- 密度 [g/cm3]: 1.41
- 缺口冲击强度: 11.2
- 弯曲强度 [MPa]: 188.0
- 弯曲模量 [MPa]: 9.72
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 188 MPa | 27300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.9 % | 2.9 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 12.6 GPa | 1830 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 9.72 GPa | 1410 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 11.2 kJ/m² | 5.33 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.920 J/cm² | 4.38 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK00564 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||