- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.15
- 缺口冲击强度: 1.39
- 拉伸强度 [MPa]: 186.0
- 断裂伸长率 [%]: 269
- 弯曲模量 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec | 0.15 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 269 MPa | 39000 psi | ASTM D790 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Thickness 3.17 mm | 2.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 15.3 µm/m-°C | 8.50 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |