- 密度 [g/cm3]: 1.08
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | |||
| Volatiles | 0.00 % | 0.00 % | EPA method #24 | ||
| Viscosity | 180 cP | 180 cP | ASTM-D562 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 57.2 MPa | 8300 psi | ASTM-D638 | ||
| Elongation at Break | 4.8 % | 4.8 % | ASTM-D638 | ||
| Flexural Strength | 65.8 MPa | 9550 psi | ASTM-D790 | ||
| Compressive Strength | 85.15 MPa | 12350 psi | ASTM-D695 | ||
| Adhesive Bond Strength | 10.89 MPa | 1579 psi | ASTM-D4541 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 230 °C | 446 °F | ASTM-D2485 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 5760 - 7200 min | 96.0 - 120 hour | (4-5 Days) | ||
| Shelf Life | 24.0 Month | 24.0 Month | |||
| Descriptive Properties | |||||
| Impact Resistance | 80 | ASTM-D4226 | |||
| Induction Period (min) | 5 to 10 | ||||
| Parts by Weight (pbw) | 100 | Part A Resin | |||
| 35-100 | Part B Hardener | ||||
| Tack-free Time (min) | 240 | ||||