- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 0.481
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.17 mm | 0.011 in/in @Thickness 0.125 in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D 638 |
| Elongation at Break | 100 % | 100 % | ASTM D 638 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D 256 |
| Taber Abrasion, mg/1000 Cycles | 6.0 | 6.0 | ASTM D 1044 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D 648 |