- 密度 [g/cm3]: 1.81
- 吸水率 [%]: 0.01
- 缺口冲击强度: 10.0
- 弯曲强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % | 0.010 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | IEC 527 |
| Tensile Modulus | 24.5 GPa | 3550 ksi | ISO 527 |
| Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ISO 178 |
| Compressive Strength | 152 MPa | 22000 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 20.5 GPa | 2970 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+7 Hz | 4.0 @Frequency 1e+7 Hz | |
| 4.5 @Frequency 1000 Hz | 4.5 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.0090 @Frequency 1e+7 Hz | 0.0090 @Frequency 1e+7 Hz | |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 182 sec | 182 sec | |
| Comparative Tracking Index | 250 V | 250 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 2.00 µm/m-°C @Temperature -50.0 - 200 °C | 1.11 µin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| 2.00 µm/m-°C @Temperature -58.0 - 390 °C | 1.11 µin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -50.0 - 200 °C | 35.6 µin/in-°F @Temperature -58.0 - 392 °F | |
| 64.0 µm/m-°C @Temperature -50.0 - 200 °C | 35.6 µin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 325 °C | 617 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/A |
| UL RTI, Electrical | 220 °C | 428 °F | |
| UL RTI, Mechanical with Impact | 200 °C | 392 °F | |
| Flammability, UL94 | V-0 | V-0 | |