- 密度 [g/cm3]: 4.27
- 缺口冲击强度: 0.66
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 67.0
- 弯曲模量 [MPa]: 4.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.27 g/cc | 0.154 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0081 - 0.0101 cm/cm @Time 86400 sec | 0.0081 - 0.0101 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0087 - 0.0107 cm/cm @Time 86400 sec | 0.0087 - 0.0107 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 3.2 % | 3.2 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.72 GPa | 685 ksi | 1 mm/min; ISO 527 |
| 4.80 GPa | 696 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 69.0 MPa | 10000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.25 GPa | 616 ksi | 2 mm/min; ISO 178 |
| 4.32 GPa | 627 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.81 J/cm | 9.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 73.5 - 75.5 µm/m-°C @Temperature -30.0 - 30.0 °C | 40.8 - 41.9 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | >= 66.8 µm/m-°C @Temperature -30.0 - 30.0 °C | >= 37.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm | 214 °F @Thickness 0.126 in | unannealed; ASTM D648 | |