- 密度 [g/cm3]: 1.48
- 缺口冲击强度: 0.9
- 拉伸强度 [MPa]: 156.0
- 弯曲模量 [MPa]: 8.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec | 0.0050 - 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| 0.0064 cm/cm @Time 86400 sec | 0.0064 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec | 0.010 - 0.012 in/in @Time 24.0 hour | ASTM D955 |
| 0.011 cm/cm @Time 86400 sec | 0.011 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 156 MPa | 22600 psi | ASTM D638 |
| 158 MPa | 22900 psi | ISO 527 | |
| Tensile Strength, Yield | 156 MPa | 22600 psi | ASTM D638 |
| 158 MPa | 22900 psi | ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| 2.7 % | 2.7 % | ISO 527 | |
| Elongation at Yield | 2.6 % | 2.6 % | ISO 527 |
| 2.7 % | 2.7 % | ASTM D638 | |
| Tensile Modulus | 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527 |
| 11.72 GPa | 1700 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 243 MPa | 35200 psi | ISO 178 |
| 248 MPa | 36000 psi | ASTM D790 | |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ISO 178 |
| 8.96 GPa | 1300 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.34 J/cm | 17.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 5.40 µm/m-°C @Temperature -40.0 - 40.0 °C | 3.00 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 51.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 28.7 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 1.80 µm/m-°C @Temperature -40.0 - 40.0 °C | 1.00 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 19.4 µm/m-°C @Temperature -40.0 - 40.0 °C | 10.8 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |