塑胶原料之家
  1. 首页
  2. 英文物性
  3. LCP
  4. Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced

Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced

Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced 物性表: Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced物性表及特性介绍,Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced注塑参数详情,如需Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.74
  • 吸水率 [%]: 0.03
  • 弯曲模量 [MPa]: 7.20
 
Physical PropertiesMetricEnglishComments
Density 1.74 g/cc0.0629 lb/in³ISO 1183
Melt Density 1.39 g/cc0.0502 lb/in³
Moisture Absorption at Equilibrium 0.010 %0.010 %23°C/50%RH; ISO 62
Water Absorption at Saturation 0.030 %0.030 %ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm0.0030 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm0.011 in/inISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 100 MPa14500 psi5mm/min; ISO 527-2/1A
Tensile Stress  9.28 MPa
@Strain 0.230 %,
Temperature 180 °C		1350 psi
@Strain 0.230 %,
Temperature 356 °F
 10.7 MPa
@Strain 0.320 %,
Temperature 200 °C		1550 psi
@Strain 0.320 %,
Temperature 392 °F
 11.2 MPa
@Strain 0.290 %,
Temperature 180 °C		1620 psi
@Strain 0.290 %,
Temperature 356 °F
 12.2 MPa
@Strain 0.260 %,
Temperature 120 °C		1770 psi
@Strain 0.260 %,
Temperature 248 °F
 13.5 MPa
@Strain 0.430 %,
Temperature 200 °C		1960 psi
@Strain 0.430 %,
Temperature 392 °F
 14.7 MPa
@Strain 0.420 %,
Temperature 180 °C		2130 psi
@Strain 0.420 %,
Temperature 356 °F
 14.8 MPa
@Strain 0.350 %,
Temperature 150 °C		2150 psi
@Strain 0.350 %,
Temperature 302 °F
 15.4 MPa
@Strain 0.250 %,
Temperature 90.0 °C		2230 psi
@Strain 0.250 %,
Temperature 194 °F
 15.8 MPa
@Strain 0.560 %,
Temperature 200 °C		2290 psi
@Strain 0.560 %,
Temperature 392 °F
 17.6 MPa
@Strain 0.550 %,
Temperature 180 °C		2550 psi
@Strain 0.550 %,
Temperature 356 °F
 17.9 MPa
@Strain 0.700 %,
Temperature 200 °C		2600 psi
@Strain 0.700 %,
Temperature 392 °F
 18.5 MPa
@Strain 0.480 %,
Temperature 150 °C		2680 psi
@Strain 0.480 %,
Temperature 302 °F
 19.7 MPa
@Strain 0.850 %,
Temperature 200 °C		2860 psi
@Strain 0.850 %,
Temperature 392 °F
 20.1 MPa
@Strain 0.690 %,
Temperature 180 °C		2920 psi
@Strain 0.690 %,
Temperature 356 °F
 20.1 MPa
@Strain 0.250 %,
Temperature 60.0 °C		2920 psi
@Strain 0.250 %,
Temperature 140 °F
 21.1 MPa
@Strain 0.990 %,
Temperature 200 °C		3060 psi
@Strain 0.990 %,
Temperature 392 °F
 21.6 MPa
@Strain 0.620 %,
Temperature 150 °C		3130 psi
@Strain 0.620 %,
Temperature 302 °F
 21.6 MPa
@Strain 0.540 %,
Temperature 120 °C		3130 psi
@Strain 0.540 %,
Temperature 248 °F
 22.2 MPa
@Strain 1.12 %,
Temperature 200 °C		3220 psi
@Strain 1.12 %,
Temperature 392 °F
 22.3 MPa
@Strain 0.830 %,
Temperature 180 °C		3230 psi
@Strain 0.830 %,
Temperature 356 °F
 22.5 MPa
