- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 0.02
- 缺口冲击强度: 20.0
- 弯曲强度 [MPa]: 160.0
- 弯曲模量 [MPa]: 14.0
- 热变形温度 [℃]: 284.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | IEC 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527 |
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Compressive Strength | 139 MPa | 20200 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 22.0 GPa | 3190 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 |
| Tensile Impact Strength | 70.0 kJ/m² | 33.3 ft-lb/in² | Notched; ASTM D1822 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.4 @Frequency 1e+7 Hz | 3.4 @Frequency 1e+7 Hz | |
| 3.8 @Frequency 1000 Hz | 3.8 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.0090 @Frequency 1e+7 Hz | 0.0090 @Frequency 1e+7 Hz | |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 182 sec | 182 sec | |
| Comparative Tracking Index | 200 V | 200 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 3.00 µm/m-°C @Temperature -50.0 - 200 °C | 1.67 µin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| 3.00 µm/m-°C @Temperature -58.0 - 390 °C | 1.67 µin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature -50.0 - 200 °C | 32.2 µin/in-°F @Temperature -58.0 - 392 °F | |
| 58.0 µm/m-°C @Temperature -50.0 - 200 °C | 32.2 µin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 325 °C | 617 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 284 °C | 543 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/A |
| Vicat Softening Point | 252 °C | 486 °F | ASTM D1525 |
| UL RTI, Electrical | 240 °C | 464 °F | |
| UL RTI, Mechanical with Impact | 220 °C | 428 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % | 44 % | ISO 4589 |