- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.2
- 缺口冲击强度: 3.21
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 0.700
- 硬度: 52.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.2 % | 1.2 % | 24 hour; ISO Test | ||
| 7.1 % | 7.1 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 52 | 52 | ASTM Test | ||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ISO 527 | ||
| 36.0 MPa | 5220 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 7.0 % | 7.0 % | 50mm/min; ISO 527 | ||
| 30 % | 30 % | 2 in/min; ASTM Test | |||
| Flexural Strength | 28.0 MPa | 4060 psi | ASTM Test | ||
| 8.00 MPa @Temperature 120 °C | 1160 psi @Temperature 248 °F | ASTM Test | |||
| 9.00 MPa @Temperature 93.0 °C | 1310 psi @Temperature 199 °F | ASTM Test | |||
| 10.0 MPa @Temperature 65.0 °C | 1450 psi @Temperature 149 °F | ASTM Test | |||
| 124 MPa @Temperature -40.0 °C | 18000 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.700 GPa | 102 ksi | ASTM Test | ||
| 0.145 GPa @Temperature 120 °C | 21.0 ksi @Temperature 248 °F | ASTM Test | |||
| 0.160 GPa @Temperature 93.0 °C | 23.2 ksi @Temperature 199 °F | ASTM Test | |||
| 0.195 GPa @Temperature 65.0 °C | 28.3 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 3.21 J/cm @Thickness 3.17 mm | 6.01 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ASTM Test | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||