- 密度 [g/cm3]: 2.24
- 吸水率 [%]: 0.1
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 33.0
- 断裂伸长率 [%]: 51.0
- 弯曲模量 [MPa]: 1.90
- 热变形温度 [℃]: 146.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.24 g/cc | 0.0809 lb/in³ | ISO 1183 |
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 42 % | 42 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 51.0 MPa | 7400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 136 µm/m-°C @Temperature 23.0 - 60.0 °C | 75.6 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 60.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |