- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.7
- 成型收缩率 [%]: 0.003
- 缺口冲击强度: 1.07
- 弯曲模量 [MPa]: 6.205
- 热变形温度 [℃]: 205.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | DAM; ASTM D792 | ||
| Density | 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 33 % | 33 % | DAM | ||
| Water Absorption | 0.70 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.70 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 1.8 % @Thickness 1.00 mm, Temperature 23.0 °C | 1.8 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.20 mm | 0.0030 in/in @Thickness 0.126 in | Flow; DAM | ||
| 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Transverse; DAM | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Strength | 131 MPa @Temperature 23.0 °C | 19000 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| Tensile Modulus | 9.80 GPa @Temperature 23.0 °C | 1420 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Strength | 193 MPa @Temperature 23.0 °C | 28000 psi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 248 MPa @Temperature 23.0 °C | 36000 psi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Flexural Modulus | 6.205 GPa @Temperature 23.0 °C | 900.0 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 8.40 GPa @Temperature 23.0 °C | 1220 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 8.965 GPa @Temperature 23.0 °C | 1300 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 1.07 J/cm @Temperature 23.0 °C | 2.00 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | ||
| 1.07 J/cm @Temperature 23.0 °C | 2.00 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | |||
| Izod Impact, Unnotched | 9.60 J/cm @Temperature 23.0 °C | 18.0 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| 9.60 J/cm @Temperature 23.0 °C | 18.0 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 11.0 kJ/m² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 219 °C | 426 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ASTM D648 | ||
| 216 °C | 421 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| 200 °C | 392 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Heat Stabilized | DAM | |||
| Heat Stabilized | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612-GF33< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA612 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Color Stable Resins | DAM | |||
| Encapsulation Resins | DAM | ||||
| Glass Reinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612-GF33 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Electrical/Electronic Applications | DAM | |||
| Electrical/Electronic Applications | DAM | ||||