- 密度 [g/cm3]: 1.291
- 吸水率 [%]: 1.1
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.291 g/cc | 0.04664 lb/in³ | Melt; ISO 1183 | ||
| 1.49 g/cc | 0.0538 lb/in³ | dry; ISO 1183 | |||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 30 % | 30 % | 5mm/min; ISO 527 | ||
| 30 % | 30 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 2.39 GPa | 347 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO Data | ||
| 76.0 MPa | 11000 psi | ASTM Test | |||
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO Data | ||
| 2.73 GPa | 396 ksi | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.999 J/g-°C | 0.4778 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.281 W/m-K | 1.95 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | X | ||||