- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.5
- 缺口冲击强度: 0.64
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 0.670
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | 24 hour; ISO Test | ||
| 8.1 % | 8.1 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa @Temperature -40.0 °C | 10200 psi @Temperature -40.0 °F | ISO Data | ||
| 70.0 MPa @Temperature -40.0 °C | 10200 psi @Temperature -40.0 °F | ASTM Test | |||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527 | ||
| 32.0 MPa | 4640 psi | 2 in/min; ASTM Test | |||
| 20.0 MPa @Temperature 80.0 °C | 2900 psi @Temperature 176 °F | ASTM Test | |||
| 20.0 MPa @Temperature 80.0 °C | 2900 psi @Temperature 176 °F | ISO Data | |||
| 116 MPa @Temperature -40.0 °C | 16800 psi @Temperature -40.0 °F | ASTM Test | |||
| 116 MPa @Temperature -40.0 °C | 16800 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| 20 % @Temperature -40.0 °C | 20 % @Temperature -40.0 °F | ASTM Test | |||
| 20 % @Temperature -40.0 °C | 20 % @Temperature -40.0 °F | ISO Data | |||
| Elongation at Yield | 15 % | 15 % | 2 in/min; ASTM Test | ||
| 15 % | 15 % | 50mm/min; ISO 527 | |||
| 30 % @Temperature 80.0 °C | 30 % @Temperature 176 °F | ISO Data | |||
| 30 % @Temperature 120 °C | 30 % @Temperature 248 °F | ASTM Test | |||
| Tensile Modulus | 0.730 GPa | 106 ksi | 1mm/min; ISO 527 | ||
| 0.220 GPa @Temperature 120 °C | 31.9 ksi @Temperature 248 °F | ISO Data | |||
| 0.370 GPa @Temperature 80.0 °C | 53.7 ksi @Temperature 176 °F | ISO Data | |||
| 3.30 GPa @Temperature -40.0 °C | 479 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 32.0 MPa | 4640 psi | ASTM Test | ||
| 141 MPa @Temperature -40.0 °C | 20500 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.670 GPa | 97.2 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.640 J/cm @Temperature -40.0 °C | 1.20 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection molding | ||
| Mold Temperature | 70.0 °C | 158 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||