- 弯曲模量 [MPa]: 2.28
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 200 cP | 200 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 88 | 88 | |
| Tensile Strength at Break | 57.9 MPa | 8400 psi | |
| Elongation at Break | 5.1 % | 5.1 % | |
| Flexural Strength | 83.4 MPa | 12100 psi | |
| Flexural Modulus | 2.28 GPa | 330 ksi | |
| Compressive Strength | 75.2 MPa | 10900 psi | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.04e+14 ohm-cm | 3.04e+14 ohm-cm | C 96/23/96 |
| 3.80e+15 ohm-cm | 3.80e+15 ohm-cm | "A" | |
| Surface Resistance | 1.13e+14 ohm | 1.13e+14 ohm | C 96/23/96 |
| 3.93e+15 ohm | 3.93e+15 ohm | Cond. A | |
| Dielectric Constant | 3.12 @Frequency 1.00e+6 Hz | 3.12 @Frequency 1.00e+6 Hz | A |
| 3.26 @Frequency 60.0 Hz | 3.26 @Frequency 60.0 Hz | A | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 79.0 °C | 174 °F | Deflection Temp at unknown load |
| Processing Properties | Metric | English | Comments |
| Cure Time | 60.0 - 120 min @Temperature 150 - 160 °C | 1.00 - 2.00 hour @Temperature 302 - 320 °F | |
| 60.0 - 240 min @Temperature 160 - 180 °C | 1.00 - 4.00 hour @Temperature 320 - 356 °F | optional | |
| Pot Life | 205 min @Temperature 100 °C | 205 min @Temperature 212 °F | |
| Shelf Life | 5.00 - 8.00 Month | 5.00 - 8.00 Month | |