- 密度 [g/cm3]: 1.101
- 弯曲模量 [MPa]: 6.2485
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.101 g/cc | 0.03978 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 77.85 MPa | 11290 psi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Elongation at Break | 2.6 % | 2.6 % | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Tensile Modulus | 7.3208 GPa | 1061.8 ksi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Flexural Strength | 131.52 MPa | 19075 psi | UNI EN ISO 14125: 2000 | ||
| Flexural Modulus | 6.2485 GPa | 906.28 ksi | UNI EN ISO 14125: 2000 | ||
| Charpy Impact Unnotched | 3.24 J/cm² | 15.4 ft-lb/in² | ASTM D256 and UNI EN ISO 179:1998 | ||
| Charpy Impact, Notched | 0.473 J/cm² | 2.25 ft-lb/in² | ASTM D256 and UNI EN ISO 179:1998 | ||
| 0.466 J/cm² @Temperature -30.0 °C | 2.22 ft-lb/in² @Temperature -22.0 °F | ASTM D256 and UNI EN ISO 179:1998 | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 130 ohm-cm | 130 ohm-cm | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 22.7 µm/m-°C @Temperature 46.0 °C | 12.6 µin/in-°F @Temperature 115 °F | X direction | ||
| 24.6 µm/m-°C @Temperature 80.0 °C | 13.7 µin/in-°F @Temperature 176 °F | X direction | |||
| 25.7 µm/m-°C @Temperature 46.0 - 120 °C | 14.3 µin/in-°F @Temperature 115 - 248 °F | X direction | |||
| 29.8 µm/m-°C @Temperature 120 °C | 16.6 µin/in-°F @Temperature 248 °F | X direction | |||
| 90.4 µm/m-°C @Temperature 46.0 °C | 50.2 µin/in-°F @Temperature 115 °F | Y direction | |||
| 99.3 µm/m-°C @Temperature 80.0 °C | 55.2 µin/in-°F @Temperature 176 °F | Y direction | |||
| 104.8 µm/m-°C @Temperature 46.0 - 120 °C | 58.22 µin/in-°F @Temperature 115 - 248 °F | Y direction | |||
| 124.7 µm/m-°C @Temperature 120 °C | 69.28 µin/in-°F @Temperature 248 °F | Y direction | |||
| 131.8 µm/m-°C @Temperature 46.0 °C | 73.22 µin/in-°F @Temperature 115 °F | Z direction | |||
| 216.7 µm/m-°C @Temperature 46.0 - 120 °C | 120.4 µin/in-°F @Temperature 115 - 248 °F | Z direction | |||
| 230.7 µm/m-°C @Temperature 80.0 °C | 128.2 µin/in-°F @Temperature 176 °F | Z direction | |||
| 287.6 µm/m-°C @Temperature 120 °C | 159.8 µin/in-°F @Temperature 248 °F | Z direction | |||
| Thermal Conductivity | 2.119 W/m-K | 14.71 BTU-in/hr-ft²-°F | |||
| Melting Point | 179.3 °C | 354.7 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175.4 °C | 347.7 °F | ASTM D648 | ||
| Vicat Softening Point | 178.1 °C | 352.6 °F | 10 N; ASTM D1252 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Surface Finish | 1.8 Ra µm | After Finishing | |||
| 6.0 Ra µm | After SLS Process | ||||