Celanese ZENITE 7145L LCP, 45% Glass Reinforced

Celanese ZENITE 7145L LCP, 45% Glass Reinforced 物性表: Celanese ZENITE 7145L LCP, 45% Glass Reinforced物性表及特性介绍,Celanese ZENITE 7145L LCP, 45% Glass Reinforced注塑参数详情,如需Celanese ZENITE 7145L LCP, 45% Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.74
  • 弯曲模量 [MPa]: 17.8
 
Physical PropertiesMetricEnglishComments
Density 1.74 g/cc0.0629 lb/in³ISO 1183
Density of Compound 1.45 g/cc0.0524 lb/in³melt; Internal
Linear Mold Shrinkage, Flow 0.000500 cm/cm0.000500 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.00500 cm/cm0.00500 in/inISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 58.058.0ISO 2039-2
Tensile Strength at Break 120 MPa17400 psi5mm/min; ISO 527-2/1A
Elongation at Break 0.900 %0.900 %5mm/min; ISO 527-2/1A
Tensile Modulus 18.0 GPa2610 ksi1mm/min; ISO 527-2/1A
Flexural Strength 180 MPa26100 psiISO 178
Flexural Modulus 17.8 GPa2580 ksiISO 178
Charpy Impact Unnotched 1.80 J/cm²8.57 ft-lb/in²ISO 179/1eU
 1.30 J/cm²
@Temperature -30.0 °C
6.19 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²4.76 ft-lb/in²ISO 179/1eA
 1.00 J/cm²
@Temperature -30.0 °C
4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
Dielectric Constant  4.40
@Frequency 1.00e+6 Hz
4.40
@Frequency 1.00e+6 Hz
IEC 60250
 4.80
@Frequency 100 Hz
4.80
@Frequency 100 Hz
IEC 60250
Dielectric Strength 36.0 kV/mm914 kV/inIEC 60243-1
Dissipation Factor  0.0130
@Frequency 100 Hz
0.0130
@Frequency 100 Hz
IEC 60250
 0.0240
@Frequency 1.00e+6 Hz
0.0240
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 200 V200 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear 7.00 µm/m-°C3.89 µin/in-°FISO 11359-2
CTE, linear, Transverse to Flow 24.0 µm/m-°C13.3 µin/in-°FISO 11359-2
Specific Heat Capacity 1.50 J/g-°C0.359 BTU/lb-°FInternal
Thermal Conductivity 0.320 W/m-K2.22 BTU-in/hr-ft²-°FInternal
Melting Point 355 °C671 °F10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 295 °C563 °FISO 75-1, -2
Flammability, UL94  V-0
@Thickness 1.60 mm
V-0
@Thickness 0.0630 in
UL94
 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
UL94
Oxygen Index 45.0 %45.0 %ISO 4589
 
Processing PropertiesMetricEnglishComments
Processing Temperature 20.0 - 30.0 °C68.0 - 86.0 °F
 80.0 - 120 °C176 - 248 °FCavity temperature
 275 °C527 °FEjection temperature; Internal
Feed Temperature 40.0 - 60.0 °C104 - 140 °F
Zone 1 355 - 365 °C671 - 689 °F
Zone 2 360 - 370 °C680 - 698 °F
Zone 3 360 - 370 °C680 - 698 °F
Zone 4 360 - 370 °C680 - 698 °F
Die Temperature 360 - 370 °C680 - 698 °F
Melt Temperature 360 - 370 °C680 - 698 °F
 360 - 370 °C680 - 698 °F
 365 °C689 °FOptimum
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature >= 150 °C>= 302 °F
Dry Time 3.00 hour3.00 hour
Moisture Content 0.0100 %0.0100 %Necessary low maximum residual
Injection Pressure 50.0 - 150 MPa7250 - 21800 psi
Hold Pressure 50.0 - 150 MPa7250 - 21800 psi
Back Pressure 3.00 MPa435 psi

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31863.html

免责声明: 本文 Celanese ZENITE 7145L LCP, 45% Glass Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4