- 拉伸强度 [MPa]: 1.9
- 脆化温度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 10 | 10 | Instant; ASTM D2240 |
| Tensile Strength, Yield | 1.90 MPa | 275 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 0.345 MPa @Strain 300 % | 50.0 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 800 % | 800 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Rebound | 65 % | 65 % | Bayshore; ASTM D2632 |
| Tear Strength | 7.89 kN/m | 45.0 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 30 % | 30 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -65.0 °C | -85.0 °F | ASTM D746 |