- 密度 [g/cm3]: 1.49
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 118 |
| Filler Content | 30 % | 30 % | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 156 MPa | 22600 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 9.70 GPa | 1410 ksi | ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 260 °C | 500 °F | (Expected) Continuous use, UL |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ISO 75 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | DSC |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |