- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 0.16
- 缺口冲击强度: 0.534
- 断裂伸长率 [%]: 96.5
- 弯曲强度 [MPa]: 68.9
- 弯曲模量 [MPa]: 3.03
- 硬度: 108.0
- 热变形温度 [℃]: 171.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 - 1.50 g/cc | 0.0408 - 0.0542 lb/in³ | Average value: 1.30 g/cc Grade Count:12 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 18.0 % Grade Count:5 |
| Water Absorption | 0.160 - 1.20 % | 0.160 - 1.20 % | Average value: 0.388 % Grade Count:5 |
| Additive Loading | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 18.0 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00200 - 0.00550 cm/cm | 0.00200 - 0.00550 in/in | Average value: 0.00340 cm/cm Grade Count:10 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00600 cm/cm | 0.00500 - 0.00600 in/in | Average value: 0.00550 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 - 109 | 108 - 109 | Average value: 108 Grade Count:4 |
| Tensile Strength, Ultimate | 68.9 - 110 MPa | 10000 - 16000 psi | Average value: 81.7 MPa Grade Count:12 |
| Elongation at Break | 2.00 - 5.00 % | 2.00 - 5.00 % | Average value: 3.42 % Grade Count:12 |
| Modulus of Elasticity | 3.79 - 7.69 GPa | 550 - 1120 ksi | Average value: 5.39 GPa Grade Count:12 |
| Flexural Yield Strength | 96.5 - 117 MPa | 14000 - 17000 psi | Average value: 107 MPa Grade Count:10 |
| Flexural Modulus | 3.03 - 5.52 GPa | 440 - 800 ksi | Average value: 4.39 GPa Grade Count:10 |
| Izod Impact, Notched | 0.534 - 1.07 J/cm | 1.00 - 2.00 ft-lb/in | Average value: 0.849 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 4.27 - 6.41 J/cm | 8.00 - 12.0 ft-lb/in | Average value: 5.29 J/cm Grade Count:10 |
| Charpy Impact Unnotched | 8.29 - 8.49 J/cm² @Temperature -30.0 - -30.0 °C | 39.5 - 40.4 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 8.39 J/cm² Grade Count:2 |
| Charpy Impact, Notched | 0.940 - 0.990 J/cm² @Temperature -30.0 - -30.0 °C | 4.47 - 4.71 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.965 J/cm² Grade Count:2 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 2.00e+13 ohm-cm | 1.00e+13 - 2.00e+13 ohm-cm | Average value: 1.20e+13 ohm-cm Grade Count:5 |
| Dielectric Strength | 19.7 - 22.0 kV/mm | 500 - 559 kV/in | Average value: 20.5 kV/mm Grade Count:3 |
| Dissipation Factor | 0.000460 - 0.0150 | 0.000460 - 0.0150 | Average value: 0.00649 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 - 72.0 µm/m-°C | 27.8 - 40.0 µin/in-°F | Average value: 63.5 µm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 - 179 °C | 340 - 355 °F | Average value: 177 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 - 174 °C | 325 - 345 °F | Average value: 169 °C Grade Count:6 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 282 °C | 420 - 540 °F | Average value: 249 °C Grade Count:5 |
| Melt Temperature | 224 - 288 °C | 435 - 550 °F | Average value: 256 °C Grade Count:5 |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | Average value: 51.7 °C Grade Count:10 |
| Drying Temperature | 79.4 °C | 175 °F | Average value: 79.4 °C Grade Count:5 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:5 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:5 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:10 |