- 密度 [g/cm3]: 0.947
- 缺口冲击强度: 0.262
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in³ | AboCure 7606-1 | ||
| 1.14 g/cc | 0.0411 lb/in³ | AboCast 7606-1 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 64 | 64 | AboCast/AboCure ratio: 100/80 pbw | ||
| 64 | 64 | AboCast/AboCure ratio: 100/100 pbw | |||
| 70 | 70 | AboCast/AboCure ratio: 100/40 pbw | |||
| 55 @Time 10.0 sec | 55 @Time 0.00278 hour | AboCast/AboCure ratio: 100/100 pbw | |||
| 62 @Time 10.0 sec | 62 @Time 0.00278 hour | AboCast/AboCure ratio: 100/80 pbw | |||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | |||
| Flexural Strength | 82.7 MPa | 12000 psi | |||
| Compressive Strength | 101 MPa | 14600 psi | |||
| Izod Impact, Notched | 0.262 J/cm | 0.490 ft-lb/in | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 180 min @Temperature 80.0 - 110 °C | 1.00 - 3.00 hour @Temperature 176 - 230 °F | |||
| 4320 - 11520 min @Temperature 20.0 °C | 72.0 - 192.0 hour @Temperature 68.0 °F | (3-8 Days) | |||
| Pot Life | 16 - 24 min @Temperature 60.0 - 80.0 °C | 16 - 24 min @Temperature 140 - 176 °F | |||
| 150 - 180 min @Temperature 20.0 - 25.0 °C | 150 - 180 min @Temperature 68.0 - 77.0 °F | ||||
| Descriptive Properties | |||||
| Hardening Time (min) | 180-480 | ||||
| Parts by Weight (pbw) | 100 | AboCast | |||
| 43 | AboCure | ||||
| Ultimate Elongation (%) | 9 | ||||