@Strain 0.410 %,
Temperature 90.0 °C		3260 psi
@Strain 0.410 %,
Temperature 194 °F
 23.1 MPa
@Strain 1.28 %,
Temperature 200 °C		3350 psi
@Strain 1.28 %,
Temperature 392 °F
 23.6 MPa
@Strain 1.45 %,
Temperature 200 °C		3420 psi
@Strain 1.45 %,
Temperature 392 °F
 24.1 MPa
@Strain 0.990 %,
Temperature 180 °C		3500 psi
@Strain 0.990 %,
Temperature 356 °F
 24.1 MPa
@Strain 0.780 %,
Temperature 150 °C		3500 psi
@Strain 0.780 %,
Temperature 302 °F
 25.4 MPa
@Strain 1.16 %,
Temperature 180 °C		3680 psi
@Strain 1.16 %,
Temperature 356 °F
 26.3 MPa
@Strain 0.930 %,
Temperature 150 °C		3810 psi
@Strain 0.930 %,
Temperature 302 °F
 26.4 MPa
@Strain 1.31 %,
Temperature 180 °C		3830 psi
@Strain 1.31 %,
Temperature 356 °F
 27.8 MPa
@Strain 1.65 %,
Temperature 180 °C		4030 psi
@Strain 1.65 %,
Temperature 356 °F
 28.0 MPa
@Strain 0.840 %,
Temperature 120 °C		4060 psi
@Strain 0.840 %,
Temperature 248 °F
 28.1 MPa
@Strain 1.08 %,
Temperature 150 °C		4080 psi
@Strain 1.08 %,
Temperature 302 °F
 29.4 MPa
@Strain 1.23 %,
Temperature 150 °C		4260 psi
@Strain 1.23 %,
Temperature 302 °F
 29.5 MPa
@Strain 0.420 %,
Temperature 60.0 °C		4280 psi
@Strain 0.420 %,
Temperature 140 °F
 30.6 MPa
@Strain 1.40 %,
Temperature 150 °C		4440 psi
@Strain 1.40 %,
Temperature 302 °F
 31.5 MPa
@Strain 1.59 %,
Temperature 150 °C		4570 psi
@Strain 1.59 %,
Temperature 302 °F
 32.6 MPa
@Strain 1.98 %,
Temperature 150 °C		4730 psi
@Strain 1.98 %,
Temperature 302 °F
 32.8 MPa
@Strain 1.21 %,
Temperature 120 °C		4760 psi
@Strain 1.21 %,
Temperature 248 °F
 33.1 MPa
@Strain 0.770 %,
Temperature 90.0 °C		4800 psi
@Strain 0.770 %,
Temperature 194 °F
 35.9 MPa
@Strain 1.60 %,
Temperature 120 °C		5210 psi
@Strain 1.60 %,
Temperature 248 °F
 35.9 MPa
@Strain 0.439 %,
Temperature 40.0 °C		5210 psi
@Strain 0.439 %,
Temperature 104 °F
 37.9 MPa
@Strain 2.02 %,
Temperature 120 °C		5500 psi
@Strain 2.02 %,
Temperature 248 °F
 39.0 MPa
@Strain 2.47 %,
Temperature 120 °C		5660 psi
@Strain 2.47 %,
Temperature 248 °F
 39.7 MPa
@Strain 2.92 %,
Temperature 120 °C		5760 psi
@Strain 2.92 %,
Temperature 248 °F
 40.2 MPa
@Strain 1.18 %,
Temperature 90.0 °C		5830 psi
@Strain 1.18 %,
Temperature 194 °F
 42.2 MPa
@Strain 0.560 %,
Temperature 40.0 °C		6120 psi
@Strain 0.560 %,
Temperature 104 °F
 42.9 MPa
@Strain 0.800 %,
Temperature 60.0 °C		6220 psi
@Strain 0.800 %,
Temperature 140 °F
 45.1 MPa
@Strain 1.64 %,
Temperature 90.0 °C		6540 psi
@Strain 1.64 %,
Temperature 194 °F
 47.6 MPa
@Strain 0.530 %,
Temperature 0.000 °C		6900 psi
@Strain 0.530 %,
Temperature 32.0 °F
 48.2 MPa
@Strain 2.10 %,
Temperature 90.0 °C		6990 psi
@Strain 2.10 %,
Temperature 194 °F
 49.5 MPa
@Strain 0.760 %,
Temperature 40.0 °C		7180 psi
@Strain 0.760 %,
Temperature 104 °F
 50.1 MPa
@Strain 2.61 %,
