- 密度 [g/cm3]: 1.53
- 缺口冲击强度: 1.17
- 弯曲模量 [MPa]: 11.03
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 181 MPa | 26300 psi | ASTM D638 |
| 187 MPa | 27100 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 12.9 GPa | 1870 ksi | 1 mm/min; ISO 527 |
| 13.03 GPa | 1890 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| 278 MPa | 40300 psi | ISO 178 | |
| Flexural Modulus | 11.03 GPa | 1600 ksi | ASTM D790 |
| 12.5 GPa | 1810 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.13 J/cm | 17.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C @Temperature -40.0 - 40.0 °C | 11.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 20.5 µm/m-°C @Temperature -40.0 - 40.0 °C | 11.4 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 20.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 36.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 20.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |