Abatron AboCast/AboCure 8110-1 Flexible Epoxy物性表参数

吸水率 [%]: 6.2
弯曲强度 [MPa]: 0.172

Physical Properties	Metric	English	Comments

Water Absorption	6.2 % @Time 7200 sec	6.2 % @Time 2.00 hour	boil; cured 2 hours @ 93°C
	11.9 % @Time 2.59e+6 sec	11.9 % @Time 720 hour	immersion; cured 30 days @ 25°C
	12.2 % @Time 2.59e+6 sec	12.2 % @Time 720 hour	immersion; cured 7 days @ 25°C
Viscosity	2570 cP	2570 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	11 @Temperature 75.0 °C	11 @Temperature 167 °F	cured 7 days @ 25°C
	21 @Temperature 25.0 °C	21 @Temperature 77.0 °F	cured 7 days @ 25°C
	28 @Temperature 75.0 °C	28 @Temperature 167 °F	cured 30 days @ 25°C
	38 @Temperature 75.0 °C	38 @Temperature 167 °F	cured 2 hrs. @ 93°C
	40 @Temperature 25.0 °C	40 @Temperature 77.0 °F	cured 30 days @ 25°C
	47 @Temperature 25.0 °C	47 @Temperature 77.0 °F	cured 2 hrs. @ 93°C
Hardness, Shore D	23 @Temperature 0.000 °C	23 @Temperature 32.0 °F	cured 7 days @ 25°C
	23 @Temperature 0.000 °C	23 @Temperature 32.0 °F	cured 30 days @ 25°C
	60 @Temperature 0.000 °C	60 @Temperature 32.0 °F	cured 2 hrs. @ 93°C
	77 @Temperature -60.0 °C	77 @Temperature -76.0 °F	cured 30 days @ 25°C
	82 @Temperature -60.0 °C	82 @Temperature -76.0 °F	cured 7 days @ 25°C
	83 @Temperature -60.0 °C	83 @Temperature -76.0 °F	cured 2 hrs. @ 93°C
Tensile Strength, Ultimate	0.172 MPa	25.0 psi	cured 7 days @ 25°C
	0.241 MPa	35.0 psi	cured 2 hours @ 93°C
	0.345 MPa	50.0 psi	cured 30 days @ 25°C
	0.758 MPa	110 psi	cured 8 hours @ 93°C
Elongation at Break	68 %	68 %	cured 8 hours @ 93°C
	90 %	90 %	cured 30 days @ 25°C
	160 %	160 %	cured 2 hours @ 93°C
	180 %	180 %	cured 7 days @ 25°C
Shear Strength	3.59 MPa @Temperature 75.0 °C	520 psi @Temperature 167 °F	Tensile, Al/Al lap joint; cured 2 hours @ 93°C
	4.90 MPa @Temperature 25.0 °C	710 psi @Temperature 77.0 °F	Tensile, Al/Al lap joint; cured 2 hours @ 93°C
	13.3 MPa @Temperature 0.000 °C	1930 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 2 hours @ 93°C

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.90e+7 ohm-cm @Temperature 150 °C	2.90e+7 ohm-cm @Temperature 302 °F	cured 2 hours @ 93°C
	3.00e+7 ohm-cm @Temperature 100 °C	3.00e+7 ohm-cm @Temperature 212 °F	cured 30 days @ 25°C
	3.40e+7 ohm-cm @Temperature 100 °C	3.40e+7 ohm-cm @Temperature 212 °F	cured 2 hours @ 93°C
	3.20e+8 ohm-cm @Temperature 100 °C	3.20e+8 ohm-cm @Temperature 212 °F	cured 7 days @ 25°C
	6.60e+8 ohm-cm @Temperature 25.0 °C	6.60e+8 ohm-cm @Temperature 77.0 °F	cured 30 days @ 25°C
	2.60e+9 ohm-cm @Temperature 25.0 °C	2.60e+9 ohm-cm @Temperature 77.0 °F	cured 2 hours @ 93°C
	4.30e+9 ohm-cm @Temperature 25.0 °C	4.30e+9 ohm-cm @Temperature 77.0 °F	cured 7 days @ 25°C

Processing Properties	Metric	English	Comments
Pot Life	120 min @Temperature 25.0 °C	120 min @Temperature 77.0 °F	200 g

Descriptive Properties
Parts by Weight (pbw)	100		AboCast 8110-1
	6		AboCure 8110-1