- 密度 [g/cm3]: 1.67
- 弯曲模量 [MPa]: 6.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.8 % | 3.8 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 6.60 GPa | 957 ksi | ISO 178 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 150 °C | 104 - 302 °F | cavity |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Drying Temperature | >= 150 °C | >= 302 °F | |
| Dry Time | 3 hour | 3 hour | |
| Moisture Content | 0.010 % | 0.010 % | Necessary low maximum |