- 密度 [g/cm3]: 1.69
- 缺口冲击强度: 0.85
- 拉伸强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 1.54
- 热变形温度 [℃]: 153.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
| 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 |
| 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 36 % | 36 % | Type I, 5 mm/min; ASTM D638 |
| 65 % | 65 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| 1.77 GPa | 257 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 54.0 MPa | 7830 psi | ISO 178 |
| Flexural Modulus | 1.54 GPa | 223 ksi | 2 mm/min; ISO 178 |
| 1.61 GPa | 234 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.0 J/cm | 26.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 92.0 kJ/m² | 43.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C | 15.5 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 13.0 J | 9.59 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 101 µm/m-°C @Temperature -30.0 - 30.0 °C | 56.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 109 µm/m-°C @Temperature -30.0 - 30.0 °C | 60.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 146 °C @Thickness 3.20 mm | 295 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 47.0 °C @Thickness 3.20 mm | 117 °F @Thickness 0.126 in | unannealed; ASTM D648 | |