- 密度 [g/cm3]: 1.89
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Transverse | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.00 % | 1.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 17.6 GPa | 2550 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 9.00 µm/m-°C | 5.00 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C | 21.7 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 310 °C | 590 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 355 - 365 °C | 671 - 689 °F | |
| Zone 2 | 360 - 370 °C | 680 - 698 °F | |
| Zone 3 | 360 - 370 °C | 680 - 698 °F | |
| Zone 4 | 360 - 370 °C | 680 - 698 °F | |
| Die Temperature | 360 - 370 °C | 680 - 698 °F | |
| Melt Temperature | 365 - 375 °C | 689 - 707 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |