- 密度 [g/cm3]: 1.41
- 弯曲模量 [MPa]: 3.43
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.6 MPa | 7340 psi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Elongation at Break | 4.6 % | 4.6 % | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Tensile Modulus | 4.304 GPa | 624.3 ksi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Flexural Strength | 80.2 MPa | 11600 psi | UNI EN ISO 14125: 2000 | ||
| Flexural Modulus | 3.43 GPa | 497 ksi | UNI EN ISO 14125: 2000 | ||
| Charpy Impact Unnotched | 2.185 J/cm² | 10.40 ft-lb/in² | ISO 179-1:2007 | ||
| Charpy Impact, Notched | 0.472 J/cm² | 2.25 ft-lb/in² | ISO 179-1:2007 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1e+13 ohm-cm | 1e+13 ohm-cm | ASTM D257-93 | ||
| Surface Resistance | 9.1e+13 ohm | 9.1e+13 ohm | ASTM D257-93 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 179.6 °C | 355.3 °F | ISO 11357-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 134.3 °C | 273.7 °F | ASTM D648 | ||
| Vicat Softening Point | 168.7 °C | 335.7 °F | 10 N; ASTM D1252 | ||
| Descriptive Properties | |||||
| Color | Aluminum | ||||
| Surface Finish | 1.8 Ra µm | After Finishing | |||
| 6.0 Ra µm | After SLS Process | ||||