- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.32
- 弯曲强度 [MPa]: 67.6
- 弯曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | |||
| Water Absorption | 0.30 - 0.40 % @Time 864000 sec | 0.30 - 0.40 % @Time 240 hour | |||
| Viscosity | 46 cP @Temperature 65.0 °C | 46 cP @Temperature 149 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 85 | 85 | |||
| Tensile Strength, Ultimate | 67.6 MPa | 9800 psi | |||
| Elongation at Break | 1.7 % | 1.7 % | |||
| Elongation at Yield | 4.7 % | 4.7 % | |||
| Tensile Modulus | 5.86 GPa | 850 ksi | |||
| Flexural Strength | 64.8 MPa | 9400 psi | |||
| Flexural Modulus | 2.07 GPa | 300 ksi | |||
| Compressive Yield Strength | 103 MPa | 15000 psi | |||
| Compressive Modulus | 3.34 GPa | 485 ksi | |||
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.50e+15 ohm-cm | 2.50e+15 ohm-cm | Cond. C (96 hrs/23°C/96% rel. humidity) | ||
| 5.10e+15 ohm-cm | 5.10e+15 ohm-cm | Cond. A (as received) | |||
| Surface Resistance | 2.70e+14 ohm | 2.70e+14 ohm | Cond. C | ||
| 2.80e+14 ohm | 2.80e+14 ohm | Cond. A | |||
| Dielectric Constant | 3.23 @Frequency 1.00e+6 Hz | 3.23 @Frequency 1.00e+6 Hz | Cond. A (as received) | ||
| 3.32 @Frequency 1.00e+6 Hz | 3.32 @Frequency 1.00e+6 Hz | Cond. D (48 hrs. in dist. H2O at 50°C) | |||
| 3.44 @Frequency 1000 Hz | 3.44 @Frequency 1000 Hz | Cond. A (as received) | |||
| 3.47 @Frequency 60.0 Hz | 3.47 @Frequency 60.0 Hz | Cond. A (as received) | |||
| 3.93 @Frequency 1000 Hz | 3.93 @Frequency 1000 Hz | Cond. D (48 hrs. in dist. H2O at 50°C) | |||
| 4.16 @Frequency 60.0 Hz | 4.16 @Frequency 60.0 Hz | Cond. D (48 hrs. in dist. H2O at 50°C) | |||
| Dissipation Factor | 0.0070 @Frequency 1000 Hz | 0.0070 @Frequency 1000 Hz | Cond. A (as received) | ||
| 0.0079 @Frequency 60.0 Hz | 0.0079 @Frequency 60.0 Hz | Cond. A (as received) | |||
| 0.026 @Frequency 1.00e+6 Hz | 0.026 @Frequency 1.00e+6 Hz | Cond. A (as received) | |||
| 0.032 @Frequency 1000 Hz | 0.032 @Frequency 1000 Hz | Cond. D (48 h. in dist. H2O at 50°C) | |||
| 0.045 @Frequency 1.00e+6 Hz | 0.045 @Frequency 1.00e+6 Hz | Cond. D (48 h. in dist. H2O at 50°C) | |||
| 0.055 @Frequency 60.0 Hz | 0.055 @Frequency 60.0 Hz | Cond. D (48 h. in dist. H2O at 50°C) | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 60.0 - 65.0 µm/m-°C | 33.3 - 36.1 µin/in-°F | |||
| Thermal Conductivity | 0.167 - 0.201 W/m-K | 1.16 - 1.39 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 49.0 °C | 120 °F | Deflection Temp at unknown load | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 - 180 min @Temperature 150 - 160 °C | 2.00 - 3.00 hour @Temperature 302 - 320 °F | |||
| 960 min @Temperature 95.0 °C | 16.0 hour @Temperature 203 °F | ||||
| Pot Life | 420 min @Temperature 65.0 °C | 420 min @Temperature 149 °F | |||
| 2880 min @Temperature 20.0 °C | 2880 min @Temperature 68.0 °F | ||||
| Descriptive Properties | |||||
| Deflection at Break | 0.53 in. | ||||
| Parts by Weight (pbw) | 100 | AboCast | |||
| 88 | AboCure | ||||