- 吸水率 [%]: 2.3
- 弯曲强度 [MPa]: 68.64
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 2.3 % @Time 7200 sec | 2.3 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | ||
| Viscosity | 1650 cP | 1650 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 76 @Temperature 75.0 °C | 76 @Temperature 167 °F | cured 2 hrs. @ 93°C | ||
| 85 @Temperature 25.0 °C | 85 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 87 @Temperature 0.000 °C | 87 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 90 @Temperature -60.0 °C | 90 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 68.64 MPa | 9955 psi | cured 2 hours @ 93°C | ||
| 72.19 MPa | 10470 psi | cured 8 hours @ 93°C | |||
| Elongation at Break | 6.4 % | 6.4 % | cured 8 hours @ 93°C | ||
| 9.8 % | 9.8 % | cured 2 hours @ 93°C | |||
| Shear Strength | 23.2 MPa @Temperature 75.0 °C | 3370 psi @Temperature 167 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | ||
| 25.2 MPa @Temperature 0.000 °C | 3650 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| 33.2 MPa @Temperature 25.0 °C | 4810 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+9 ohm-cm @Temperature 150 °C | 2.00e+9 ohm-cm @Temperature 302 °F | cured 2 hours @ 93°C | ||
| 3.20e+9 ohm-cm @Temperature 112 °C | 3.20e+9 ohm-cm @Temperature 234 °F | cured 2 hours @ 93°C | |||
| 4.10e+10 ohm-cm @Temperature 100 °C | 4.10e+10 ohm-cm @Temperature 212 °F | cured 2 hours @ 93°C | |||
| 1.80e+16 ohm-cm @Temperature 25.0 °C | 1.80e+16 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 19 min @Temperature 25.0 °C | 19 min @Temperature 77.0 °F | 200 g | ||
| Gel Time | 2.00 min @Temperature 93.0 °C | 2.00 min @Temperature 199 °F | 10 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-5 | |||
| 11.6 | AboCure 8110-1 | ||||