.008
- 缺口冲击强度: 0.43
- 拉伸强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 3.45
- 热变形温度 [℃]: 230.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | DAM; ASTM D792 | ||
| Density | 1.16 g/cc | 0.0419 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.8 % @Temperature 23.0 °C | 1.8 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | ||
| Linear Mold Shrinkage | 0.0080 cm/cm @Thickness 1.60 mm | 0.0080 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.0080 cm/cm @Thickness 1.60 mm | 0.0080 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Strength | 89.6 MPa @Temperature 23.0 °C | 13000 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Tensile Strength, Yield | 90.0 MPa @Temperature 23.0 °C | 13100 psi @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | ||
| Elongation at Break | 10 % @Temperature 23.0 °C | 10 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 10 % @Temperature 23.0 °C | 10 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 14 % @Temperature 23.0 °C | 14 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | ||
| Tensile Modulus | 3.75 GPa @Temperature 23.0 °C | 544 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 3.45 GPa @Temperature 23.0 °C | 500 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 3.66 GPa @Temperature 23.0 °C | 531 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature 23.0 °C | 0.806 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Charpy Impact Unnotched | 13.5 J/cm² @Temperature 23.0 °C | 64.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -40.0 °C | 1.43 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 0.370 J/cm² @Temperature 23.0 °C | 1.76 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | DAM; IEC 60112 | ||
| >= 600 V @Thickness 3.00 mm, Temperature 23.0 °C | >= 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 264 °C | 507 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DAM; ASTM D648 | ||
| 235 °C | 455 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ASTM D648 | ||
| 84.0 °C | 183 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 75.0 °C @Thickness 1.50 mm | 167 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.750 mm | 185 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 3.00 mm | 185 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | DAM; UL94 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | DAM; UL94 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | DAM; UL94 | |||
| Glow Wire Test | 775 °C @Thickness 3.00 mm | 1430 °F @Thickness 0.118 in | DAM; Ignition; IEC 60695-2-13 | ||
| 775 °C @Thickness 1.50 mm | 1430 °F @Thickness 0.0591 in | DAM; Ignition; IEC 60695-2-13 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | DAM; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | DAM; Optimum | |||
| 270 - 290 °C | 518 - 554 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Flame Retardant | DAM | |||
| Lubricant | DAM | ||||
| Appearance | Natural Color | DAM | |||
| Contains Flame Retardant | Yes | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Crystalline, Semi | DAM | |||
| Flame Retardant | DAM | ||||
| Nucleated | DAM | ||||
| Processability, Good | DAM | ||||
| Flame Retardant - Halogen/Red Phosphorus Free | Yes | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-FR(30)< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Flame Retardant Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-FR(30) | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Connectors | DAM | |||
| Electrical Parts | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||