- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 0.37
- 弯曲模量 [MPa]: 9.51
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.130 % | 0.130 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec | 0.0020 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0028 - 0.0031 cm/cm @Time 86400 sec | 0.0028 - 0.0031 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0051 - 0.0058 cm/cm @Time 86400 sec | 0.0051 - 0.0058 in/in @Time 24.0 hour | ISO 294 |
| 0.0050 - 0.0060 cm/cm @Time 86400 sec | 0.0050 - 0.0060 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 153 MPa | 22200 psi | ASTM D638 |
| 163 MPa | 23600 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 10.52 GPa | 1526 ksi | 1 mm/min; ISO 527 |
| 11.51 GPa | 1669 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 259 MPa | 37600 psi | ASTM D790 |
| 263 MPa | 38100 psi | ISO 178 | |
| Flexural Modulus | 9.51 GPa | 1380 ksi | ASTM D790 |
| 9.85 GPa | 1430 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1000 - 1.00e+7 ohm | 1000 - 1.00e+7 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 51.9 µm/m-°C @Temperature -40.0 - 40.0 °C | 28.8 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 52.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 28.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 53.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 29.8 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 53.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 29.8 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 298 °C | 568 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 270 °C @Thickness 3.20 mm | 518 °F @Thickness 0.126 in | unannealed; ASTM D648 | |