Temperature 90.0 °C		7270 psi
@Strain 2.61 %,
Temperature 194 °F
 50.3 MPa
@Strain 0.580 %,
Temperature 23.0 °C		7300 psi
@Strain 0.580 %,
Temperature 73.4 °F
 50.9 MPa
@Strain 2.86 %,
Temperature 90.0 °C		7380 psi
@Strain 2.86 %,
Temperature 194 °F
 52.4 MPa
@Strain 1.23 %,
Temperature 60.0 °C		7600 psi
@Strain 1.23 %,
Temperature 140 °F
 56.3 MPa
@Strain 0.990 %,
Temperature 40.0 °C		8170 psi
@Strain 0.990 %,
Temperature 104 °F
 58.5 MPa
@Strain 1.69 %,
Temperature 60.0 °C		8480 psi
@Strain 1.69 %,
Temperature 140 °F
 59.5 MPa
@Strain 0.810 %,
Temperature 23.0 °C		8630 psi
@Strain 0.810 %,
Temperature 73.4 °F
 59.5 MPa
@Strain 0.700 %,
Temperature 0.000 °C		8630 psi
@Strain 0.700 %,
Temperature 32.0 °F
 62.8 MPa
@Strain 2.16 %,
Temperature 60.0 °C		9110 psi
@Strain 2.16 %,
Temperature 140 °F
 65.8 MPa
@Strain 2.65 %,
Temperature 60.0 °C		9540 psi
@Strain 2.65 %,
Temperature 140 °F
 66.0 MPa
@Strain 1.02 %,
Temperature 23.0 °C		9570 psi
@Strain 1.02 %,
Temperature 73.4 °F
 66.3 MPa
@Strain 1.47 %,
Temperature 40.0 °C		9620 psi
@Strain 1.47 %,
Temperature 104 °F
 67.1 MPa
@Strain 0.680 %,
Temperature -20.0 °C		9730 psi
@Strain 0.680 %,
Temperature -4.00 °F
 67.9 MPa
@Strain 3.18 %,
Temperature 60.0 °C		9850 psi
@Strain 3.18 %,
Temperature 140 °F
 69.6 MPa
@Strain 3.72 %,
Temperature 60.0 °C		10100 psi
@Strain 3.72 %,
Temperature 140 °F
 73.1 MPa
@Strain 1.99 %,
Temperature 40.0 °C		10600 psi
@Strain 1.99 %,
Temperature 104 °F
 76.8 MPa
@Strain 1.49 %,
Temperature 23.0 °C		11100 psi
@Strain 1.49 %,
Temperature 73.4 °F
 77.6 MPa
@Strain 1.07 %,
Temperature 0.000 °C		11300 psi
@Strain 1.07 %,
Temperature 32.0 °F
 77.8 MPa
@Strain 2.50 %,
Temperature 40.0 °C		11300 psi
@Strain 2.50 %,
Temperature 104 °F
 81.1 MPa
@Strain 3.03 %,
Temperature 40.0 °C		11800 psi
@Strain 3.03 %,
Temperature 104 °F
 83.9 MPa
@Strain 3.63 %,
Temperature 40.0 °C		12200 psi
@Strain 3.63 %,
Temperature 104 °F
 84.8 MPa
@Strain 2.03 %,
Temperature 23.0 °C		12300 psi
@Strain 2.03 %,
Temperature 73.4 °F
 85.8 MPa
@Strain 4.21 %,
Temperature 40.0 °C		12400 psi
@Strain 4.21 %,
Temperature 104 °F
 88.4 MPa
@Strain 1.04 %,
Temperature -20.0 °C		12800 psi
@Strain 1.04 %,
Temperature -4.00 °F
 89.9 MPa
@Strain 1.50 %,
Temperature 0.000 °C		13000 psi
@Strain 1.50 %,
Temperature 32.0 °F
 90.1 MPa
@Strain 2.54 %,
Temperature 23.0 °C		13100 psi
@Strain 2.54 %,
Temperature 73.4 °F
 94.0 MPa
@Strain 3.08 %,
Temperature 23.0 °C		13600 psi
@Strain 3.08 %,
Temperature 73.4 °F
 97.2 MPa
@Strain 3.68 %,
Temperature 23.0 °C		14100 psi
@Strain 3.68 %,
Temperature 73.4 °F
 98.6 MPa
@Strain 4.32 %,
Temperature 23.0 °C		14300 psi
@Strain 4.32 %,
Temperature 73.4 °F
 99.0 MPa
@Strain 1.95 %,
Temperature 0.000 °C		14400 psi
@Strain 1.95 %,
Temperature 32.0 °F
