LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement

LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement 物性表: LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement物性表及特性介绍,LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement注塑参数详情,如需LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement下载, 可到相关下载区下载
  • 缺口冲击强度: 0.641
  • 拉伸强度 [MPa]: 228.0
  • 弯曲模量 [MPa]: 21.6
  • 热变形温度 [℃]: 300.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.41 g/cc1.41 g/ccMethod A; ASTM D792
Linear Mold Shrinkage 0.0010 cm/cm0.0010 in/inASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm0.0080 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 228 MPa33100 psiASTM D638
Tensile Strength, Yield 228 MPa33100 psiASTM D638
Elongation at Break 1.3 %1.3 %ASTM D638
Elongation at Yield 1.3 %1.3 %ASTM D638
Tensile Modulus 25.0 GPa3630 ksiASTM D638
Flexural Strength 338 MPa49000 psiASTM D790
Flexural Modulus 21.6 GPa3130 ksiASTM D790
Izod Impact, Notched 0.641 J/cm
@Thickness 3.18 mm
1.20 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.32 J/cm
@Thickness 3.18 mm
8.09 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²2.86 ft-lb/in²ISO 180
Izod Impact, Unnotched (ISO) 37.4 kJ/m²17.8 ft-lb/in²ISO 180
Falling Dart Impact 7.62 J5.62 ft-lbASTM D3763
Impact Test 4.57 J3.37 ft-lbMulti-Axial Instrumented Impact Energy; ISO 6603-2
 
Thermal PropertiesMetricEnglishComments
CTE, linear 18.0 µm/m-°C
@Temperature 20.0 °C
10.0 µin/in-°F
@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 32.0 µm/m-°C
@Temperature 20.0 °C
17.8 µin/in-°F
@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 300 °C572 °FUnannealed; ASTM D648
 
Processing PropertiesMetricEnglishComments
Melt Temperature 379 - 388 °C714 - 730 °F
Mold Temperature 135 - 163 °C275 - 325 °F
Drying Temperature 121 - 149 °C250 - 300 °F
Dry Time 4 hour4 hour
Moisture Content 0.10 %0.10 %Suggested
Back Pressure 0.345 - 0.689 MPa50.0 - 99.9 psi

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-50413.html

免责声明: 本文 LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家