- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.5
- 弯曲强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 6.63
- 硬度: 121.0
- 热变形温度 [℃]: 217.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Flexural Strength | 170 MPa | 24700 psi | ISO Data | ||
| Flexural Modulus | 6.63 GPa | 962 ksi | ISO Data | ||
| 7.59 GPa | 1100 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.17 mm | 0.937 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 17.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ISO 75 | ||
| 203 °C | 397 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||