 104 MPa
@Strain 1.43 %,
Temperature -20.0 °C		15100 psi
@Strain 1.43 %,
Temperature -4.00 °F
 106 MPa
@Strain 2.43 %,
Temperature 0.000 °C		15400 psi
@Strain 2.43 %,
Temperature 32.0 °F
 111 MPa
@Strain 2.92 %,
Temperature 0.000 °C		16100 psi
@Strain 2.92 %,
Temperature 32.0 °F
 115 MPa
@Strain 1.89 %,
Temperature -20.0 °C		16700 psi
@Strain 1.89 %,
Temperature -4.00 °F
 115 MPa
@Strain 3.43 %,
Temperature 0.000 °C		16700 psi
@Strain 3.43 %,
Temperature 32.0 °F
 118 MPa
@Strain 3.96 %,
Temperature 0.000 °C		17100 psi
@Strain 3.96 %,
Temperature 32.0 °F
 123 MPa
@Strain 2.34 %,
Temperature -20.0 °C		17800 psi
@Strain 2.34 %,
Temperature -4.00 °F
 130 MPa
@Strain 2.84 %,
Temperature -20.0 °C		18900 psi
@Strain 2.84 %,
Temperature -4.00 °F
 135 MPa
@Strain 3.34 %,
Temperature -20.0 °C		19600 psi
@Strain 3.34 %,
Temperature -4.00 °F
 138 MPa
@Strain 3.85 %,
Temperature -20.0 °C		20000 psi
@Strain 3.85 %,
Temperature -4.00 °F
Elongation at Break 3.2 %3.2 %5mm/min; ISO 527-2/1A
Tensile Modulus 9.00 GPa1310 ksi1mm/min; ISO 527-2/1A
Flexural Strength 140 MPa20300 psiISO 178
Flexural Modulus 7.20 GPa1040 ksiISO 178
Charpy Impact Unnotched 4.50 J/cm²21.4 ft-lb/in²ISO 179/1eU
 4.00 J/cm²
@Temperature 30.0 °C		19.0 ft-lb/in²
@Temperature 86.0 °F		ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²3.33 ft-lb/in²ISO 179/1eA
 0.600 J/cm²
@Temperature 30.0 °C		2.86 ft-lb/in²
@Temperature 86.0 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 7500 MPa1.09e+6 psiISO 899-1
Tensile Creep Modulus, 1000 hours 5500 MPa798000 psiISO 899-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+13 ohm-cm>= 1.00e+13 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
Dielectric Strength 32.0 kV/mm813 kV/inIEC 60243-1
Comparative Tracking Index 175 V175 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 12.0 µm/m-°C6.67 µin/in-°FISO 11359-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C30.6 µin/in-°FISO 11359-2
Specific Heat Capacity 1.50 J/g-°C0.359 BTU/lb-°F
Thermal Conductivity 0.350 W/m-K2.43 BTU-in/hr-ft²-°F
Melting Point 335 °C635 °FISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 240 °C464 °FISO 75-1, -2
Glass Transition Temp, Tg 125 °C257 °FISO 11357-1,-2,-3
Flammability, UL94 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in
 
Processing PropertiesMetricEnglishComments
Processing Temperature 40.0 - 150 °C104 - 302 °Fcavity
Melt Temperature 350 - 360 °C662 - 680 °F
Ejection Temperature 275 °C527 °F
Drying Temperature >= 150 °C>= 302 °F
Dry Time 3 hour3 hour
Moisture Content 0.010 %0.010 %Necessary low maximum

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31872.html

免责声明: 本文 Celanese ZENITE 6635 LCP, 40% Mineral / Glass Reinforced 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4