  4. LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant

LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant

LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant 物性表: LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant物性表及特性介绍,LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant注塑参数详情,如需LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.42
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 1.76
  • 拉伸强度 [MPa]: 192.0
  • 弯曲模量 [MPa]: 9.03
  • 热变形温度 [℃]: 223.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.42 g/cc1.42 g/ccMethod A; ASTM D792
Density 1.42 g/cc0.0513 lb/in³ISO 1183
Water Absorption 0.10 %0.10 %at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm0.0010 - 0.0020 in/inASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0080 cm/cm0.0070 - 0.0080 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 192 MPa27800 psiASTM D638
Tensile Strength, Yield 192 MPa27800 psiASTM D638
Elongation at Break 3.5 %3.5 %ASTM D638
Elongation at Yield 3.5 %3.5 %ASTM D638
Tensile Modulus 11.9 GPa1730 ksiASTM D638
Flexural Strength 276 MPa40000 psiASTM D790
Flexural Modulus 9.03 GPa1310 ksiASTM D790
Izod Impact, Notched 1.76 J/cm
@Thickness 3.18 mm		3.30 ft-lb/in
@Thickness 0.125 in		ASTM D256
Izod Impact, Unnotched 13.7 J/cm
@Thickness 3.18 mm		25.7 ft-lb/in
@Thickness 0.125 in		ASTM D256
Izod Impact, Notched (ISO) 16.9 kJ/m²8.04 ft-lb/in²ISO 180
Izod Impact, Unnotched (ISO) 88.3 kJ/m²42.0 ft-lb/in²ISO 180
Falling Dart Impact 11.8 J8.70 ft-lbASTM D3763
Impact Test 4.76 J3.51 ft-lbMulti-Axial Instrumented Impact Energy; ISO 6603-2
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 223 °C433 °FUnannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 214 °C417 °FUnannealed; ASTM D648
 
Processing PropertiesMetricEnglishComments
Melt Temperature 268 - 274 °C514 - 525 °F
Mold Temperature 82.2 - 93.3 °C180 - 200 °F
Drying Temperature 82.2 °C180 °F
Dry Time 4 hour4 hour
Moisture Content 0.20 %0.20 %Suggested
Back Pressure 0.172 - 0.345 MPa24.9 - 50.0 psi

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-48046.html

免责声明: 本文 LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络