- 密度 [g/cm3]: 1.16
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Part A | ||
| 1.17 g/cc | 0.0424 lb/in³ | Part B | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 71.7 MPa | 10400 psi | |||
| Elongation at Break | 5.9 % | 5.9 % | |||
| Tensile Modulus | 2.61 GPa | 379 ksi | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.80e+15 ohm-cm | 1.80e+15 ohm-cm | |||
| Dielectric Constant | 3.2 @Frequency 60.0 Hz, Temperature 23.0 °C | 3.2 @Frequency 60.0 Hz, Temperature 73.4 °F | |||
| 4.2 @Frequency 60.0 Hz, Temperature 100 °C | 4.2 @Frequency 60.0 Hz, Temperature 212 °F | ||||
| 4.72 @Frequency 60.0 Hz, Temperature 150 °C | 4.72 @Frequency 60.0 Hz, Temperature 302 °F | ||||
| Dissipation Factor | 0.016 @Frequency 60.0 Hz, Temperature 23.0 °C | 0.016 @Frequency 60.0 Hz, Temperature 73.4 °F | |||
| 0.053 @Frequency 60.0 Hz, Temperature 100 °C | 0.053 @Frequency 60.0 Hz, Temperature 212 °F | ||||
| 0.089 @Frequency 60.0 Hz, Temperature 150 °C | 0.089 @Frequency 60.0 Hz, Temperature 302 °F | ||||
| Arc Resistance | >= 150 sec | >= 150 sec | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 123 °C | 253 °F | Deflection Temp at unknown load | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 - 180 min @Temperature 100 °C | 2.00 - 3.00 hour @Temperature 212 °F | |||
| 60.0 - 240 min @Temperature 120 - 160 °C | 1.00 - 4.00 hour @Temperature 248 - 320 °F | optional | |||
| Pot Life | 30 min @Temperature 80.0 °C | 30 min @Temperature 176 °F | |||
| >= 480 min @Temperature 25.0 °C | >= 480 min @Temperature 77.0 °F | ||||
| Descriptive Properties | |||||
| Arc-Track Free (min) | > 2000 | 2.5 KV | |||
| Color | Opaque | ||||
| Parts by Weight (pbw) | 100 | Part A | |||
| 78 | Part B | ||||
| Thermal Shock Resistance | Scale 0 (poor) to 10 (excellent) | ||||