- 密度 [g/cm3]: 1.61
- 缺口冲击强度: 0.69
- 拉伸强度 [MPa]: 156.0
- 弯曲模量 [MPa]: 9.65
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec | 0.011 in/in @Time 24.0 hour | ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 154 MPa | 22300 psi | ASTM D638 |
| 155 MPa | 22500 psi | ISO 527 | |
| Tensile Strength, Yield | 156 MPa | 22600 psi | ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Elongation at Yield | 2.2 % | 2.2 % | ISO 527 |
| 2.4 % | 2.4 % | ASTM D638 | |
| Tensile Modulus | 12.81 GPa | 1858 ksi | 1 mm/min; ISO 527 |
| 13.78 GPa | 1999 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 234 MPa | 33900 psi | ASTM D790 |
| 240 MPa | 34800 psi | ISO 178 | |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| 10.4 GPa | 1510 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.11 J/cm | 15.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 3.60 µm/m-°C @Temperature -40.0 - 40.0 °C | 2.00 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 4.00 µm/m-°C @Temperature -40.0 - 40.0 °C | 2.22 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 1.80 µm/m-°C @Temperature -40.0 - 40.0 °C | 1.00 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 2.00 µm/m-°C @Temperature -40.0 - 40.0 °C | 1.11 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |