- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.11
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D995 | ||
| Melt Flow | 50 - 80 g/10 min | 50 - 80 g/10 min | Melt Volume Rate (cm³/10 min) | ||
| Melt Index of Compound | 65 g/10 min @Load 21.6 kg, Temperature 190 °C | 65 g/10 min @Load 47.6 lb, Temperature 374 °F | cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 87 | 87 | ASTM D2240 | ||
| Hardness, Shore D | 38 | 38 | ASTM D2240 | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 | ||
| Elongation at Break | 700 % | 700 % | ASTM D412 | ||
| 100% Modulus | 0.00730 GPa | 1.06 ksi | DIN 53504 | ||
| 300% Modulus | 0.0110 GPa | 1.60 ksi | DIN 53504 | ||
| Rebound | 38 % | 38 % | Bayshore; ASTM D2632 | ||
| Tear Strength | 98.2 kN/m | 560 pli | ASTM D624 | ||
| Abrasion | 35 | 35 | [mm3]; ISO 4649 | ||
| Compression Set | 24 % @Temperature 23.0 °C, Time 252000 sec | 24 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 | ||
| 42 % @Temperature 70.0 °C, Time 86400 sec | 42 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 155 - 175 °C | 311 - 347 °F | Huntsman/TMA | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 25.0 - 35.0 °C | 77.0 - 95.0 °F | Injection | ||
| 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | |||
| Nozzle Temperature | 180 - 190 °C | 356 - 374 °F | Extrusion | ||
| 185 - 200 °C | 365 - 392 °F | Injection | |||
| Adapter Temperature | 175 - 185 °C | 347 - 365 °F | Extrusion | ||
| Die Temperature | 185 - 195 °C | 365 - 383 °F | Extrusion | ||
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Injection | ||
| Descriptive Properties | |||||
| Heating Zone | 185-195°C | Injection | |||