- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 1.1
- 断裂伸长率 [%]: 295
- 弯曲强度 [MPa]: 185.0
- 弯曲模量 [MPa]: 8.40
- 热变形温度 [℃]: 218.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.4 % | 6.4 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 185 MPa | 26800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 11.17 GPa | 1620 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 295 MPa | 42800 psi | ASTM Data |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO Value |
| 9.45 GPa | 1370 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 4.10 GPa | 595 ksi | calculated |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO Data |
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO data | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature 20.0 °C | 11.7 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO data |
| 207 °C | 405 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |