- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.55
- 弯曲强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 7.20
- 硬度: 121.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1mm/min; ISO 527 | ||
| 2.74 GPa @Temperature 120 °C | 397 ksi @Temperature 248 °F | ISO Data | |||
| 3.53 GPa @Temperature 80.0 °C | 512 ksi @Temperature 176 °F | ISO Data | |||
| 9.79 GPa @Temperature -40.0 °C | 1420 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 195 MPa | 28300 psi | ISO Data | ||
| 215 MPa | 31200 psi | ASTM Test | |||
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO Data | ||
| 7.93 GPa | 1150 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.550 J/cm @Thickness 3.17 mm | 1.03 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Unnotched | 7.40 J/cm | 13.9 ft-lb/in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| 4.00 kJ/m² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 | ||
| 0.350 J/cm² @Temperature -30.0 °C | 1.67 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 17.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| 202 °C | 396 °F | ASTM Test | |||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||